Peroxide clean before buried contact polysilicon deposition
Assignee: United Microelectronics Corp
•
Filing: 1993-05-07
•
Granted: 1994-07-12
•
Expires: 2013-05-07
Abstract
Abstract A method of removing impurities from the surface of an integrated circuit and forming a uniform thin native oxide layer on the same surface of an integrated circuit is described. A hydrofluoric acid solution, followed by a rinse and spin dry, is often used to remove gate oxide from within an opening etched in a polysilicon layer. The rinsing leaves water spots. Spin drying leaves impurities where water tracks were. An H 2 O 2 cleaning is performed to remove the water spots. After the cleaning, a uniform thin layer of native oxide is formed on the surface of the silicon substrate. A second layer of polysilicon is deposited over this first thin native oxide layer and doped with an implant dosage chosen so that it will go through the uniform native oxide layer. The substrate is annealed to drive in the buried contact. Processing continues to form polysilicon or silicide gate electrodes. Source and drain regions are formed within the openings to the silicon substrate between the gate electrodes. Spacers are formed on the sidewalls of the gate electrodes. An insulating layer is deposited over the surface of the silicon substrate. Contact openings are etched through the insulating layer to the second polysilicon layer and to the silicon substrate. A metal layer is deposited over the insulating layer and filling the openings to the second polysilicon layer and the silicon substrate. The metal layer is patterned, completing the formation of the buried contacts within the integrated circuit.
Inventors
- 👤 Sun-Chieh Chien
- 👤 Yu-Ju Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 08:58
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/10; H10P70/15; Y; Y10; Y10S; Y10S148/00; Y10S148/017; Y10S148/118; Y10S438/00; Y10S438/906
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
112 words
The method of removing water spots from the surface of an integrated circuit comprising: providing a thin layer of native oxide on the surface of said integrated circuit; etching away said thin native oxide layer; rinsing and drying said surface after said etching away of said native oxide layer whereby water spots are formed on the surface of said integrated circuit as a result of said rinsing and drying; and H 2 O 2 cleaning of said surface to remove said water spots whereby a uniform second thin layer of native oxide is formed on the surface of said integrated circuit as a result of said H 2 O 2 cleaning process.
Claim 2
Independent Claim
112 words
The method of removing water spots from the surface of an integrated circuit comprising: providing a thin layer of native oxide on the surface of said integrated circuit; etching away said thin native oxide layer; rinsing and drying said surface after said etching away of said native oxide layer whereby water spots are formed on the surface of said integrated circuit as a result of said rinsing and drying; and H 2 O 2 cleaning of said surface to remove said water spots whereby a uniform second thin layer of native oxide is formed on the surface of said integrated circuit as a result of said H 2 O 2 cleaning process.
Claim 3
Dependent Claim
111 words
The method of claim 1 wherein said H 2 O 2 cleaning comprises the steps of immersing said integrated circuit in a solution of NH 4 OH + H 2 O 2 + H 2 O in the concentration 5:1:1 at a temperature of between about 60° to 80° C., followed by a rinsing said integrated circuit with deionized water, immersing said integrated circuit in a solution of HCl + H 2 O 2 + H 2 O in the concentration 6:1:1 at a temperature of between about 60° to 80° C., rinsing said integrated circuit with de-ionized water for a second time, and spinning said integrated circuit to dry it.
Claim 4
Dependent Claim
33 words
The method of claim 1 wherein said H 2 O 2 cleaning results in the growth of a controlled second native oxide layer having a thickness of between about 10 to 30 Angstroms.
