Process and plant for obtaining steel strip coils having cold-rolled characteristics and directly obtained in a hot-rolling line
Assignee: Tata Steel Ijmuiden BV
•
Filing: 1991-07-05
•
Granted: 1994-07-19
•
Expires: 2011-07-05
Abstract
Abstract A process for obtaining steel strip coils with characteristics of a cold-rolled product, directly in a hot-rolling line, comprises subsequently to steps of casting and thickness reduction at a temperature of more than 1100° C. upon solidification, induction heating of the product and a further step of hot rolling, above point Ar 3 , a step of cooling and temperature control in a range of between 600° and 250° C., thus lower than said point Ar 3 , as well as one or more passes of cold-rolling in series, with final coiling of the obtained product. Also a preferred plant is described for putting into practice such a process.
Inventors
- 👤 Giovanni Arvedi
- 👤 Giovanni Gosio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 04:22
CPC Classifications
B; B21; B21B; B21B1/00; B21B1/22; B21B1/24; B21B1/46; B21B1/463; C; C21; C21D; C21D8/00; C21D8/02; C21D8/0221; C21D8/0226; B21B2201/00; B21B2201/04; B21B2201/14; C21D8/021; C21D8/0215; C21D8/0231; C21D8/0236; Y; Y10; Y10S; Y10S29/00; Y10S29/032; Y10T; Y10T29/00; Y10T29/45; Y10T29/4517; Y10T29/49; Y10T29/4998; Y10T29/49988; Y10T29/49991; Y10T29/51; Y10T29/5184
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
180 words
A process for obtaining steel strip coil directly from a hot-rolling line, said steel strip coil having characteristics of a cold-rolled product, comprising: mould casting a flat product having a thickness of less than 100 mm; reducing the thickness of said flat product immediately beyond the mould while maintaining a liquid core of said flat product; after solidification of the core of said flat product, further reducing the thickness of said flat product by rolling at a temperature greater than 1100° C. to provide a flat product of 10-30 mm thickness; induction re-heating said flat product to provide a substantially homogeneous temperature throughout said flat product of about 1100° C.; subjecting said flat product to a further stage of hot-rolling in the austenitic region at a temperature above a temperature value corresponding to transformation point Ar 3 ; reducing the temperature of the flat product to a temperature lower than a temperature corresponding to said transformation point Ar 3 ; and subjecting said flat product to at least one cold-rolling to obtain said steel strip having characteristics of cold-rolled product.
Claim 2
Dependent Claim
180 words
A process for obtaining steel strip coil directly from a hot-rolling line, said steel strip coil having characteristics of a cold-rolled product, comprising: mould casting a flat product having a thickness of less than 100 mm; reducing the thickness of said flat product immediately beyond the mould while maintaining a liquid core of said flat product; after solidification of the core of said flat product, further reducing the thickness of said flat product by rolling at a temperature greater than 1100° C. to provide a flat product of 10-30 mm thickness; induction re-heating said flat product to provide a substantially homogeneous temperature throughout said flat product of about 1100° C.; subjecting said flat product to a further stage of hot-rolling in the austenitic region at a temperature above a temperature value corresponding to transformation point Ar 3 ; reducing the temperature of the flat product to a temperature lower than a temperature corresponding to said transformation point Ar 3 ; and subjecting said flat product to at least one cold-rolling to obtain said steel strip having characteristics of cold-rolled product.
Claim 3
Dependent Claim
29 words
A process according to claim 1, wherein said hot-rolling stage at a temperature below the transformation point Ar 3 is carried out in the range of 250° C.-600° C.
Claim 4
Dependent Claim
54 words
A process according to claim 1, further comprising at least one of the following steps: (i) coiling and subsequent uncoiling of the strip immediately after the induction re-heating, upon cutting the strip immediately after the first rolling stage; (ii) at least one discaling step; and (iii) additional heating between two further stages of hot-rolling.
Claim 5
Dependent Claim
161 words
A plant for obtaining steel strip coils having characteristics of cold-rolled product, directly obtained in a hot-rolling line, comprising: means (10) for continuous casting of flat product (1) with a subsequent arc-shaped guide roller path (11); first reduction means (13, 15) for reducing thickness of the flat product in said arc-shaped path when it is in a condition of liquid core or immediately thereafter upon solidification of said flat product (1); heating means (21) for induction heating and homogenization of temperature throughout of the flat product (1) downstream of said first reduction means; at least one additional rolling stand (27) downstream from said heating means; cooling means (29) for cooling and controlling the temperature of the flat product (1) until under transformation point Ar 3 immediately downstream of said additional hot-rolling stand (27); at least one cold-rolling stand (31) downstream of said cooling means; and coiler means (33) for winding the strip in a coil (1') downstream of said cold-rolling stand.
