Process for producing a blue emitting lamp phosphor
Assignee: Osram Sylvania Inc
•
Filing: 1993-11-24
•
Granted: 1994-10-25
•
Expires: 2013-11-24
Abstract
Abstract A fluorescent lamp comprising a sealed envelope, a pair of opposing electrodes, a fill of inert gas and mercury and a phosphor coating on the internal walls of the envelope wherein the coating contains as at least one element thereof particles of europium activated barium magnesium aluminate having an average particle size of about 4 micrometers, less than about 5% of the particles having a size greater than 15 microns and less than about 5% of the particles having a size less than about 1 micron, said particles having on the external surfaces thereof a coating of sub-micron aluminum oxide having a surface area of from about 80 to about 120 square meters per gram, said coating being sufficient to impart stir in quality to said phosphor.
Inventors
- 👤 Joseph J. Lenox
- 👤 Albert K. Fan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:23
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/02; C09K11/025; C09K11/08; C09K11/77; C09K11/7728; C09K11/7734; H; H01; H01J; H01J61/00; H01J61/02; H01J61/38; H01J61/42; H01J61/44; H01J61/46
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
215 words
A process for producing a phosphor, comprising the steps of: a) forming a relatively uniform admixture of (1) a source of aluminum oxide, (2) a source of magnesium oxide, (3) barium halide, (4) a source of europium oxide, and (5) barium carbonate, wherein the atomic ratio of magnesium to aluminum in said admixture is 0.942:11 and the atomic ratio of europium to aluminum is from 0.086:11 to 0.12:11 and the atomic ratio of barium to aluminum is from about 0.6:11 to about 0.65:11 and the molar ratio of said barium halide to barium carbonate is from about 14:86 to about 16:84; b) firing said admixture at a temperature of from about 1625° C. to about 1675° C. for at least about 3 hours in a mildly reducing atmosphere of hydrogen-nitrogen to form a fired material; and c) dry milling said fired material by vibratory milling of said fired material in the presence of a finely divided aluminum oxide having a particle size below 1 micron and a surface area of from about 85 to about 115 square meters per gram to thereby crush and deagglomerate said fired material to form particles of said fired material and coat said particles with a coating of finely divided aluminum oxide sufficient to impart stir-in qualities to said phosphor.
Claim 2
Dependent Claim
215 words
A process for producing a phosphor, comprising the steps of: a) forming a relatively uniform admixture of (1) a source of aluminum oxide, (2) a source of magnesium oxide, (3) barium halide, (4) a source of europium oxide, and (5) barium carbonate, wherein the atomic ratio of magnesium to aluminum in said admixture is 0.942:11 and the atomic ratio of europium to aluminum is from 0.086:11 to 0.12:11 and the atomic ratio of barium to aluminum is from about 0.6:11 to about 0.65:11 and the molar ratio of said barium halide to barium carbonate is from about 14:86 to about 16:84; b) firing said admixture at a temperature of from about 1625° C. to about 1675° C. for at least about 3 hours in a mildly reducing atmosphere of hydrogen-nitrogen to form a fired material; and c) dry milling said fired material by vibratory milling of said fired material in the presence of a finely divided aluminum oxide having a particle size below 1 micron and a surface area of from about 85 to about 115 square meters per gram to thereby crush and deagglomerate said fired material to form particles of said fired material and coat said particles with a coating of finely divided aluminum oxide sufficient to impart stir-in qualities to said phosphor.
Claim 3
Dependent Claim
26 words
A process according to claim 1 wherein said finely divided aluminum oxide constitutes from about 0.3% to about 1% by weight of the total phosphor composition.
Claim 4
Dependent Claim
26 words
A process according to claim 1 wherein said finely divided aluminum oxide constitutes from about 0.4% to about 0.6% by weight of the total phosphor composition.