Claim 5
Independent Claim
403 words
The method of fabricating an integrated circuit with buried contacts comprising: forming a gate oxide layer on a silicon substrate; depositing a first layer of polysilicon over said gate oxide layer; patterning said first polysilicon layer to form openings to said gate oxide layer; etching away said gate oxide layer within said openings; rinsing and drying said silicon substrate after said etching away of said gate oxide layer whereby water spots are formed on the surface of said silicon substrate as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform first thin layer of native oxide is formed on the surface of said silicon substrate as a result of said H 2 O 2 cleaning process; depositing a second layer of polysilicon over said first thin native oxide layer; doping said second polysilicon layer with a concentration sufficient to penetrate through said uniform first thin native oxide layer to form said buried contact regions in said silicon substrate; annealing said silicon substrate to drive said doping concentration into said silicon substrate to form said buried contact regions whereby a second thin layer of native oxide forms on the surface of said second polysilicon layer; etching away said second thin native oxide layer; rinsing and drying said silicon substrate after said etching away of said second native oxide layer whereby water spots are formed on the surface of said second polysilicon layer as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform third thin layer of native oxide is formed on the surface of said second polysilicon layer as a result of said H 2 O 2 cleaning process; patterning said second and first polysilicon layers to form gate electrodes on the surface of said silicon substrate; forming source and drain regions within openings to said silicon substrate between said gate electrodes; forming spacers on the sidewalls of said gate electrodes; depositing an insulating layer over the surface of said silicon substrate; etching contact openings through said insulating layer to said second polysilicon layer and to said silicon substrate; depositing a metal layer over said insulating layer and filling said openings to said second polysilicon layer and said silicon substrate; and patterning said metal layer to complete said buried contacts within said integrated circuit.
Claim 6
Independent Claim
403 words
The method of fabricating an integrated circuit with buried contacts comprising: forming a gate oxide layer on a silicon substrate; depositing a first layer of polysilicon over said gate oxide layer; patterning said first polysilicon layer to form openings to said gate oxide layer; etching away said gate oxide layer within said openings; rinsing and drying said silicon substrate after said etching away of said gate oxide layer whereby water spots are formed on the surface of said silicon substrate as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform first thin layer of native oxide is formed on the surface of said silicon substrate as a result of said H 2 O 2 cleaning process; depositing a second layer of polysilicon over said first thin native oxide layer; doping said second polysilicon layer with a concentration sufficient to penetrate through said uniform first thin native oxide layer to form said buried contact regions in said silicon substrate; annealing said silicon substrate to drive said doping concentration into said silicon substrate to form said buried contact regions whereby a second thin layer of native oxide forms on the surface of said second polysilicon layer; etching away said second thin native oxide layer; rinsing and drying said silicon substrate after said etching away of said second native oxide layer whereby water spots are formed on the surface of said second polysilicon layer as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform third thin layer of native oxide is formed on the surface of said second polysilicon layer as a result of said H 2 O 2 cleaning process; patterning said second and first polysilicon layers to form gate electrodes on the surface of said silicon substrate; forming source and drain regions within openings to said silicon substrate between said gate electrodes; forming spacers on the sidewalls of said gate electrodes; depositing an insulating layer over the surface of said silicon substrate; etching contact openings through said insulating layer to said second polysilicon layer and to said silicon substrate; depositing a metal layer over said insulating layer and filling said openings to said second polysilicon layer and said silicon substrate; and patterning said metal layer to complete said buried contacts within said integrated circuit.
Claim 7
Dependent Claim
20 words
The method of claim 4 wherein the thickness of said gate oxide layer is between about 180 to 220 Angstroms.
Claim 8
Dependent Claim
22 words
The method of claim 4 wherein said first polysilicon layer is deposited to a thickness of between about 700 to 900 Angstroms.
Claim 9
Dependent Claim
22 words
The method of claim 4 wherein said second polysilicon layer is deposited to a thickness of between about 1350 to 1650 Angstroms.
Claim 10
Dependent Claim
57 words
The method of claim 4 wherein said second polysilicon layer is doped by ion implantation of phosphorus P31 with a dosage of between about 5 E 15 to 1 E 16 atoms/cm 2 and energy of between about 45 to 55 Kev whereby said implant dosage is sufficient to go through said uniform third native oxide layer.
Claim 11
Dependent Claim
30 words
The method of claim 4 wherein said etching away of said gate oxide layer is performed by a hydrofluoric acid etch in the concentration 10 H 2 O: 1 HF.
