Methods for preparing magnetic powder material and magnet, process for preparaton of resin composition and process for producing a powder molded product
Assignee: Idemitsu Kosan Co Ltd
•
Filing: 1993-08-04
•
Granted: 1994-09-27
•
Expires: 2013-08-04
Abstract
Abstract There is disclosed a process for preparing a resin composition for powder molding, comprising 50 to 97 wt % of a metal or alloy powder and 50 to 3 wt % of a thermoplastic resin having heat resistance and crystallinity, which process comprises dissolving the thermoplastic resin having heat resistance crystallinity in a solvent and at the same time, dispersing therein at least one metal or alloy powder selected from iron, brass, nickel silver, stainless steel and aluminum, having an average particle diameter of not more than 500 mu m to thereby prepare a mixture. In addition, there is disclosed a process for producing a powder molded product which comprises cold compressing molding the above resin composition and then heating the molding at a temperature not less than the melting point of the thermoplastic resin. This powder molded product has excellent dimensional stability against heat, chemical resistance, and mechanical strength.
Inventors
- 👤 Hiroshi Kawato
- 👤 Tatsuya Tomioka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 18:25
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/02; H01F41/0253; H01F41/0266; C; C08; C08G; C08G65/00; C08G65/34; C08G65/38; C08G65/40; C08G65/4006; C08J; C08J3/00; C08J3/20; C08J3/205; C08K; C08K3/00; C08K3/02; C08K3/08; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; H01F1/061; H01F1/08; H01F1/083; H01F1/10; H01F1/11; H01F1/113; H01F1/12; H01F1/14; H01F1/20; H01F1/22; H01F1/24; H01F1/26; C08G2650/00; C08G2650/62; C08G2650/64
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
166 words
A process for preparing a resin composition for powder molding, said composition comprising 50 to 97 vol % of a metal or alloy powder and 50 to 3 vol % of a thermoplastic resin having heat resistance and crystallinity, said resin comprising a polycyanoarylether having a repeating unit represented by the formula: ##STR11## wherein Ar represents ##STR12## and a limiting viscosity (η) in a solvent of p-chlorophenol at 60° C. of at least 0.2 dl/g, which comprises dissolving the thermoplastic resin having heat resistance and crystallinity in N-methylpyrrolidone at a temperature of at least 190° C. to form a solution and at the same time dispersing therein at least one metal or alloy powder selected from the group-consisting of iron, brass, nickel, silver, stainless steel and aluminum and having an average particle diameter of not more than 500 μm to prepare a mixture of the powder and the solution and then volatilizing or evaporating the N-methylpyrrolidone thereby precipitating the resin onto the metal or alloy powder.
Claim 2
Dependent Claim
166 words
A process for preparing a resin composition for powder molding, said composition comprising 50 to 97 vol % of a metal or alloy powder and 50 to 3 vol % of a thermoplastic resin having heat resistance and crystallinity, said resin comprising a polycyanoarylether having a repeating unit represented by the formula: ##STR11## wherein Ar represents ##STR12## and a limiting viscosity (η) in a solvent of p-chlorophenol at 60° C. of at least 0.2 dl/g, which comprises dissolving the thermoplastic resin having heat resistance and crystallinity in N-methylpyrrolidone at a temperature of at least 190° C. to form a solution and at the same time dispersing therein at least one metal or alloy powder selected from the group-consisting of iron, brass, nickel, silver, stainless steel and aluminum and having an average particle diameter of not more than 500 μm to prepare a mixture of the powder and the solution and then volatilizing or evaporating the N-methylpyrrolidone thereby precipitating the resin onto the metal or alloy powder.
Claim 3
Dependent Claim
22 words
A process as defined in claim 1, which further comprises cooling the solution prior to effecting volatilization and evaporation of the N-methylpyrrolidone.
Claim 4
Dependent Claim
51 words
A process for producing a powder molded product which comprises subjecting the resin composition for powder molding as obtained in claim 1 to cold compression molding, and then heating the resultant molding at a temperature of not less than the melting point of the thermoplastic resin having heat resistance and crystallinity.
Claim 5
Dependent Claim
26 words
A process as defined in claim 1, wherein the metal or alloy powder is surface-treated with not more than 3 vol % of a coupling agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-09-26 | 1998-03-28 | 1998-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-09-26 | 2002-03-28 | 2002-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-09-26 | 2006-03-28 | 2006-09-27 | $7700.00 | Window Closed / Lapsed |