Dry etching method for W polycide using sulfur deposition
Assignee: Sony Corp
•
Filing: 1992-06-16
•
Granted: 1994-11-29
•
Expires: 2012-06-16
Abstract
Abstract A dry etching method for anisotropically etching a polycide film without using chlorofluorocarbon (CFC). For instance, in a W polycide gate electrode forming process, a W polycide film is etched by using sulfur fluorides, like S2F2, with a high S/F ratio (i.e. the ratio of the number of sulfur atoms to that of fluorine atoms). In a first step, at least the upper WSix layer of the W polycide film is etched with the wafer kept at temperatures between -20 DEG C. and room temperature or with non-depositional fluorine based compounds like SF6 added to etching gas, thus decreasing the S/F ratio of the etching system. This first step promotes elimination of WFx and reduces the quantity of free sulfur. Therefore, WFx is inhibited from reacting with sulfur to form WSx for deposition in excessive quantities on the sidewalls of the WSix pattern, thus preventing occurrence of critical dimension losses between the resist mask and the W polycide gate electrode. In a second step, the lower polysilicon layer of the W polycide film is etched with the wafer cooled to lower temperatures or with H2S, etc. added to etching gas, thus increasing the S/F ratio of the etching system. This second step promotes deposition of sulfur on the sidewalls of the polycide pattern and improves anisotropy.
Inventors
- 👤 Tetsuya Tatsumi
- 👤 Tetsuji Nagayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:52
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268; Y; Y10; Y10S; Y10S438/00; Y10S438/963
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
102 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising plasma etching at least said refractory metal silicide layer to form sidewalls by using an etching gas containing at least one sulfur fluoride selected from a group consisting of S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 ; and inhibiting the formation of refractory metal sulfides on the metal silicide sidewalls while depositing sulfur on the silicon sidewalls.
Claim 2
Dependent Claim
102 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising plasma etching at least said refractory metal silicide layer to form sidewalls by using an etching gas containing at least one sulfur fluoride selected from a group consisting of S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 ; and inhibiting the formation of refractory metal sulfides on the metal silicide sidewalls while depositing sulfur on the silicon sidewalls.
Claim 3
Dependent Claim
48 words
A dry etching method as claimed in claim 1 wherein said substrate is a single-crystal silicon substrate coated on the surface thereof with a gate oxide film, said silicon based material layer is an impurity-doped polysilicon layer, and said refractory metal silicide layer is a tungsten silicide layer.
Claim 4
Dependent Claim
135 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer by using etching gas containing at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 with said substrate kept at temperatures between -20° C. and room temperature to inhibit formation of refractory metal sulfides on the metal silicide sidewalls, and a second step of plasma etching said silicon based material layer with said substrate being kept at lower temperatures than in said first step to deposit sulfur on the silicon sidewalls that are being formed.
Claim 5
Dependent Claim
135 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer by using etching gas containing at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 with said substrate kept at temperatures between -20° C. and room temperature to inhibit formation of refractory metal sulfides on the metal silicide sidewalls, and a second step of plasma etching said silicon based material layer with said substrate being kept at lower temperatures than in said first step to deposit sulfur on the silicon sidewalls that are being formed.
Claim 6
Dependent Claim
48 words
A dry etching method as claimed in claim 3 wherein said substrate is a single-crystal silicon substrate coated on the surface thereof with a gate oxide film, said silicon based material layer is an impurity-doped polysilicon layer, and said refractory metal silicide layer is a tungsten silicide layer.
Claim 7
Dependent Claim
161 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer to form sidewalls by using an etching gas containing at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 with said substrate kept at temperatures between -20° C. and room temperature to inhibit formation of refractory metal sulfides on the metal silicide sidewalls, and a second step of plasma etching said silicon based material layer by using said etching gas further containing at least one fluorine radical consuming compound selected from H 2 , H 2 S, and silane based compounds to increase the ratio of S to F and to deposit sulfur on sidewalls of the silicon based material layer.
Claim 8
Dependent Claim
161 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer to form sidewalls by using an etching gas containing at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 with said substrate kept at temperatures between -20° C. and room temperature to inhibit formation of refractory metal sulfides on the metal silicide sidewalls, and a second step of plasma etching said silicon based material layer by using said etching gas further containing at least one fluorine radical consuming compound selected from H 2 , H 2 S, and silane based compounds to increase the ratio of S to F and to deposit sulfur on sidewalls of the silicon based material layer.
Claim 9
Dependent Claim
48 words
A dry etching method as claimed in claim 5 wherein said substrate is a single-crystal silicon substrate coated on the surface thereof with a gate oxide film, said silicon based material layer is an impurity-doped polysilicon layer, and said refractory metal silicide layer is a tungsten silicide layer.
