Neutral gray absorbing glass comprising manganese oxide for selenium retention during processing

Claim 2

A heat absorbing, neutral gray colored glass composition having a base glass composition comprising by weight: 68 to 75% SiO 2 , 10 to 18% Na 2 O, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% Al 2 O 3 , and 0 to 5% K 2 O, where CaO + MgO is 6 to 15% and Na 2 O + K 2 O is 10 to 20%, and colorants consisting essentially of: 0.90 to 1.90 wt. % total iron oxide as Fe 2 O 3 ; 0.002 to 0.025 wt. % cobalt as Co; 0.0010 to 0.0060 wt. % selenium as Se; 0.10 to 1.0 wt. % manganese oxide as MnO 2 ; and 0.0 to 1.0% titanium oxide as TiO 2 ; the glass at 4 mm. control thickness having light transmittance using illuminant A of 10.0% to 55.0%, ultra violet transmittance less than 25.0%, and infra red transmittance is less than about 50.0%.

Claim 3

The neutral grey glass composition according to claim 1, wherein the dominant wavelength is between 470 and 590 nanometers.

Claim 4

The neutral grey glass composition according to claim 1, wherein SO 3 is present in the composition in an amount about 0.01 to 0.03 wt. %.

Claim 5

A heat absorbing, neutral gray colored glass composition having a base glass composition comprising: 71 to 74% SiO 2 , 13 to 13.80% Na 2 O, 8.4 to 8.7% CaO, 3.5 to 4% MgO, 0.15 to 0.25% Al 2 O 3 , and 0 to 0.1% K 2 O, where CaO + MgO is 6 to 15% and Na 2 O +K 2 O is 10 to 20%, and colorants consisting essentially of: 1.20 to 1.60 wt. % total iron oxide as Fe 2 O 3 ; 0.0160 to 0.0185 wt. % cobalt as Co; 0.0020 to 0.0040 wt % selenium as Se; 0.15 to 0.60 wt. % manganese oxide as MnO 2 ; and 0.0 to 0.35 wt. % titanium oxide as TiO 2 , the glass at 4 mm. control thickness having light transmittance using illuminant A between 16.0% and 20.0%, ultra violet transmittance between 5 and 10%, infra red transmittance between 10 and 18%, and a dominant wavelength between about 470 and 590 nanometers.

Claim 6

A heat absorbing, neutral gray colored glass composition having a base glass composition comprising: 71 to 74% SiO 2 , 13 to 13.80% Na 2 O, 8.4 to 8.7% CaO, 3.5 to 4% MgO, 0.15 to 0.25% Al 2 O 3 , and 0 to 0.1% K 2 O, where CaO + MgO is 6 to 15% and Na 2 O +K 2 O is 10 to 20%, and colorants consisting essentially of: 1.20 to 1.60 wt. % total iron oxide as Fe 2 O 3 ; 0.0160 to 0.0185 wt. % cobalt as Co; 0.0020 to 0.0040 wt % selenium as Se; 0.15 to 0.60 wt. % manganese oxide as MnO 2 ; and 0.0 to 0.35 wt. % titanium oxide as TiO 2 , the glass at 4 mm. control thickness having light transmittance using illuminant A between 16.0% and 20.0%, ultra violet transmittance between 5 and 10%, infra red transmittance between 10 and 18%, and a dominant wavelength between about 470 and 590 nanometers.

Claim 7

The neutral grey glass composition according to claim 4, wherein its excitation purity is less than about 5.5%.

Claim 8

The neutral grey glass composition according to claim 3, wherein the FeO/total iron oxide as Fe 2 O 3 is between 0.18 and 0.26.

Claim 9

The neutral grey glass composition according to claim 1, wherein based on 1000 lbs. of sand used in batch ingredients to make said composition, other batch ingredients comprise: 6-24 lbs. salt cake; 3-20 lbs. sodium nitrate; and 0.1-1.5 lbs. carbocite.

Claim 10

The neutral grey glass composition according to claim 6, wherein said batch ingredients comprise 8-18 lbs. salt cake; 5-15 lbs. sodium nitrate; and 0.3-1.0 lbs carbocite.

Claim 11

The neutral grey glass composition according to claim 8, wherein said batch ingredients comprise 8-12 lbs. salt cake; 5-10 lbs. sodium nitrate; 0.3-1.0 lbs. carbocite; and said neutral grey glass composition comprises 0.15-0.60 MnO 2 and 1.2-1.6 wt. % total iron as Fe 2 O 3 .

Claim 12

A heat absorbing, neutral gray colored glass composition having a base glass composition comprising by weight: 68 to 75% SiO 2 , 10 to 18% Na 2 O, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% Al 2 O 3 , and 0 to 5% K 2 O, where CaO + MgO is 6 to 15% and Na 2 O + K 2 O is 10 to 20%, and colorants consisting essentially of: 0.90 to 1.90 wt. % total iron oxide as Fe 2 O 3 ; 0.002 to 0.025 wt. % cobalt as Co; 0.0010 to 0.0060 wt. % selenium as Se; 0.10 to 1.0 wt. % manganese oxide as MnO 2 ; and 0.0 to 1.0% titanium oxide as TiO 2 ; the glass at 4 mm. control thickness having light transmittance using illuminant A of 10.0% to 55.0%, ultra violet transmittance less than 25.0%, and infra red transmittance is less than about 50.0%; and being made from batch materials comprising sand, soda ash, dolomite, limestone, salt cake, rouge, sodium nitrate, a manganese containing compound, carbocite, a cobalt containing compound, and selenium.

Claim 13

A heat absorbing, neutral gray colored glass composition having a base glass composition comprising by weight: 68 to 75% SiO 2 , 10 to 18% Na 2 O, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% Al 2 O 3 , and 0 to 5% K 2 O, where CaO + MgO is 6 to 15% and Na 2 O + K 2 O is 10 to 20%, and colorants consisting essentially of: 0.90 to 1.90 wt. % total iron oxide as Fe 2 O 3 ; 0.002 to 0.025 wt. % cobalt as Co; 0.0010 to 0.0060 wt. % selenium as Se; 0.10 to 1.0 wt. % manganese oxide as MnO 2 ; and 0.0 to 1.0% titanium oxide as TiO 2 ; the glass at 4 mm. control thickness having light transmittance using illuminant A of 10.0% to 55.0%, ultra violet transmittance less than 25.0%, and infra red transmittance is less than about 50.0%; and being made from batch materials comprising sand, soda ash, dolomite, limestone, salt cake, rouge, sodium nitrate, a manganese containing compound, carbocite, a cobalt containing compound, and selenium.

Claim 14

The neutral grey glass composition according to claim 10, wherein based on 1000 lbs. of said sand in said batch ingredients used to make said composition, said ingredients comprise 6-24 lbs. salt cake; 3-20 lbs. sodium nitrate; and 0.1-1.5 lbs carbocite.

Claim 15

The neutral grey glass composition according to claim 11, wherein said ingredients comprise 8-18 lbs. salt cake; 5-15 lbs. sodium nitrate; and 0.3-1.0 lbs. carbocite.

Claim 16

The neutral grey glass composition according to claim 12, wherein said ingredients comprise 8-12 lbs. salt cake; 5-10 lbs. sodium nitrate; 0.3-1.0 lbs. carbocite; and said neutral grey glass composition comprises 0.15-0.60 MnO 2 and 1.2-1.6 wt. % total iron as Fe 2 O 3 .

Claim 17

A glazing for automotive or architectural use prepared from the neutral grey glass composition of claim 1.