Method for hydrophilizing absorbent foam materials
Assignee: Procter and Gamble Co
•
Filing: 1991-08-12
•
Granted: 1994-10-04
•
Expires: 2011-08-12
Abstract
Abstract Normally hydrophobic foams, such as polyurethane foams and polymerized water-in-oil emulsion foams, are rendered hydrophilic by means of treatment with simple surfactants and hydrophilizing agent salts. Thus, a surfactant-containing foam is treated with a solution of, for example, calcium chloride, and is dried to leave a substantially uniformly distributed residue of hydrated or hydratable calcium chloride on the surfactant-containing internal foam surfaces. In-use, the combination of surfactant and calcium chloride hydrate provides a hydrophilic surface to the foam. Other hydratable calcium or magnesium salts such as magnesium chloride can be used. The resulting hydrophilized foams are suitable for use in absorbent devices, including diapers, sanitary napkins, bandages, and the like.
Inventors
- 👤 Thomas A. DesMarais
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:26
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/36; C08J9/40; A; A61; A61F; A61F13/00; A61F13/15; A61F13/53; A61L; A61L15/00; A61L15/16; A61L15/18; A61L15/42; A61L15/425; A61L15/48; C08J9/28; A61F13/15203; A61F2013/15284; A61F2013/15365; A61F2013/1539; A61F2013/530007; A61F2013/530036; A61F2013/530437; A61F2013/530452; A61F2013/530459; A61F2013/530467; A61F2013/530474; A61F2013/530481; A61F2013/530708; A61F2013/530802; A61F2013/53081; A61F2013/530817; A61F2013/530839; A61F2013/530854; C08J2201/00; C08J2201/04; C08J2201/05; C08J2207/00; C08J2207/12
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
121 words
A method for rendering substantially hydrophobic polymeric foam material suitable for absorbing hydrophilic liquids, which method comprises A) incorporating into a substantially hydrophobic polymeric foam material a substantially water-insoluble surfactant selected from the group consisting of sorbitan fatty acid esters, polyglycerol fatty acid esters and polyoxyethylene fatty acids and esters polyglycerol fatty acid esters and polyoxyethylene fatty acids and esters and a hydrophilizing salt solution formed from a solvent and a dissolved hydrophilizing salt selected from the group consisting of toxicologically acceptable, hydrated or hydratable calcium and magnesium slats; and B) thereafter drying said polymeric foam material to remove solvent therefrom and to thereby leave incorporated within said polymeric foam material a hydrophilizing amount of said surfactant and said hydrophilizing salt.
Claim 2
Independent Claim
121 words
A method for rendering substantially hydrophobic polymeric foam material suitable for absorbing hydrophilic liquids, which method comprises A) incorporating into a substantially hydrophobic polymeric foam material a substantially water-insoluble surfactant selected from the group consisting of sorbitan fatty acid esters, polyglycerol fatty acid esters and polyoxyethylene fatty acids and esters polyglycerol fatty acid esters and polyoxyethylene fatty acids and esters and a hydrophilizing salt solution formed from a solvent and a dissolved hydrophilizing salt selected from the group consisting of toxicologically acceptable, hydrated or hydratable calcium and magnesium slats; and B) thereafter drying said polymeric foam material to remove solvent therefrom and to thereby leave incorporated within said polymeric foam material a hydrophilizing amount of said surfactant and said hydrophilizing salt.
Claim 3
Dependent Claim
28 words
A method according to claim 1 wherein the solvent used to form the hydrolizing salt solution is selected from the group consisting of water, isopropanol and mixtures thereof.
Claim 4
Dependent Claim
24 words
A method according to claim 2 wherein the hydrophilizing salt is selected from the group consisting of calcium halides, magnesium halides and mixtures thereof.
Claim 5
Dependent Claim
15 words
A method according to claim 3 wherein the polymeric foam material is an open-celled foam.
Claim 6
Dependent Claim
33 words
A method according to claim 4 wherein the total amount of surfactant and hydrophilizing agent salt left incorporated within the foam material comprises at least about 0.05% by weight of the foam material.
Claim 7
Dependent Claim
32 words
A method according to claim 5 wherein the polymeric foam material is dried to the extent that it contains no more than about 50% by weight of the foam of free water.
Claim 8
Dependent Claim
15 words
A method according to claim 6 wherein the polymeric foam material is a polyurethane foam.
Claim 9
Dependent Claim
17 words
A method according to claim 6 wherein the polymeric foam material is a polymerized water-in-oil emulsion foam.
Claim 10
Dependent Claim
30 words
A method according to claim 8 wherein the polymeric foam material is formed from polymerized monomers selected from the group consisting of styrene, alkyl(meth)acrylates, divinylbenzene and combinations of these monomers.
Claim 11
Independent Claim
137 words
A method for rendering substantially hydrophobic polymeric foam material suitable for absorbing hydrophilic liquids, which method comprises A) incorporating an aqueous solution containing from about 1% to 10% by weight of calcium chloride in water into a polymeric foam material prepared by polymerizing a water-in-oil emulsion containing polymerizable monomers and from about 0.5% to 20% by weight of the polymerizable monomers of a surfactant selected from the group consisting of sorbitan monolaurate and mixtures of sorbitan monooleate and sorbitan trioleate in the oil phase of said emulsion; and B) thereafter drying said polymeric foam material to remove water therefrom and to leave incorporated within said foam material at least about 0.05% by weight of said foam material of surfactant plus calcium chloride and no more than about 50% by weight of said foam material of free water.
