Abstract
Abstract The present invention has as its object providing a solder mask which permits high density mounting, is suitable for protecting conductor circuits, particularly has mask thickness on the circuit parts and each edge part of the circuits which make almost no difference from those on other parts, and is excellent in electrical insulation, heat resistance and solvent resistance. This invention provides a method of forming a solder mask for printed circuit boards, using any powder paint which is curable by both irradiation of ultraviolet ray and heat, comprising: (1) a step of coating the powder paint on a printed circuit board, while holding it at a temperature higher than a softening point of the powder paint, (2) a step of irradiating ultraviolet rays thereon through a pattern mask, (3) a step of making development with a medium which dissolves the region not irradiated by ultraviolet rays and, (4) a step of completely curing the coating part developed on the printed circuit board at a temperature higher than the curing temperature of the powder paint.
Inventors
- 👤 Yoshikazu Yamagami
- 👤 Akio Kashihara
- 👤 Mamoru Seio
- 👤 Hisaki Tanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:54
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/16; G03F7/164; H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K2203/00; H05K2203/11; H05K2203/1105; H05K2203/13; H05K2203/1333; H05K2203/1355; H05K3/0073; H05K3/0079
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
266 words
A method of forming a solder mask on printed circuit boards, using powder paint which is curable by both irradiation of ultraviolet rays and heat, comprising: (1) a step of coating the powder paint on a printed circuit board, while holding it at a temperature higher than a softening point of the powder paint but lower than its curing temperature, (2) a step of irradiating ultraviolet rays thereon through a pattern mask, (3) a step of making development with a medium which dissolves the region not irradiated by ultraviolet rays and, (4) a step of completely curing the coating part developed on the printed circuit board at a temperature higher than the curing temperature of the powder paint, wherein said powder paint comprises: (i) 30-90 parts by weight of a resin with its number average molecular weight larger than 1000 and being in solid state at the normal temperature, which has 0.1-3 radically polymerizable unsaturated groups and 0.1-5 functional groups which undergo self-setting reaction or react with other functional groups under heating in molecules having a 1000 number average molecular weight, (ii) 70-10 parts by weight of compounds with their number average molecular weight smaller than 1000 and being in solid state at the normal temperature, which have a plurality of radically polymerizable unsaturated groups and (iii) 0.1-10 parts by weight of photopolymerization initiator in proportion to 100 parts by weight of the sum of the components (i) and (ii) mixed therewith, and wherein a crystalline resin having a phase transition temperature of 60°-120° C. is used as part of the resin of the component (i).
Claim 2
Independent Claim
266 words
A method of forming a solder mask on printed circuit boards, using powder paint which is curable by both irradiation of ultraviolet rays and heat, comprising: (1) a step of coating the powder paint on a printed circuit board, while holding it at a temperature higher than a softening point of the powder paint but lower than its curing temperature, (2) a step of irradiating ultraviolet rays thereon through a pattern mask, (3) a step of making development with a medium which dissolves the region not irradiated by ultraviolet rays and, (4) a step of completely curing the coating part developed on the printed circuit board at a temperature higher than the curing temperature of the powder paint, wherein said powder paint comprises: (i) 30-90 parts by weight of a resin with its number average molecular weight larger than 1000 and being in solid state at the normal temperature, which has 0.1-3 radically polymerizable unsaturated groups and 0.1-5 functional groups which undergo self-setting reaction or react with other functional groups under heating in molecules having a 1000 number average molecular weight, (ii) 70-10 parts by weight of compounds with their number average molecular weight smaller than 1000 and being in solid state at the normal temperature, which have a plurality of radically polymerizable unsaturated groups and (iii) 0.1-10 parts by weight of photopolymerization initiator in proportion to 100 parts by weight of the sum of the components (i) and (ii) mixed therewith, and wherein a crystalline resin having a phase transition temperature of 60°-120° C. is used as part of the resin of the component (i).
