US5370759A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing multilayered ceramic substrate
Assignee: Panasonic Holdings Corp
•
Filing: 1993-05-14
•
Granted: 1994-12-06
•
Expires: 2013-05-14
Abstract
Abstract A method for producing a multilayered ceramic substrate including the steps of: forming at least two green sheets each including a low-temperature firing glass-ceramic substrate material, forming an electrode pattern and a via hole electrode on and through each green sheet with a conductor paste, laminating said green sheets to obtain a laminate, forming a pair of green sheets which include an inorganic material which is not sintered at a firing temperature of the green sheet of the low-temperature firing glass-ceramic substrate material or lower, and then forming a hole through the inorganic material green sheet, laminating the inorganic material green sheet on the outermost green sheet of the laminate to obtain a resultant laminate in which the hole is positioned over a portion of the electrode pattern of an outermost low-temperature firing glass-ceramic green sheets of the laminate, firing said resultant laminate at the firing temperature, and removing the unsintered inorganic material. The substrate does not shrink in its plane direction and surface smoothness, electrical resistance and solderability of the top layer wiring pattern are improved.
Inventors
- 👤 Yasuhiko Hakotani
- 👤 Seiichi Nakatani
- 👤 Tsuneharu Katada
- 👤 Satoru Yuhaku
- 👤 Kazuhiro Miura
- 👤 Yoshifumi Nakamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 21:10
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/68; H10W70/685; H10W70/01; H10W70/05; H10W70/62; H10W70/66; H10W70/666
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
309 words
A method for producing a multilayered ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one inorganic material green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, and then forming at least one hole through the at least one green sheet comprising the inorganic material so that the at least one hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of an outermost low-temperature firing glass-ceramic green sheet of the laminate, laminating said at least one inorganic material green sheet having the at least one hole on one of the outermost low-temperature firing glass-ceramic green sheets of the laminate to produce a resultant laminate wherein the at least one hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of an outermost low-temperature firing glass-ceramic green sheets of the laminate, firing the resultant laminate comprising the inorganic material green sheet with the at least one hole at the firing temperature of the low-temperature glass-ceramic substrate material, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 2
Independent Claim
309 words
A method for producing a multilayered ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one inorganic material green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, and then forming at least one hole through the at least one green sheet comprising the inorganic material so that the at least one hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of an outermost low-temperature firing glass-ceramic green sheet of the laminate, laminating said at least one inorganic material green sheet having the at least one hole on one of the outermost low-temperature firing glass-ceramic green sheets of the laminate to produce a resultant laminate wherein the at least one hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of an outermost low-temperature firing glass-ceramic green sheets of the laminate, firing the resultant laminate comprising the inorganic material green sheet with the at least one hole at the firing temperature of the low-temperature glass-ceramic substrate material, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 3
Dependent Claim
56 words
The method according to claim 1 wherein a pair of the green sheets each comprising the inorganic material and having at least one hole are laminated on both of the outermost low-temperature firing glass-ceramic green sheets of the laminate so that the laminate is sandwiched by the pair of the green sheets comprising the inorganic material.
Claim 4
Dependent Claim
27 words
The method according to claim 1 wherein at least one hole in the green sheet comprising the inorganic material has a diameter of 0.1 to 5 mm.
Claim 5
Dependent Claim
19 words
The method according to claim 1 wherein the firing temperature is in a range of 800° to 1000° C.
Claim 6
Dependent Claim
49 words
The method according to claim 1 wherein at least one green sheet comprising the inorganic material which is not sintered at the firing temperature comprises at least one selected from the group consisting of Al 2 O 3 , MgO, ZrO 2 , TiO 2 , BeO and BN.
Claim 7
Dependent Claim
32 words
The method according to claim 1 wherein the conductor paste composition comprises, as a main component, one selected from the group consisting of Ag, Cu and a mixture of Ag and Pd.