Claim 12
Independent Claim
137 words
A method for rendering substantially hydrophobic polymeric foam material suitable for absorbing hydrophilic liquids, which method comprises A) incorporating an aqueous solution containing from about 1% to 10% by weight of calcium chloride in water into a polymeric foam material prepared by polymerizing a water-in-oil emulsion containing polymerizable monomers and from about 0.5% to 20% by weight of the polymerizable monomers of a surfactant selected from the group consisting of sorbitan monolaurate and mixtures of sorbitan monooleate and sorbitan trioleate in the oil phase of said emulsion; and B) thereafter drying said polymeric foam material to remove water therefrom and to leave incorporated within said foam material at least about 0.05% by weight of said foam material of surfactant plus calcium chloride and no more than about 50% by weight of said foam material of free water.
Claim 13
Dependent Claim
70 words
A method according to claim 10 wherein A) the aqueous solution incorporated into the polymeric foam material contains from about 1% to 5% by weight calcium chloride; B) the dried polymeric foam material contains from about 0.1% to 7% by weight of said foam material of calcium chloride; and C) the dried polymeric foam material contains no more than about 10% by weight of said foam material of free water.
Claim 14
Dependent Claim
40 words
A method according to claim 11 wherein the polymerizable monomers in the oil phase of the water-in-oil emulsion used to form the polymeric foam material are selected from the group consisting of styrene, alkyl(meth)acrylates, divinylbenzene and combinations of these monomers.
Claim 15
Dependent Claim
112 words
A hydrophilized polymeric foam material suitable for absorbing hydrophilic liquids, said hydrophilized polymeric foam material comprising a substantially hydrophobic polymeric foam material; a hydrophilizing amount of at least about 0.05% by weight of said polymeric foam material of the combination of a substantially water-insoluble surfactant selected from the group consisting of sorbitan fatty acid esters, polyglycerol fatty acid esters and polyoxyethylene fatty acids and esters and a hydrophilizing salt selected from the group consisting of toxicologically acceptable, hydrated or hydratable calcium and magnesium salts, incorporated into aid polymeric foam material; and no more than about 50% by weight of said polymeric foam material of free water incorporated within said polymeric foam material.
Claim 16
Dependent Claim
112 words
A hydrophilized polymeric foam material suitable for absorbing hydrophilic liquids, said hydrophilized polymeric foam material comprising a substantially hydrophobic polymeric foam material; a hydrophilizing amount of at least about 0.05% by weight of said polymeric foam material of the combination of a substantially water-insoluble surfactant selected from the group consisting of sorbitan fatty acid esters, polyglycerol fatty acid esters and polyoxyethylene fatty acids and esters and a hydrophilizing salt selected from the group consisting of toxicologically acceptable, hydrated or hydratable calcium and magnesium salts, incorporated into aid polymeric foam material; and no more than about 50% by weight of said polymeric foam material of free water incorporated within said polymeric foam material.
Claim 17
Dependent Claim
18 words
A hydrophilized polymeric foam material according to claim 13 wherein the polymeric foam material is an open-celled foam.
Claim 18
Dependent Claim
28 words
A hydrophilized polymeric foam material according to claim 14 wherein the hydrophilizing agent salt is selected from the group consisting of calcium halides, magnesium halides and mixtures thereof.
Claim 19
Dependent Claim
85 words
A hydrophilized polymeric foam material according to claim 15 wherein the amount of surfactant incorporated within the foam material ranges from about 0.5% to 20% by weight of the foam material; the amount of hydrophilizing agent salt incorporated within the foam material ranges from about 0.1% to 7% by weight of the foam material; the amount of free water incorporated within the polymeric foam material comprises no more than about 10% by weight of said foam material; and the hydrophilizing agent salts are fully hydrated.
Claim 20
Dependent Claim
18 words
A hydrophilized polymeric foam material according to claim 16 wherein the polymeric foam material is a polyurethane-type foam.
Claim 21
Dependent Claim
19 words
A hydrophilized polymeric foam according to claim 16 wherein the polymeric foam material is a polymerized water-in-oil emulsion foam.
Claim 22
Dependent Claim
33 words
A hydrophilized polymeric foam material according to claim 18 wherein the polymeric foam material is formed from polymerized monomers selected from the group consisting of styrene, alkyl(meth)acrylates, divinylbenzene and combinations of these monomers.
Claim 23
Dependent Claim
36 words
A hydrophilized polymeric foam material according to claim 19 wherein the surfactant is selected from the group consisting of sorbitan monolaurate and mixtures of sorbitan monooleate and sorbitan trioleate and the hydrophilizing salt is calcium chloride.
References Cited (Backward Citations)
US3255127A
Cited
US3763056A
Cited
US4076656A
Cited
US3734867A
Cited
US4522953A
Cited
US4797310A
Cited
US4473611A
Cited
US4606958A
Cited
US4611014A
Cited
US4612334A
Cited
US4668709A
Cited
US4675213A
Cited
US4788225A
Cited
EP0299762A2
Cited
US5147345A
Cited
US5149720A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-10-03 | 1998-04-04 | 1998-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-10-03 | 2002-04-04 | 2002-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-10-03 | 2006-04-04 | 2006-10-04 | $7700.00 | Window Closed / Lapsed |