Claim 5
Dependent Claim
212 words
A process for producing a phosphor, comprising the steps of: a) forming a relatively uniform admixture of (1) a source of aluminum oxide, (2) a source of magnesium oxide, (3) barium halide, (4) a source of europium oxide, and (5) barium carbonate, wherein the atomic ratio of magnesium to aluminum in said admixture is 0.942:11 and the atomic ratio of europium to aluminum is 0.12:11 and the atomic ratio of barium to aluminum is from about 0.6:11 to about 0.65:11 and the molar ratio of said barium halide to barium carbonate is from about 14:86 to about 16:84; b) firing said admixture at a temperature of from about 1625° C. to about 1675° C. for at least about 3 hours in a mildly reducing atmosphere of hydrogen-nitrogen to form a fired material; and c) dry milling said fired material by vibratory milling of said fired material in the presence of a finely divided aluminum oxide having a particle size below 1 micron and a surface area of from about 85 to about 115 square meters per gram to thereby crush and deagglomerate said fired material to form particles of said fired material and coat said particles with a coating of finely divided aluminum oxide sufficient to impart stir-in qualities to said phosphor.
Claim 6
Dependent Claim
212 words
A process for producing a phosphor, comprising the steps of: a) forming a relatively uniform admixture of (1) a source of aluminum oxide, (2) a source of magnesium oxide, (3) barium halide, (4) a source of europium oxide, and (5) barium carbonate, wherein the atomic ratio of magnesium to aluminum in said admixture is 0.942:11 and the atomic ratio of europium to aluminum is 0.12:11 and the atomic ratio of barium to aluminum is from about 0.6:11 to about 0.65:11 and the molar ratio of said barium halide to barium carbonate is from about 14:86 to about 16:84; b) firing said admixture at a temperature of from about 1625° C. to about 1675° C. for at least about 3 hours in a mildly reducing atmosphere of hydrogen-nitrogen to form a fired material; and c) dry milling said fired material by vibratory milling of said fired material in the presence of a finely divided aluminum oxide having a particle size below 1 micron and a surface area of from about 85 to about 115 square meters per gram to thereby crush and deagglomerate said fired material to form particles of said fired material and coat said particles with a coating of finely divided aluminum oxide sufficient to impart stir-in qualities to said phosphor.
Claim 7
Dependent Claim
212 words
A process for producing a phosphor, comprising the steps of: a) forming a relatively uniform admixture of (1) a source of aluminum oxide, (2) a source of magnesium oxide, (3) barium halide, (4) a source of europium oxide, and (5) barium carbonate, wherein the atomic ratio of magnesium to aluminum in said admixture is 0.942:11 and the atomic ratio of europium to aluminum is 0.086:11 and the atomic ratio of barium to aluminum is from about 0.6:11 to about 0.65:11 and the molar ratio of said barium halide to barium carbonate is from about 14:86 to about 16:84; b) firing said admixture at a temperature of from about 1625° C. to about 1675° C. for at least about 3 hours in a mildly reducing atmosphere of hydrogen-nitrogen to form a fired material; and c) dry milling said fired material by vibratory milling of said fired material in the presence of a finely divided aluminum oxide having a particle size below 1 micron and a surface area of from about 85 to about 115 square meters per gram to thereby crush and deagglomerate said fired material to form particles of said fired material and coat said particles with a coating of finely divided aluminum oxide sufficient to impart stir-in qualities to said phosphor.
Claim 8
Dependent Claim
212 words
A process for producing a phosphor, comprising the steps of: a) forming a relatively uniform admixture of (1) a source of aluminum oxide, (2) a source of magnesium oxide, (3) barium halide, (4) a source of europium oxide, and (5) barium carbonate, wherein the atomic ratio of magnesium to aluminum in said admixture is 0.942:11 and the atomic ratio of europium to aluminum is 0.086:11 and the atomic ratio of barium to aluminum is from about 0.6:11 to about 0.65:11 and the molar ratio of said barium halide to barium carbonate is from about 14:86 to about 16:84; b) firing said admixture at a temperature of from about 1625° C. to about 1675° C. for at least about 3 hours in a mildly reducing atmosphere of hydrogen-nitrogen to form a fired material; and c) dry milling said fired material by vibratory milling of said fired material in the presence of a finely divided aluminum oxide having a particle size below 1 micron and a surface area of from about 85 to about 115 square meters per gram to thereby crush and deagglomerate said fired material to form particles of said fired material and coat said particles with a coating of finely divided aluminum oxide sufficient to impart stir-in qualities to said phosphor.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-10-24 | 1998-04-25 | 1998-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-10-24 | 2002-04-25 | 2002-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-10-24 | 2006-04-25 | 2006-10-25 | $7700.00 | Window Closed / Lapsed |