Claim 6
Dependent Claim
161 words
A plant for obtaining steel strip coils having characteristics of cold-rolled product, directly obtained in a hot-rolling line, comprising: means (10) for continuous casting of flat product (1) with a subsequent arc-shaped guide roller path (11); first reduction means (13, 15) for reducing thickness of the flat product in said arc-shaped path when it is in a condition of liquid core or immediately thereafter upon solidification of said flat product (1); heating means (21) for induction heating and homogenization of temperature throughout of the flat product (1) downstream of said first reduction means; at least one additional rolling stand (27) downstream from said heating means; cooling means (29) for cooling and controlling the temperature of the flat product (1) until under transformation point Ar 3 immediately downstream of said additional hot-rolling stand (27); at least one cold-rolling stand (31) downstream of said cooling means; and coiler means (33) for winding the strip in a coil (1') downstream of said cold-rolling stand.
Claim 7
Dependent Claim
25 words
A plant according to claim 4, further comprising at least an additional induction oven intermediate between two subsequent ones of said additional rolling stands (27).
Claim 8
Dependent Claim
61 words
A plant according to claim 4, characterized in that the range of variation of the temperature at the exit of said device (29) is between 250° and 600° C., with a deviation of more or less 10° from the prefixed value at the inside of said range according to the quality of steel, the feeding speed and the product (1) thickness.
Claim 9
Dependent Claim
36 words
A plant according to claim 6, further comprising a device (23) for winding and subsequently unwinding the strip immediately downstream of the induction oven (21), upstream of the latter being provided a shear cutting device (17).
Claim 10
Dependent Claim
29 words
A plant according to claim 7, further comprising at least a discaling device (19, 25), respectively upstream of the first rolling stage (15) and downstream of said induction oven.
Claim 11
Dependent Claim
35 words
A plant according to claim 4, wherein said cooling apparatus (29) is a water cooling device with water feeding valves and having a temperature detector with feed-back for automatic controlling the cooling water feeding valves.
Claim 12
Dependent Claim
36 words
A plant according to claim 9, further comprising a device (23) for winding and subsequently unwinding the strip immediately downstream of the induction oven (21), upstream of the latter being provided a shear cutting device (17).
Claim 13
Dependent Claim
29 words
A plant according to claim 9, further comprising at least a discaling device (19, 25), respectively upstream of the first rolling stage (15) and downstream of said induction oven.
Claim 14
Dependent Claim
21 words
A plant according to claim 9, further comprising at least an additional induction oven intermediate between two subsequent rolling stands (27).
Claim 15
Dependent Claim
47 words
A plant according to claim 9, wherein said cooling means (29) comprises means for cooling the flat product when leaving said cooling means to within the range of 250° to 600° C., according to the quality of steel, the feeding speed and the flat product (1) thickness.
Claim 16
Dependent Claim
29 words
A plant according to claim 13, further comprising at least a discaling device (19, 25), respectively upstream of the first rolling stage (15) and downstream of said induction oven.
Claim 17
Dependent Claim
21 words
A plant according to claim 13, further comprising at least an additional induction oven intermediate between two subsequent rolling stands (27).
Claim 18
Dependent Claim
38 words
A plant according to claim 4, further comprising means (23) for winding and subsequently unwinding the flat product immediately downstream of the heating means (21), upstream of the heating means there being provided a shear cutting device (17).
Claim 19
Dependent Claim
21 words
A plant according to claim 16, further comprising at least an additional induction oven intermediate between two subsequent rolling stands (27).
Claim 20
Dependent Claim
43 words
A plant according to claim 16, further comprising discaling means upstream of the first reduction means (15) or downstream of said heating means 21, or a discaling means (19, 25) both upstream of said first reduction means and downstream of said heating means.
Claim 21
Dependent Claim
27 words
A plant according to claim 18, wherein the discaling means (25) downstream of the heating means (21) is positioned immediately after said winding and unwinding means (23).
References Cited (Backward Citations)
FI27800A
Cited
US2226500A
Cited
US2359095A
Cited
US2702766A
Cited
US3154442A
Cited
DE1903554A1
Cited
JPS56144805A
Cited
US4872245A
Cited
EP0226446A2
Cited
US4793168A
Cited
EP0306076A1
Cited
WO1989011363A1
Cited
EP0370575A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-18 | 1998-01-17 | 1998-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-18 | 2002-01-17 | 2002-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-18 | 2006-01-17 | 2006-07-19 | $7700.00 | Window Closed / Lapsed |