Claim 12
Dependent Claim
32 words
The method of claim 4 wherein said etching away of said second native oxide layer is performed by a hydrofluoric acid etch in the concentration 10 H 2 O : 1 HF.
Claim 13
Dependent Claim
106 words
The method of claim 4 wherein said H 2 O 2 cleaning comprises the steps of immersing said substrate in a solution of NH 4 OH + H 2 O 2 + H 2 O in the concentration 5: 1:1 at a temperature of between about 60° to 80° C., followed by rinsing said substrate with de-ionized water, immersing said substrate in a solution of HCl + H 2 O 2 + H 2 O in the concentration 6:1:1 at a temperature of between about 60° to 80° C., rinsing said substrate with de-ionized water for a second time, and spinning said substrate to dry it.
Claim 14
Dependent Claim
32 words
The method of claim 11 wherein said H 2 O 2 cleaning results in the growth of a controlled native oxide layer having a thickness of between about 10 to 30 Angstroms.
Claim 15
Dependent Claim
76 words
The method of claim 4 wherein said source and drain regions are formed by an N- implantation of P31 with a dosage of between about 2 to 3 E 13 atoms/cm 2 and an energy of between about 45 to 55 Key followed by spacer formation followed by an N+ implantation of Arsenic with a dosage of between about 4.5 to 5.5 E 15 atoms/cm 2 and an energy of between about 70 to 90 Kev.
Claim 16
Dependent Claim
58 words
The method of claim 4 wherein said insulating layer is formed of a first layer of undoped silicon oxide with a thickness of between about 1800 to 2200 Angstroms and a second layer of borophosphosilicate glass with a thickness of between about 6400 to 7000 Angstroms for a total insulator thickness of between about 8200 to 9200 Angstroms.
Claim 17
Dependent Claim
13 words
The method of claim 4 wherein said metal layer is composed of aluminum.
Claim 18
Dependent Claim
13 words
The method of claim 4 wherein said metal layer is composed of AlSiCu.
Claim 19
Independent Claim
432 words
The method of fabricating an integrated circuit with buried contacts comprising: forming a gate oxide layer on a silicon substrate; depositing a first layer of polysilicon over said gate oxide layer; patterning said first polysilicon layer to form openings to said gate oxide layer; etching away said gate oxide layer within said openings; rinsing and drying said silicon substrate after said etching away of said gate oxide layer whereby water spots are formed on the surface of said silicon substrate as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform first thin layer of native oxide is formed on the surface of said silicon substrate as a result of said H 2 O 2 cleaning process; depositing a second layer of polysilicon over said first thin native oxide layer; doping said second polysilicon layer with a concentration sufficient to penetrate through said uniform first thin native oxide layer to form said buried contact regions in said silicon substrate; annealing said silicon substrate to drive said doping concentration into said silicon substrate to form said buried contact regions whereby a second thin layer of native oxide forms on the surface of said second polysilicon layer; etching away said second thin native oxide layer; rinsing and drying said silicon substrate after said etching away of said second native oxide layer whereby water spots are formed on the surface of said second polysilicon layer as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform third thin layer of native oxide is formed on the surface of said second polysilicon layer as a result of said H 2 O 2 cleaning process; etching said silicon substrate to remove said third native oxide layer; depositing a layer of tungsten silicide on top of said second polysilicon layer; patterning said tungsten silicide layer and said second and first polysilicon layers to form gate electrodes on the surface of said silicon substrate; forming source and drain regions within openings to said silicon substrate between said gate electrodes; forming spacers on the sidewalls of said gate electrodes; depositing an insulating layer over the surface of said silicon substrate; etching contact openings through said insulating layer to said second polysilicon layer and to said silicon substrate; depositing a metal layer over said insulating layer and filling said openings to said second polysilicon layer and said silicon substrate; and patterning said metal layer to complete said buried contacts within said integrated circuit.
