Process for making composite containing fibrous material

Claim 2

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 20% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (c) depositing a silicon-wettable coating on said boron nitride-coated fibrous material leaving no significant portion of said boron nitride exposed; (d) disposing a layer of the resulting coated fibrous material between the faces of two of said tapes forming a layered structure; (e) laminating the layered structure to form a laminated structure; (f) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (g) infiltrating a molten infiltrant comprised of boron and silicon into said porous body to produce an infiltrated product, said molten infiltrant containing boron in solution in an amount ranging from about 0.1% by weight of silicon to an amount which forms a saturated solution with silicon; and (h) cooling said infiltrated product producing said composite.

Claim 3

The process according to claim 1, wherein said composite contains at least about 20% by volume of boron nitride coated fibrous material and has a porosity of less than about 10% by volume

Claim 4

The process according to claim 1, wherein said infiltration-promoting material in step (a) is selected from the group consisting of a powder, a fibrous material and mixtures thereof.

Claim 5

The process according to claim 1, wherein said infiltration-promoting material in step (a) is comprised of a mixture of fibrous material and powder wherein the powder ranges from about 1% to about 50% by weight of the infiltration-promoting material.

Claim 6

The process according to claim 1, wherein said infiltration-promoting material in step (a) is comprised of a mixture of fibrous material of elemental carbon and silicon carbide powder, and the silicon carbide powder ranges from about 10% to about 40% by weight of the infiltration-promoting material.

Claim 7

The process according to claim 1, wherein said infiltration-promoting material in step (a) is selected from the group consisting of elemental carbon, a metal carbide, a metal which reacts with silicon to form a silicide, a metal nitride, a metal silicide and mixtures thereof.

Claim 8

The process according to claim 1, wherein said fibrous material in step (b) is selected from the group consisting of fibers, filaments, strands, bundles, whiskers, cloth, felt, and mixtures thereof.

Claim 9

The process according to claim 1, wherein said fibrous material in step (b) is selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride, silica, and mixtures thereof.

Claim 10

The process according to claim 1, wherein said fibrous material in step (b) is a carbon-containing material.

Claim 11

The process according to claim 1, wherein said fibrous material in step (b) is a silicon carbide-containing material.

Claim 12

The process according to claim 1, wherein said silicon-wettable coating in step (c) is selected from the group consisting of elemental carbon, metal carbide, a metal which reacts with silicon to form a silicide thereof, a metal nitride, a metal silicide, and mixtures thereof.

Claim 13

The process according to claim 1, wherein in step (d) a plurality of layers of said coated fibrous material and more than two tapes are used in forming the layered structure and wherein all of the layers of coated fibrous material are separated from each other by tape.

Claim 14

The process according to claim 1, wherein in step (d) the layer of coated fibrous material is comprised of a plurality of continuous spaced filaments.

Claim 15

The process according to claim 1, wherein in step (g) said infiltrant is comprised of boron and silicon wherein boron ranges from about 1% by weight to about 3% by weight of silicon containing boron in solution in said silicon ranging from about 1% by weight of silicon to an amount which forms a saturated solution with silicon.

Claim 16

The process according to claim 1, wherein in step (g) said infiltrant is comprised of a saturated solution of boron in silicon.

Claim 17

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 10% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (c) depositing a silicon-wettable coating on said boron nitride-coated fibrous material leaving no significant portion of said boron nitride exposed; (d) disposing a layer of the resulting coated fibrous material between the faces of two of said tapes forming a layered structure; (e) laminating the layered structure to form a laminated structure; (f) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (g) providing an infiltrant composition comprised of boron and silicon; (h) contacting said porous body and said infiltrant composition; (i) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant composition is molten whereby molten infiltrant containing boron in solution in silicon in an amount ranging from about 0.1% by weight of silicon to a saturated solution of boron in silicon is infiltrated into said porous body; and (j) cooling said infiltrated product producing said composite.

Claim 18

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 10% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (c) depositing a silicon-wettable coating on said boron nitride-coated fibrous material leaving no significant portion of said boron nitride exposed; (d) disposing a layer of the resulting coated fibrous material between the faces of two of said tapes forming a layered structure; (e) laminating the layered structure to form a laminated structure; (f) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (g) providing an infiltrant composition comprised of boron and silicon; (h) contacting said porous body and said infiltrant composition; (i) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant composition is molten whereby molten infiltrant containing boron in solution in silicon in an amount ranging from about 0.1% by weight of silicon to a saturated solution of boron in silicon is infiltrated into said porous body; and (j) cooling said infiltrated product producing said composite.

Claim 19

The process according to claim 16, wherein said infiltration-promoting material in step (a) is comprised of a mixture of fibrous material of elemental carbon and silicon carbide powder, and the silicon carbide powder ranges from about 10% to about 40% by weight of the infiltration-promoting material.

Claim 20

The process according to claim 16, wherein said fibrous material in step (b) is selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride, silica, and mixtures thereof.

Claim 21

The process according to claim 16, wherein in step (d) a plurality of layers of said coated fibrous material and more than two tapes are used in forming the layered structure and wherein all of the layers of coated fibrous material are separated from each other by tape.

Claim 22

The process according to claim 16, wherein in seep (d) the layer of coated fibrous material is comprised of a plurality of continuous spaced filaments.

