Spray conversion process for the production of nanophase composite powders
Assignee: Umicore NV SA
•
Filing: 1991-07-09
•
Granted: 1994-10-04
•
Expires: 2011-07-09
Abstract
Abstract A process is described for the production of composite powders with ultrafine microstructures. The process involves three coordinated steps: 1) preparation and mixing of an appropriate starting solution; 2) spray drying to form a chemically homogeneous precursor powder; and 3) fluid bed thermochemical conversion of the precursor into the desired nanophase composite powder. Both spray drying and fluid bed conversion are scaleable technologies, and together provide the means for producing bulk quantities of nanophase composite powders at low manufacturing cost. Processing parameters are controlled to ensure maintenance of chemical and microstructural uniformity at the nanoscale (less than 0.1 micron) level. Spray conversion processing is a versatile technology, which can be applied to a variety of metal-metal (e.g. W-Cu), ceramic-metal (e.g. WC-Co), and ceramic-ceramic (e.g. Al2O3-SiO2) nanophase composite powders ceramic-metal (e.g. WC-Co), and ceramic-ceramic (e.g. Al2O3-SiO2) nanophase composite powders.
Inventors
- 👤 Larry E. McCandlish
- 👤 Bernard H. Kear
- 👤 Swarn J. Bhatia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:16
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B01; B01D; B01D1/00; B01D1/16; B01D1/18; B01J; B01J8/00; B01J8/18; B01J8/1836; B22F1/00; B22F1/05; B22F1/054; B22F9/026; B22F9/16; B22F9/18; B22F9/20; B22F9/22; B82; B82Y; B82Y30/00; C; C01; C01B; C01B13/00; C01B13/14; C01B13/18; C01B13/185; C22; C22C; C22C1/00; C22C1/04; C22C1/05; C22C1/051; C22C1/053; C22C1/056; C22C1/059; B01J2208/00; B01J2208/00008; B01J2208/00017; B01J2208/00026; B01J2208/00035; B01J2208/00088; B01J2208/00106; B01J2208/00168; B01J2208/00212; B01J2208/00389; B01J2208/00407; B01J2208/0053; B22F2999/00; C01P; C01P2002/00; C01P2002/70; C01P2002/72; C01P2002/80; C01P2002/84; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/60; C01P2004/64
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
82 words
A spray conversion process for the production of nanophase composition tungsten carbide cobalt powders comprising the steps of: a. Preparing and mixing a starting solution consisting essentially of a tungsten compound and a cobalt compound dissolved in a solution; b. drying droplets of said solution at a sufficiently rapid rate to form a chemically homogeneous precursor powder; c. converting the precursor powder by thermochemical means in the presence of a carburization gas to form a homogeneous nanophase composite tungsten carbide cobalt powder.
Claim 2
Dependent Claim
82 words
A spray conversion process for the production of nanophase composition tungsten carbide cobalt powders comprising the steps of: a. Preparing and mixing a starting solution consisting essentially of a tungsten compound and a cobalt compound dissolved in a solution; b. drying droplets of said solution at a sufficiently rapid rate to form a chemically homogeneous precursor powder; c. converting the precursor powder by thermochemical means in the presence of a carburization gas to form a homogeneous nanophase composite tungsten carbide cobalt powder.
Claim 3
Dependent Claim
38 words
The process according to claim 1 wherein the drying of the starting solution is achieved by a method selected from the group consisting of spray drying, atomized droplet drying, calcining, roasting, rotary atomization, pressure atomization and ultrasonic atomization.
Claim 4
Dependent Claim
27 words
The process according to claim 1 wherein the thermochemical conversion of the precursor powder to the homogeneous nanophase composite powder is achieved in a fluidized bed reactor.
Claim 5
Dependent Claim
39 words
The process according to claim 1 wherein the drying of the starting solution is achieved by spray drying and the thermochemical conversion of the precursor powder to the homogeneous nanophase composite powder is achieved in a fluid bed reactor.
Claim 6
Dependent Claim
49 words
The process according to claim 1 wherein during the thermochemical conversion step the carburization temperature is in the range 700° C. to 1100° C., the carbon activity is controlled in the range a c ≈0.3 to 1.0 and the Co/W atomic ratio is in the range 0.1 to 1.5.
Claim 7
Dependent Claim
18 words
The process according to claim 5 wherein the drying of the starting solution is achieved by spray drying.
Claim 8
Dependent Claim
39 words
The process according to claim 5 wherein the drying of the starting solution is achieved by spray drying and the thermochemical conversion of the precursor powder to the homogeneous nanophase composite powder is achieved in a fluid bed reactor.
Claim 9
Dependent Claim
65 words
A spray conversion process for the production of nanophase tungsten carbide-cobalt (WC--Co) comprising the steps of: a. preparing and mixing a starting solution comprising ammonium metatungstate and a cobalt containing chemical; b. drying the starting solution by atomized-droplet drying at a sufficiently high rate to form a chemically homogeneous precursor powder; c. converting the precursor powder by thermochemical means to form homogeneous nanophase WC--Co powder.
Claim 10
Dependent Claim
65 words
A spray conversion process for the production of nanophase tungsten carbide-cobalt (WC--Co) comprising the steps of: a. preparing and mixing a starting solution comprising ammonium metatungstate and a cobalt containing chemical; b. drying the starting solution by atomized-droplet drying at a sufficiently high rate to form a chemically homogeneous precursor powder; c. converting the precursor powder by thermochemical means to form homogeneous nanophase WC--Co powder.
Claim 11
Dependent Claim
44 words
The process according to claim 8 wherein the cobalt containing chemical is selected from the group consisting of cobalt chloride: CoCl 2 ·6H 2 O, cobalt nitrate: Co(NO 3 ) 2 ·6H 2 O, or cobalt acetate: Co(CH 3 COO) 2 ·4H 2 O.
Claim 12
Dependent Claim
27 words
The process according to claim 8 wherein the thermochemical conversion of the precursor powder to the homogeneous nanophase composite powder is achieved in a fluid bed reactor.
Claim 13
Dependent Claim
49 words
The process according to claim 11 wherein during the thermochemical conversion step the carburization temperature is in the range 700° C. to 1100° C., the carbon activity is controlled in the range a c =0.3 to 1.0 and the Co/W atomic ratio is in the range 0.1 to 1.5.
References Cited (Backward Citations)
US2176802A
Cited
US2160670A
Cited
US3077385A
Cited
US3488291A
Cited
US3512962A
Cited
US3932594A
Cited
US4320156A
Cited
US4664899A
Cited
US4579713A
Cited
US4851041A
Cited
US4915733A
Cited
US4915733B1
Cited
DE3830111A1
Cited
DE3835728A1
Cited
WO1991007244A1
Cited
US5057147A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-10-03 | 1998-04-04 | 1998-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-10-03 | 2002-04-04 | 2002-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-10-03 | 2006-04-04 | 2006-10-04 | $7700.00 | Window Closed / Lapsed |