Copper-based metallizations for hybrid integrated circuits
Assignee: Nokia Bell Labs
•
Filing: 1993-10-20
•
Granted: 1994-10-18
•
Expires: 2013-10-20
Abstract
Abstract A new metallization is described which is a composite of subsequent metal layers beginning with a layer of titanium and having in an ascending order the following composition: Ti--TiPd--Cu--Ni--Au. TiPd is an alloy of titanium and palladium containing from 0.3 to 14 weight percent Pd, by the weight of the alloy. The TiPd alloy is etchable in an aqueous HF solution containing from 0.5 to 2.0 and higher, preferably from 0.5 to 1.2 weight percent HF. The use of the TiPd alloy avoids the occurrence of Pd residues remaining after the etching of Ti layer and lift-off (rejection etching) of Pd layer in a prior art Ti--Pd--Cu--Ni--Au metallization. Ti and TiPd layers are present in a thickness ranging from 100 to 300 nm and from 50 to 300 nm, respectively, and in a total minimum thickness needed to maintain bonding characteristics of the metallization. The metallization is suitable for use in various circuits including integrated circuits (ICs), hybrid integrated circuits (HICs), film integrated circuits (FICs), multi-chip modules (MCMs), etc.
Inventors
- 👤 Robert P. Frankenthal
- 👤 Ajibola O. Ibidunni
- 👤 Dennis L. Krause
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 16:38
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H10; H10P; H10P50/00; C; C23; C23C; C23C28/00; C23C28/02; C23C28/021; C25; C25D; C25D5/00; C25D5/02; C25D5/022; C25D5/10; C25D5/12; H05K3/10; H05K3/108; H05K3/38; H05K3/388; H10W; H10W70/00; H10W70/60; H10W70/62; H10W70/66; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0723; H05K3/02; H05K3/06; H05K3/061; H05K3/062; H05K3/243
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
149 words
A method of forming electrical interconnections between conductive elements on the major surface of an insulating substrate, which comprises; depositing on the substrate a first metal layer comprising titanium, depositing over said first metal layer a second metal layer comprising an alloy of titanium and palladium, said alloy comprising 0.3-14 weight percent palladium, remainder being essentially titanium, depositing over said second metal layer a third metal layer comprising copper, said depositing including first forming a thin film of copper on said second metal layer and then electroplating additional copper on selected portions of said thin film, electroplating a fourth metal layer comprising nickel over the electroplated copper layer, electroplating a fifth metal layer comprising gold on at least preselected portions of said fourth layer, and removing those portions of said first and second layers and of said thin film of copper which are not covered by said electroplated metals.
Claim 2
Independent Claim
149 words
A method of forming electrical interconnections between conductive elements on the major surface of an insulating substrate, which comprises; depositing on the substrate a first metal layer comprising titanium, depositing over said first metal layer a second metal layer comprising an alloy of titanium and palladium, said alloy comprising 0.3-14 weight percent palladium, remainder being essentially titanium, depositing over said second metal layer a third metal layer comprising copper, said depositing including first forming a thin film of copper on said second metal layer and then electroplating additional copper on selected portions of said thin film, electroplating a fourth metal layer comprising nickel over the electroplated copper layer, electroplating a fifth metal layer comprising gold on at least preselected portions of said fourth layer, and removing those portions of said first and second layers and of said thin film of copper which are not covered by said electroplated metals.
Claim 3
Dependent Claim
118 words
The method of claim 1 wherein said first metal layer is deposited in a thickness within a range of 100 to 300 nm, said second metal layer is deposited in a thickness within a range of 50 to 300 nm, said thin film of the third metal layer is deposited in a thickness within a range of 300 to 700 nm, said additional metal of the third metal layer is electroplated on the thin film in a thickness adding to a total thickness of the third metal layer of 2500 to 4000 nm, said fourth metal layer is electroplated in a thickness of 800-2000 nm, and said fifth metal layer is electroplated in a thickness of 1500-2500 nm.
Claim 4
Dependent Claim
26 words
The method of claim 1 in which said forming of the first and second metal layers and of the thin metal film is conducted by sputtering.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein said sputtering of the titanium and palladium alloy is conducted from a titanium target including plugs of palladium.