Claim 8
Independent Claim
351 words
A method for producing a low-temperature firing multilayered glass-ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition comprising cupric oxide as a main component to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition comprising cupric oxide as a main component, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one inorganic material green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, and then forming at least one hole through the at least one green sheet comprising the inorganic material so that the at least one hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of an outermost low-temperature firing glass-ceramic green sheet of the laminate, laminating said at least one inorganic material green sheet having the at least one hole on one of the outermost low-temperature firing glass-ceramic green sheets of the laminate to produce a resultant laminate wherein the hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of the outermost low-temperature firing glass-ceramic green sheets of the laminate, heating the resultant laminate in an oxidizing atmosphere at a temperature at which the organic binder of the green sheets and an organic component of the conductor paste composition are decomposed and burnt off, and then subjecting the heated laminate to a reduction treatment under a reducing atmosphere, firing the laminate under an inert atmosphere, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 9
Independent Claim
351 words
A method for producing a low-temperature firing multilayered glass-ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition comprising cupric oxide as a main component to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition comprising cupric oxide as a main component, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one inorganic material green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, and then forming at least one hole through the at least one green sheet comprising the inorganic material so that the at least one hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of an outermost low-temperature firing glass-ceramic green sheet of the laminate, laminating said at least one inorganic material green sheet having the at least one hole on one of the outermost low-temperature firing glass-ceramic green sheets of the laminate to produce a resultant laminate wherein the hole is positioned over a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of the outermost low-temperature firing glass-ceramic green sheets of the laminate, heating the resultant laminate in an oxidizing atmosphere at a temperature at which the organic binder of the green sheets and an organic component of the conductor paste composition are decomposed and burnt off, and then subjecting the heated laminate to a reduction treatment under a reducing atmosphere, firing the laminate under an inert atmosphere, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 10
Dependent Claim
25 words
The method according to claim 7 wherein the hole in the green sheet comprising the inorganic material has a diameter of 0.1 to 5 mm.
Claim 11
Dependent Claim
39 words
The method according to claim 7 wherein a top layer wiring pattern is formed on the substrate with a Cu paste composition after the firing step and then the substrate is fired in an atmosphere essentially consisting of nitrogen.
Claim 12
Dependent Claim
19 words
The method according to claim 7 wherein the firing temperature is in a range of 800° to 1000° C.
Claim 13
Dependent Claim
49 words
The method according to claim 7 wherein at least one green sheet comprising the inorganic material which is not sintered at the firing temperature comprises at least one selected from the group consisting of Al 2 O 3 , MgO, ZrO 2 , TiO 2 , BeO and BN.
Claim 14
Independent Claim
248 words
A method for producing a multilayered ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one organic resin layer over at least a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of the outermost low-temperature firing glass-ceramic green sheets of the substrate which layer is decomposed and burnt off during a subsequent firing step of the laminate, forming at least one green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, laminating the at least one green sheet comprising the inorganic material on the laminate having the at least one organic resin layer to obtain a resultant laminate, firing the said resultant laminate having the at least one green sheet comprising the inorganic material, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 15
Independent Claim
248 words
A method for producing a multilayered ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one organic resin layer over at least a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of the outermost low-temperature firing glass-ceramic green sheets of the substrate which layer is decomposed and burnt off during a subsequent firing step of the laminate, forming at least one green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, laminating the at least one green sheet comprising the inorganic material on the laminate having the at least one organic resin layer to obtain a resultant laminate, firing the said resultant laminate having the at least one green sheet comprising the inorganic material, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 16
Dependent Claim
57 words
The method according to claim 12 wherein a pair of the green sheets each comprising the inorganic material are laminated on both of the outermost low-temperature firing glass-ceramic green sheets each of which has an organic resin layer formed thereon so that the laminate is sandwiched by the pair of the green sheets comprising the inorganic material.
Claim 17
Dependent Claim
19 words
The method according to claim 12 wherein the firing temperature is in a range of 800° to 1000° C.
