US5340774A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Semiconductor fabrication technique using local planarization with self-aligned transistors
Assignee: Paradigm Technology Inc
•
Filing: 1993-02-04
•
Granted: 1994-08-23
•
Expires: 2013-02-04
Abstract
Abstract A CMOS integrated circuit fabrication technique for forming self-aligned transistors combined with local planarization in the vicinity of the transistors so as to allow local interconnects which are free of bridging, have good continuity over the planarized topography and are compatible with the self-alignment schemes, hence conserving chip real estate. The technique is compatible with planarization schemes using BPSG, BPTEOS, SOG or CMP. After formation of self-aligned insulated transistor gates and active transistor regions, the integrated circuit structure is planarized by formation of an oxide layer and a reflowed overlying glass layer. The glass layer is etched back to planarize the surface. Using a buried contact mask the remaining portions of the glass layer and underlying oxide layer are removed in the area of the buried contact only. In one version (prior to formation of the oxide layer and glass layer) a polysilicon "landing pad" is formed on the substrate at the buried contact location so as to allow more effective etching at the exact location of the buried contact.
Inventors
- 👤 Ting-Pwu Yen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:37
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698; C; C03; C03C; C03C15/00; Y; Y10; Y10S; Y10S148/00; Y10S148/133
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
145 words
A method of forming an integrated circuit comprising: providing a semiconductory substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures; implanting a dopant in the substrate after the step of forming the gate structures, thereby forming at least one doped region int he substrate; forming a masking layer on the principal surface overlying the at least one doped region; patterning the masking layer; then planarizing the principal surface by forming a filler layer over the principal surface and over the gate structures and patterned mask layer; defining a contact opening to the at least one doped region by removing a portion of the filler layer overlying the doped region, the filler layer otherwise remaining overlying a portion of the principal surface between two of the gate structures; and then etching to remove the underlying patterned mask layer.
Claim 2
Independent Claim
145 words
A method of forming an integrated circuit comprising: providing a semiconductory substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures; implanting a dopant in the substrate after the step of forming the gate structures, thereby forming at least one doped region int he substrate; forming a masking layer on the principal surface overlying the at least one doped region; patterning the masking layer; then planarizing the principal surface by forming a filler layer over the principal surface and over the gate structures and patterned mask layer; defining a contact opening to the at least one doped region by removing a portion of the filler layer overlying the doped region, the filler layer otherwise remaining overlying a portion of the principal surface between two of the gate structures; and then etching to remove the underlying patterned mask layer.
Claim 3
Dependent Claim
30 words
The method of claim 1, wherein the step of defining a contact opening includes removing a central portion of the patterned mask layer, but not removing a peripheral portion thereof.
Claim 4
Dependent Claim
20 words
The method of claim 1, wherein the patterned masking layer overlies at least a portion of an adjacent gate structure.
Claim 5
Dependent Claim
37 words
The method of claim 1, further comprising the step of forming an insulating layer over the gate structures and over the principal surface prior to the step of planarizing, wherein the filler layer is a glass material.
Claim 6
Dependent Claim
17 words
The method of claim 4, wherein the glass material is at least 800 Å thick when formed.
Claim 7
Dependent Claim
37 words
The method of claim 1, further comprising the step of forming an insulating layer over the gate structure and over the principal surface prior to the step of planarizing, wherein the filler layer is a glass material.
Claim 8
Dependent Claim
30 words
The method of claim 6, wherein the step of defining includes the steps of: etching to remove the filler layer; and a then etching to remove the underlying insulating layer.
Claim 9
Independent Claim
145 words
A method of forming an integrated circuit, comprising the steps of: providing a semiconductor substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures each including a conductive electrode surrounded on its lateral and top surfaces by a first insulating layer; implanting a dopant in portions of the substrate adjoining the gate structure; forming a second insulating layer over the principal surface; forming a filler layer over the second insulating layer; removing at least part of the filler layer; forming a masking layer over the filler layer; patterning the masking layer, thereby exposing a portion of the filler layer; removing at least part of the exposed portion of the filler layer and the underlying second insulating layer, thereby exposing a portion of the principal surface; and forming a conductive contact to the exposed portion of the principal surface.
Claim 10
Independent Claim
145 words
A method of forming an integrated circuit, comprising the steps of: providing a semiconductor substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures each including a conductive electrode surrounded on its lateral and top surfaces by a first insulating layer; implanting a dopant in portions of the substrate adjoining the gate structure; forming a second insulating layer over the principal surface; forming a filler layer over the second insulating layer; removing at least part of the filler layer; forming a masking layer over the filler layer; patterning the masking layer, thereby exposing a portion of the filler layer; removing at least part of the exposed portion of the filler layer and the underlying second insulating layer, thereby exposing a portion of the principal surface; and forming a conductive contact to the exposed portion of the principal surface.
Claim 11
Dependent Claim
12 words
The method of claim 8, wherein the mask layer comprises polycrystalline silicon.