Claim 6
Independent Claim
293 words
A method of forming a circuit including thin film elements and electrical interconnections on the major surface of an insulating substrate comprising the steps of: depositing onto substantially the entire major surface of said substrate a first metal layer consisting essentially of titanium in a thickness within the range 100-300 nm; depositing onto substantially the entire surface of said first metal layer a second metal layer consisting essentially of an alloy of titanium and palladium in a thickness within the range 50-300 nm, said alloy comprising 0.3-14 weight percent palladium, remainder being essentially titanium; depositing onto substantially the entire surface of said second metal layer a thin metal film consisting essentially of copper in a thickness within the range 300 to 700 nm; electroplating additional copper onto selected portions of said layer of copper in the desired interconnection pattern to produce a total Cu thickness within the range 2500-4000 nm, said thin film and electroplated copper forming a third metal layer; while said electroplated copper layer is still wet, electroplating a fourth metal layer consisting essentially of nickel on substantially the entire surface of said electroplated copper layer in a thickness within the range 800-2,000 nm utilizing a plating bath comprising nickel sulfamate; electroplating onto at least portions of said fourth metal layer a fifth metal layer consisting essentially of gold in a thickness within the range 700-2500 nm utilizing a plating bath comprising gold cyanide; removing portions of the copper layer not covered by at least one of said electroplated layers by immersing in an aqueous etching solution comprising ammoniacal solution; and removing portions of the titanium layer and titanium-palladium alloy layer not covered by at least one of said electroplated layers by immersing in an aqueous etching solution comprising hydrofluoric acid.
Claim 7
Independent Claim
293 words
A method of forming a circuit including thin film elements and electrical interconnections on the major surface of an insulating substrate comprising the steps of: depositing onto substantially the entire major surface of said substrate a first metal layer consisting essentially of titanium in a thickness within the range 100-300 nm; depositing onto substantially the entire surface of said first metal layer a second metal layer consisting essentially of an alloy of titanium and palladium in a thickness within the range 50-300 nm, said alloy comprising 0.3-14 weight percent palladium, remainder being essentially titanium; depositing onto substantially the entire surface of said second metal layer a thin metal film consisting essentially of copper in a thickness within the range 300 to 700 nm; electroplating additional copper onto selected portions of said layer of copper in the desired interconnection pattern to produce a total Cu thickness within the range 2500-4000 nm, said thin film and electroplated copper forming a third metal layer; while said electroplated copper layer is still wet, electroplating a fourth metal layer consisting essentially of nickel on substantially the entire surface of said electroplated copper layer in a thickness within the range 800-2,000 nm utilizing a plating bath comprising nickel sulfamate; electroplating onto at least portions of said fourth metal layer a fifth metal layer consisting essentially of gold in a thickness within the range 700-2500 nm utilizing a plating bath comprising gold cyanide; removing portions of the copper layer not covered by at least one of said electroplated layers by immersing in an aqueous etching solution comprising ammoniacal solution; and removing portions of the titanium layer and titanium-palladium alloy layer not covered by at least one of said electroplated layers by immersing in an aqueous etching solution comprising hydrofluoric acid.
Claim 8
Dependent Claim
116 words
The method according to claim 5, wherein said first metal layer is deposited in a thickness within a range of 100 to 300 rim, said second metal layer is deposited in a thickness within a range of 50 to 300 rim, said thin film of the third metal layer is deposited in a thickness within a range of 300 to 700 nm, said additional third metal layer is electroplated on the thin film in a thickness adding to a total thickness of the third metal layer of 2500 to 4000 nm, said fourth metal layer is electroplated in a thickness of 800-2000 nm, and said fifth metal layer is electroplated in a thickness of 1500-2500 nm.
Claim 9
Dependent Claim
14 words
The method according to claim 5, in which said depositing is accomplished by sputtering.
Claim 10
Dependent Claim
21 words
The method according to claim 5, wherein the fifth layer is formed on substantially the entire surface of said fourth layer.
Claim 11
Dependent Claim
27 words
The method according to claim 5, wherein the fifth layer is formed only on the areas of the fourth layer which comprise bonding pads for said circuit.
Claim 12
Dependent Claim
27 words
The method according to claim 5, wherein said solution for etching the titanium and titanium-palladium alloy layers comprises from 0.5 to 2 and more weight percent HF.
Claim 13
Dependent Claim
18 words
The method of claim 5, wherein said HF etching solution comprises from 0.5 to 1.2 weight percent HF.
References Cited (Backward Citations)
US4927505A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-10-17 | 1998-04-18 | 1998-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-10-17 | 2002-04-18 | 2002-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-10-17 | 2006-04-18 | 2006-10-18 | $7700.00 | Window Closed / Lapsed |