Claim 18
Dependent Claim
49 words
The method according to claim 12 wherein at least one green sheet comprising the inorganic material which is not sintered at the firing temperature comprises at least one selected from the group consisting of Al 2 O 3 , MgO, ZrO 2 , TiO 2 , BeO and BN.
Claim 19
Dependent Claim
32 words
The method according to claim 12 wherein the conductor paste composition comprises, as a main component, one selected from the group consisting of Ag, Cu and a mixture of Ag and Pd.
Claim 20
Independent Claim
291 words
A method for producing a multilayered ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition comprising cupric oxide as a main component to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition comprising cupric oxide as a main component, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one organic resin layer over at least a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of the outermost green sheets comprising the glass-ceramic substrate material which layer is decomposed and burnt off during a subsequent heating step of the laminate, forming at least one green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, laminating the at least one green sheet comprising the inorganic material on the laminate having the at least one organic resin layer to obtain a resultant laminate, heating the resultant laminate in an oxidizing atmosphere at a temperature at which the organic binder of the green sheets is decomposed and burnt off, and then the heated laminate is subject to reduction treatment under a reducing atmosphere, firing the laminate under an inert atmosphere, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 21
Independent Claim
291 words
A method for producing a multilayered ceramic substrate comprising the steps of: forming at least two green sheets each of which comprises a low-temperature firing glass-ceramic substrate material, an organic binder and a plasticizer, forming at least one via hole through each of said green sheets, and then filling said at least one via hole with a conductor paste composition comprising cupric oxide as a main component to form at least one via electrode, forming at least one electrode pattern on each of said green sheets with the conductor paste composition comprising cupric oxide as a main component, laminating said green sheets to obtain a laminate having a predetermined wiring structure and having outermost low-temperature firing glass-ceramic green sheets, forming at least one organic resin layer over at least a portion of at least one of the at least one electrode pattern and the at least one via electrode of one of the outermost green sheets comprising the glass-ceramic substrate material which layer is decomposed and burnt off during a subsequent heating step of the laminate, forming at least one green sheet which comprises an inorganic material which is not sintered at a firing temperature of the low-temperature firing glass-ceramic substrate material or lower, laminating the at least one green sheet comprising the inorganic material on the laminate having the at least one organic resin layer to obtain a resultant laminate, heating the resultant laminate in an oxidizing atmosphere at a temperature at which the organic binder of the green sheets is decomposed and burnt off, and then the heated laminate is subject to reduction treatment under a reducing atmosphere, firing the laminate under an inert atmosphere, and removing the at least one inorganic material green sheet from the fired laminate.
Claim 22
Dependent Claim
39 words
The method according to claim 17 wherein a top layer wiring pattern is formed on the substrate with a Cu paste composition after the firing step and then the substrate is fired in an atmosphere essentially consisting of nitrogen.
Claim 23
Dependent Claim
19 words
The method according to claim 17 wherein the firing temperature is in a range of 800° to 1000° C.
Claim 24
Dependent Claim
49 words
The method according to claim 17 wherein at least one green sheet comprising the inorganic material which is not sintered at the firing temperature comprises at least one selected from the group consisting of Al 2 O 3 , MgO, ZrO 2 , TiO 2 , BeO and BN.
Claim 25
Dependent Claim
21 words
The method according to claim 17 wherein the removal of the inorganic material is carried out using a ultrasonic cleaning method.
Claim 26
Dependent Claim
15 words
The method according to claim 17 wherein the substrate is fired while it is pressed.
References Cited (Backward Citations)
US3879509A
Cited
US4642148A
Cited
JPS6116749A
Cited
US4863683A
Cited
JPS625848A
Cited
JPS62260777A
Cited
US4753694A
Cited
US4879156A
Cited
US5130067A
Cited
US5085720A
Cited
JPH04243978A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-12-05 | 1998-06-06 | 1998-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-12-05 | 2002-06-06 | 2002-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-12-05 | 2006-06-06 | 2006-12-06 | $7700.00 | Window Closed / Lapsed |