Claim 10
Dependent Claim
103 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising plasma etching at least said refractory metal silicide layer by using an etching gas containing a non-depositional fluorine based compound and at least one sulfur fluoride selected from the group consisting of S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 to inhibit the formation of refractory metal sulfides on the metal silicide while depositing sulfur on the silicon sidewalls.
Claim 11
Dependent Claim
103 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising plasma etching at least said refractory metal silicide layer by using an etching gas containing a non-depositional fluorine based compound and at least one sulfur fluoride selected from the group consisting of S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 to inhibit the formation of refractory metal sulfides on the metal silicide while depositing sulfur on the silicon sidewalls.
Claim 12
Dependent Claim
35 words
A dry etching method as claimed in claim 7 wherein said non-depositional fluorine based compound is at least one compound selected from SF 6 , NF 3 , F 2 , and CF 4 .
Claim 13
Dependent Claim
48 words
A dry etching method as claimed in claim 7 wherein said substrate is a single-crystal silicon substrate coated on the surface thereof with a gate oxide film, said silicon based material layer is an impurity-doped polysilicon layer, and said refractory metal silicide layer is a tungsten silicide layer.
Claim 14
Dependent Claim
133 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer by using an etching gas containing a non-depositional fluorine based compound and at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 to inhibit the formation of refractory metal sulfides on the metal silicide sidewall, and a second step of plasma etching said silicon based material layer with said substrate being kept at lower temperatures than in said first step to deposit sulfur on sidewalls being formed in the silicon based material layer.
Claim 15
Dependent Claim
133 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer by using an etching gas containing a non-depositional fluorine based compound and at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 to inhibit the formation of refractory metal sulfides on the metal silicide sidewall, and a second step of plasma etching said silicon based material layer with said substrate being kept at lower temperatures than in said first step to deposit sulfur on sidewalls being formed in the silicon based material layer.
Claim 16
Dependent Claim
35 words
A dry etching method as claimed in claim 10 wherein said non-depositional fluorine based compound is at least one compound selected from SF 6 , NF 3 , F 2 , and CF 4 .
Claim 17
Dependent Claim
48 words
A dry etching method as claimed in claim 10 wherein said substrate is a single-crystal silicon substrate coated on the surface thereof with a gate oxide film, said silicon based material layer is an impurity-doped polysilicon layer, and said refractory metal silicide layer is a tungsten silicide layer.
Claim 18
Dependent Claim
151 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer by using an etching gas containing a non-depositional fluorine based compound and at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 to inhibit formation of refractory metal sulfides on the metal silicide sidewalls, and a second step of plasma etching said silicon based material layer by using an etching gas containing said sulfur fluoride and at least one fluorine radical consuming compound selected from H 2 , H 2 S, and silane based compounds to increase the S to F ratio and deposit sulfur on said silicon sidewalls being etched.
Claim 19
Dependent Claim
151 words
A dry etching method for etching a polycide film formed of at least a silicon based material layer and a refractory metal silicide layer which are fabricated in this order on a substrate, said method comprising: a first step of plasma etching said refractory metal silicide layer by using an etching gas containing a non-depositional fluorine based compound and at least one sulfur fluoride selected from S 2 F 2 , SF 2 , SF 4 , and S 2 F 10 to inhibit formation of refractory metal sulfides on the metal silicide sidewalls, and a second step of plasma etching said silicon based material layer by using an etching gas containing said sulfur fluoride and at least one fluorine radical consuming compound selected from H 2 , H 2 S, and silane based compounds to increase the S to F ratio and deposit sulfur on said silicon sidewalls being etched.
Claim 20
Dependent Claim
35 words
A dry etching method as claimed in claim 13 wherein said non-depositional fluorine based compound is at least one compound selected from SF 6 , NF 3 , F 2 , and CF 4 .
Claim 21
Dependent Claim
48 words
A dry etching method as claimed in claim 13 wherein said substrate is a single-crystal silicon substrate coated on the surface thereof with a gate oxide film, said silicon based material layer is an impurity-doped polysilicon layer, and said refractory metal silicide layer is a tungsten silicide layer.
References Cited (Backward Citations)
JPS58204537A
Cited
JPS63163A
Cited
US4943344A
Cited
US4986877A
Cited
JPH01166539A
Cited
JPH0496224A
Cited
US5118387A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-11-28 | 1998-05-30 | 1998-11-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-11-28 | 2002-05-30 | 2002-11-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-11-28 | 2006-05-30 | 2006-11-29 | $7700.00 | Window Closed / Lapsed |