Claim 12
Dependent Claim
11 words
The method of claim 8, wherein the mask layer comprises titanium.
Claim 13
Dependent Claim
13 words
The method of claim 8, wherein the filler layer is a doped glass.
Claim 14
Dependent Claim
12 words
The method of claim 11, wherein the doped glass is boro-phosphosilicate glass.
Claim 15
Dependent Claim
17 words
The method of claim 8, wherein the filler layer is at least 800 Å thick when formed.
Claim 16
Dependent Claim
29 words
The method of claim 8, wherein the step of forming a filler layer comprises: forming a layer of glass at least 800 Å thick; and reflowing the glass layer.
Claim 17
Dependent Claim
40 words
The method of claim 8, wherein the step of removing at least part of the filler layer comprises removing an upper portion of the filler layer, thereby exposing those portions of the underlying second insulating layer overlying the gate structures.
Claim 18
Dependent Claim
25 words
The method of claim 8, wherein the exposed portion of the principal surfaces overlies one of the portions of the substrate having the implanted dopant.
Claim 19
Dependent Claim
26 words
The method of claim 8, further comprising the step of forming an electrical contact to the conductive electrode of at least one of the gate structures.
Claim 20
Dependent Claim
35 words
The method of claim 8, wherein the step of removing at least part of the filler layer comprises: etching the at least part of the filler layer; and then etching the underlying second insulating layer.
Claim 21
Dependent Claim
22 words
The method of claim 18, wherein the first etching step uses an acid and the second etching step is a dry etching.
Claim 22
Independent Claim
189 words
A method of forming an integrated circuit, comprising the steps of: providing a semiconductor substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures each including a conductive electrode surrounded on its lateral and top surfaces by a first insulating layer; implanting a dopant in portions of the substrate extending to the principal surface at locations adjoining the gate structures; forming a masking layer over the principal surface and the gate structures; patterning the masking layer to remove portions thereof, the remaining portions overlying the principal surface at the locations adjoining the gate structures; forming a second insulating layer extending over the gate structures and the masking layer and the principal surface; forming a filler layer over the second insulating layer; removing at least part of the filler layer and at least part of the underlying second insulating layer, thereby exposing at least part of the remaining portion of the masking layer; removing the exposed part of the masking layer; and forming a conductive contact to the portion of the substrate underlying the location of the removed part of the masking layer.
Claim 23
Independent Claim
189 words
A method of forming an integrated circuit, comprising the steps of: providing a semiconductor substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures each including a conductive electrode surrounded on its lateral and top surfaces by a first insulating layer; implanting a dopant in portions of the substrate extending to the principal surface at locations adjoining the gate structures; forming a masking layer over the principal surface and the gate structures; patterning the masking layer to remove portions thereof, the remaining portions overlying the principal surface at the locations adjoining the gate structures; forming a second insulating layer extending over the gate structures and the masking layer and the principal surface; forming a filler layer over the second insulating layer; removing at least part of the filler layer and at least part of the underlying second insulating layer, thereby exposing at least part of the remaining portion of the masking layer; removing the exposed part of the masking layer; and forming a conductive contact to the portion of the substrate underlying the location of the removed part of the masking layer.
Claim 24
Dependent Claim
32 words
The method of claim 1, wherein the step of defining a contact opening results in at least one of the gate structures having a sidewall of a single layer of insulating material.
Claim 25
Independent Claim
146 words
A method of forming an integrated circuit comprising: providing a semiconductor substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures; implanting a dopant int he substrate after the step of forming the gate structures, thereby forming at least one doped region int he substrate; planarizing the principal surface by forming a filler layer over the principal surface and over the gate structure; uniformly etching away a top portion of the filler layer, exposing an upper portion of the gate structure; then, forming a mask layer over the gate structures and over remaining portion of the filler layer; defining a opening int he mask layer adjacent one of the gate structure; and then, etching away the filler layer and down to the principal surface of the substrate through the opening, thereby defining a contact opening to the principal surface.
Claim 26
Independent Claim
146 words
A method of forming an integrated circuit comprising: providing a semiconductor substrate having a principal surface; forming on the principal surface a plurality of spaced apart gate structures; implanting a dopant int he substrate after the step of forming the gate structures, thereby forming at least one doped region int he substrate; planarizing the principal surface by forming a filler layer over the principal surface and over the gate structure; uniformly etching away a top portion of the filler layer, exposing an upper portion of the gate structure; then, forming a mask layer over the gate structures and over remaining portion of the filler layer; defining a opening int he mask layer adjacent one of the gate structure; and then, etching away the filler layer and down to the principal surface of the substrate through the opening, thereby defining a contact opening to the principal surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-22 | 1998-02-21 | 1998-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-22 | 2002-02-21 | 2002-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-22 | 2006-02-21 | 2006-08-23 | $7700.00 | Window Closed / Lapsed |