Abstract A tungsten carbide powder and cemented tungsten carbide article made from the powder are disclosed. The powder has a particle size of greater than 20 micrometers in diameter and no particles less than one-half the average particle size or greater than two and one-half times the average particle size. A process is disclosed for producing the powder which comprises deagglomerating and classifying the tungsten powder to produce a powder wherein the Fisher Subseive Size is greater than 20 micrometers in diameter and wherein essentially no particles are greater than two and one-half times larger than the average Fisher Subsieve Size, forming a first mixture of the tungsten powder and carbon, carburizing, and deagglomerating and classifying the resulting tungsten carbide powder to eliminate particles greater than two and one-half times the average Fisher Subseive Size value and produce a tungsten carbide powder wherein the particle size is greater than 20 micrometers in diameter and wherein there are no particles less than one-half of the average particle size and no particles greater than two and one-half times the average particle size of the tungsten carbide powder. To produce the article a uniform second mixture is formed of the daeagglomerated and classified tungsten carbide powder and cobalt powder wherein the cobalt content is about 3% to 20% by weight, a third mixture is formed of the second mixture and a wax binder, a green article is formed from the third mixture, and sintered at about 1380° C. to 1550° C.
A process for producing tungsten carbide powder, said process comprising: (a) deagglomerating tungsten powder and thereafter classifying said tungsten powder to produce a deagglomerated and classified tungsten powder wherein the average particle size as measured by Fisher Subseive Size is greater than about 20 micrometers in diameter and wherein essentially no particles are greater than about two and one-half times larger than the average Fisher Subsieve Size; (b) forming a uniform first mixture of said deagglomerated and classified tungsten powder and carbon wherein the amount of said carbon is sufficient to react with essentially all of said tungsten to produce tungsten carbide in the subsequent heating step; (c) heating said first mixture at a temperature of from about 1425° to about 2000° C. for a sufficient time in a reducing atmosphere to produce tungsten carbide powder; and (d) deagglomerating and thereafter classifying said tungsten carbide powder to eliminate essentially all particles that are greater than about two and one-half times the average Fisher Subseive Size value and to produce a tungsten carbide powder wherein the average particle size is greater than about 20 micrometers in diameter and wherein there are essentially no particles that are less than about one-half of the average particle size and wherein there are essentially no particles that are greater than about two and one-half times the average particle size of said tungsten carbide powder.
Claim 2
Dependent Claim
229 words
A process for producing tungsten carbide powder, said process comprising: (a) deagglomerating tungsten powder and thereafter classifying said tungsten powder to produce a deagglomerated and classified tungsten powder wherein the average particle size as measured by Fisher Subseive Size is greater than about 20 micrometers in diameter and wherein essentially no particles are greater than about two and one-half times larger than the average Fisher Subsieve Size; (b) forming a uniform first mixture of said deagglomerated and classified tungsten powder and carbon wherein the amount of said carbon is sufficient to react with essentially all of said tungsten to produce tungsten carbide in the subsequent heating step; (c) heating said first mixture at a temperature of from about 1425° to about 2000° C. for a sufficient time in a reducing atmosphere to produce tungsten carbide powder; and (d) deagglomerating and thereafter classifying said tungsten carbide powder to eliminate essentially all particles that are greater than about two and one-half times the average Fisher Subseive Size value and to produce a tungsten carbide powder wherein the average particle size is greater than about 20 micrometers in diameter and wherein there are essentially no particles that are less than about one-half of the average particle size and wherein there are essentially no particles that are greater than about two and one-half times the average particle size of said tungsten carbide powder.
Claim 3
Dependent Claim
146 words
A process of claim 1 comprising the additional steps of: (e) forming a uniform second mixture of the resulting deagglomerated and classified tungsten carbide powder and of cobalt powder wherein the cobalt content of said second mixture is from about 3% to about 20% by weight of said second mixture; (b) forming a third mixture of said second mixture and a wax binder; (c) forming a green article from said third mixture; and (d) sintering said green article at a temperature of from about 1380° C. to about 1550° C. for a sufficient time to form a densified article wherein the microstructure of said densified article exhibits essentially no grains that are less than about one-half of the average grain size and which exhibits essentially no grains that are greater than about two and one-half times the average grain size of said cemented tungsten carbide article.
Claim 4
Dependent Claim
23 words
A process of claim 1 wherein said first mixture is heated at a temperature of from about 1425° C. to about 1650° C.