Claim 23

The process according to claim 16, wherein in step (g) said infiltrant composition is comprised of boron and silicon wherein boron ranges from about 1% by weight to about 3% by weight of silicon containing boron in solution in said silicon ranging from about 1% by weight of silicon to an amount which forms a saturated solution with silicon.

Claim 24

The process according to claim 16, wherein in step (i) said molten infiltrant is comprised of a saturated solution of boron in silicon.

Claim 25

A process for producing a composite containing at least about 10% by volume of boron nitride coated filaments and having a porosity of less than about 10% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on filaments leaving no significant portion thereof exposed, each said filament having a diameter of at least about 50 microns and a length of at least about 10 times its diameter; (c) disposing a layer of said coated filaments between the faces of two of said tapes forming a layered structure, said filaments in said layer being spaced from each other; (d) laminating the layered structure to form a laminated structure; (e) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (f) infiltrating a molten infiltrant comprised of boron and silicon into said porous body to produce an infiltrated product, said molten infiltrant containing boron in solution in an amount ranging from about 0.1% by weight of silicon an amount which forms a saturated solution with silicon; and (g) cooling said infiltrated product producing said composite.

Claim 26

A process for producing a composite containing at least about 10% by volume of boron nitride coated filaments and having a porosity of less than about 10% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on filaments leaving no significant portion thereof exposed, each said filament having a diameter of at least about 50 microns and a length of at least about 10 times its diameter; (c) disposing a layer of said coated filaments between the faces of two of said tapes forming a layered structure, said filaments in said layer being spaced from each other; (d) laminating the layered structure to form a laminated structure; (e) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (f) infiltrating a molten infiltrant comprised of boron and silicon into said porous body to produce an infiltrated product, said molten infiltrant containing boron in solution in an amount ranging from about 0.1% by weight of silicon an amount which forms a saturated solution with silicon; and (g) cooling said infiltrated product producing said composite.

Claim 27

The process according to claim 23, wherein said infiltration-promoting material in step (a) is selected from the group consisting of a powder, a fibrous material and mixtures thereof.

Claim 28

The process according to claim 23, wherein said infiltration-promoting material in step (a) is comprised of a mixture of fibrous material of elemental carbon and silicon carbide powder, and the silicon carbide powder ranges from about 10% to about 40% by weight of the infiltration-promoting material.

Claim 29

The process according to claim 23, wherein said filaments in step (b) are selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride, silica, and mixtures thereof.

Claim 30

The process according to claim 23, wherein in seep (c) a plurality of layers of said coated filaments and more than two tapes are used in forming the layered structure and wherein all of the layers of coated filaments are separated from each other by tape.

Claim 31

The process according to claim 23, wherein in step (f) said infiltrant is comprised of boron and silicon wherein boron ranges from about 1% by weight to about 3% by weight of silicon containing boron in solution in said silicon ranging from about 1% by weight of silicon to an amount which forms a saturated solution with silicon.

Claim 32

The process according to claim 23, wherein in step (f) said infiltrant is comprised of a saturated solution of boron in silicon.

Claim 33

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 10% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on filaments leaving no significant portion thereof exposed, each said filament having a diameter of at least about 50 microns and a length of at least about 10 times its diameter; (c) disposing a layer of said coated filaments between the faces of two of said tapes forming a layered structure, said filaments in said layer being spaced from each other; (d) laminating the layered structure to form a laminated structure; (e) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (f) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in an amount ranging from about 0.1% by weight of elemental silicon to an amount which forms a saturated solution with silicon; (g) contacting said porous body and said infiltrant with infiltrating means whereby molten infiltrant is infiltrated into said porous body; (h) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (i) cooling said infiltrated product producing said composite.

Claim 34

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 10% by volume which comprises the following steps: (a) forming tapes comprised of a mixture of infiltration-promoting material and organic binding material; (b) depositing a coating of boron nitride on filaments leaving no significant portion thereof exposed, each said filament having a diameter of at least about 50 microns and a length of at least about 10 times its diameter; (c) disposing a layer of said coated filaments between the faces of two of said tapes forming a layered structure, said filaments in said layer being spaced from each other; (d) laminating the layered structure to form a laminated structure; (e) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue producing a porous body; (f) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in an amount ranging from about 0.1% by weight of elemental silicon to an amount which forms a saturated solution with silicon; (g) contacting said porous body and said infiltrant with infiltrating means whereby molten infiltrant is infiltrated into said porous body; (h) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (i) cooling said infiltrated product producing said composite.

Claim 35

The process according to claim 30, wherein said infiltration-promoting material in step (a) is comprised of a mixture of fibrous material of elemental carbon and silicon carbide powder, and the silicon carbide powder ranges from about 10% to about 40% by weight of the infiltration-promoting material.

Claim 36

The process according to claim 30, wherein in step (c) a plurality of layers of said coated filaments and more than two tapes are used in forming the layered structure and wherein all of the layers of coated filaments are separated from each other by tape.

Claim 37

The process according to claim 30, wherein in step (f) said infiltrant is comprised of boron and silicon wherein boron ranges from about 1% by weight to about 3% by weight of silicon containing boron in solution in said silicon ranging from about 1% by weight of silicon to an amount which forms a saturated solution with silicon.

Claim 38

The process according to claim 30, wherein in step (f) said infiltrant is comprised of a saturated solution of boron in silicon.