Claim 3
Dependent Claim
62 words
The method according to claim 1, wherein in the step of irradiating ultraviolet rays through a pattern mask, ultraviolet rays are irradiated on the printed circuit board, without allowing the pattern mask to be in contact with the printed circuit board, while holding it at a temperature higher than the softening point of said powdery paint but lower than its curing temperature.
Claim 4
Dependent Claim
53 words
The method according to claim 1 wherein after finishing the step (1), the powder paint on the printed circuit board is made into a continuous coating by controlling the temperature of the printed circuit board to a temperature higher than a softening point of the powder paint but lower than its curing temperature.
Claim 5
Dependent Claim
23 words
The method according to claim 1 wherein, after finishing the step (1), the printed circuit board having the powder coating layer is quenched.
Claim 6
Independent Claim
147 words
A method of forming a solder mask on printed circuit boards using powder paint which is curable by both irradiation of ultraviolet rays and heat, comprising: (1-a) a step of putting on a printed circuit board 1-1000 mg/dm 2 of an organic solvent whose contact angle with the conductor and the insulating substrate is smaller than 20 degrees, (1-b) a step of coating on a printed circuit board having the organic solvent the powder paint which gives an SP value less than 3 between it and the organic solvent, (2) a step of irradiating ultraviolet rays thereon through a pattern mask, (3) a step of making development with a medium which dissolves the region not irradiated by ultraviolet rays and, (4) a step of completely curing the coating part developed on the printed circuit board at a temperature higher than the curing temperature of the powder paint.
Claim 7
Independent Claim
147 words
A method of forming a solder mask on printed circuit boards using powder paint which is curable by both irradiation of ultraviolet rays and heat, comprising: (1-a) a step of putting on a printed circuit board 1-1000 mg/dm 2 of an organic solvent whose contact angle with the conductor and the insulating substrate is smaller than 20 degrees, (1-b) a step of coating on a printed circuit board having the organic solvent the powder paint which gives an SP value less than 3 between it and the organic solvent, (2) a step of irradiating ultraviolet rays thereon through a pattern mask, (3) a step of making development with a medium which dissolves the region not irradiated by ultraviolet rays and, (4) a step of completely curing the coating part developed on the printed circuit board at a temperature higher than the curing temperature of the powder paint.
Claim 8
Dependent Claim
53 words
The method according to claim 5 wherein after finishing the step (1-b), the powder paint on the printed circuit board is made into a continuous coating by controlling the temperature of the printed circuit board to a temperature higher than a softening point of the powder paint but lower than its curing temperature.
Claim 9
Dependent Claim
22 words
The method according to claim 5 wherein in the step (1-b), coating is conducted at a temperature of 5° to 90° C.
Claim 10
Dependent Claim
23 words
The method according to claim 7 wherein, after finishing the step (1-b), the printed circuit board having the powder coating layer is quenched.
Claim 11
Dependent Claim
130 words
The method according to claim 5 wherein said powder paint comprises (i) 30-90 parts by weight of a resin with its number average molecular weight larger than 1000 and being in solid state at the normal temperature, which has 0.1-3 radically polymerizable unsaturated groups and 0.1-5 functional groups which undergo self-setting reaction or react with other functional groups under heating in molecules having a 1000 number average molecular weight, (ii) 70-10 parts by weight of compounds with their number average molecular weight smaller than 1000 and being in solid state at the normal temperature, which have a plurality of radically polymerizable unsaturated groups and (ii) 0.1-10 parts by weight of photopolymerization initiator in proportion to 100 parts by weight of the sum of the components (i) and (ii) mixed therewith.
Claim 12
Dependent Claim
29 words
The method according to claim 9 wherein a crystalline resin having a phase transition temperature of 60°-120° C. is used as part of the resin of the component (1).
References Cited (Backward Citations)
US4216246A
Cited
US4469777A
Cited
US4567062A
Cited
US4894317A
Cited
EP0286594A2
Cited
WO1991003770A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-11-28 | 1998-05-30 | 1998-11-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-11-28 | 2002-05-30 | 2002-11-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-11-28 | 2006-05-30 | 2006-11-29 | $7700.00 | Window Closed / Lapsed |