Claim 20
Independent Claim
432 words
The method of fabricating an integrated circuit with buried contacts comprising: forming a gate oxide layer on a silicon substrate; depositing a first layer of polysilicon over said gate oxide layer; patterning said first polysilicon layer to form openings to said gate oxide layer; etching away said gate oxide layer within said openings; rinsing and drying said silicon substrate after said etching away of said gate oxide layer whereby water spots are formed on the surface of said silicon substrate as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform first thin layer of native oxide is formed on the surface of said silicon substrate as a result of said H 2 O 2 cleaning process; depositing a second layer of polysilicon over said first thin native oxide layer; doping said second polysilicon layer with a concentration sufficient to penetrate through said uniform first thin native oxide layer to form said buried contact regions in said silicon substrate; annealing said silicon substrate to drive said doping concentration into said silicon substrate to form said buried contact regions whereby a second thin layer of native oxide forms on the surface of said second polysilicon layer; etching away said second thin native oxide layer; rinsing and drying said silicon substrate after said etching away of said second native oxide layer whereby water spots are formed on the surface of said second polysilicon layer as a result of said rinsing and drying; H 2 O 2 cleaning of said silicon substrate to remove said water spots whereby a uniform third thin layer of native oxide is formed on the surface of said second polysilicon layer as a result of said H 2 O 2 cleaning process; etching said silicon substrate to remove said third native oxide layer; depositing a layer of tungsten silicide on top of said second polysilicon layer; patterning said tungsten silicide layer and said second and first polysilicon layers to form gate electrodes on the surface of said silicon substrate; forming source and drain regions within openings to said silicon substrate between said gate electrodes; forming spacers on the sidewalls of said gate electrodes; depositing an insulating layer over the surface of said silicon substrate; etching contact openings through said insulating layer to said second polysilicon layer and to said silicon substrate; depositing a metal layer over said insulating layer and filling said openings to said second polysilicon layer and said silicon substrate; and patterning said metal layer to complete said buried contacts within said integrated circuit.
Claim 21
Dependent Claim
20 words
The method of claim 17 wherein the thickness of said gate oxide layer is between about 180 to 220 Angstroms.
Claim 22
Dependent Claim
22 words
The method of claim 17 wherein said first polysilicon layer is deposited to a thickness of between about 700 to 900 Angstroms.
Claim 23
Dependent Claim
31 words
The method of claim 17 wherein said etching away of said gate oxide layer is performed with a hydrofluoric acid etch in the ratio 10 H 2 O : 1 HF.
Claim 24
Dependent Claim
57 words
The method of claim 17 wherein said second polysilicon layer is doped by ion implantation of phosphorus P31 with a dosage of between about 5 E 15 to 1 E 16 atoms/cm 2 and energy of between about 45 to 55 Kev whereby said implant dosage is sufficient to go through said uniform third native oxide layer.
Claim 25
Dependent Claim
22 words
The method of claim 17 wherein said second polysilicon layer is deposited to a thickness of between about 1350 to 1650 Angstroms.
Claim 26
Dependent Claim
32 words
The method of claim 17 wherein said etching away of said second native oxide layer is performed by a hydrofluoric acid etch in the concentration 10 H 2 O : 1 HF.
Claim 27
Dependent Claim
107 words
The method of claim 17 wherein said H 2 O 2 cleaning comprises the steps of immersing said substrate in a solution of NH 4 OH + H 2 O 2 + H 2 O in the concentration 5: 1:1 at a temperature of between about 60° to 80° C., followed by a rinsing said substrate with de-ionized water, immersing said substrate in a solution of HCl + H 2 O 2 + H 2 O in the concentration 6:1:1 at a temperature of between about 60° to 80° C., rinsing said substrate with de-ionized water for a second time, and spinning said substrate to dry it.
Claim 28
Dependent Claim
32 words
The method of claim 24 wherein said H 2 O 2 cleaning results in the growth of a controlled native oxide layer having a thickness of between about 10 to 30 Angstroms.
Claim 29
Dependent Claim
21 words
The method of claim 17 wherein said etching to remove said third native oxide layer is a hydrofluoric acid vapor etch.
Claim 30
Dependent Claim
42 words
The method of claim 17 wherein said tungsten silicide layer is deposited by low pressure chemical vapor deposition using tungsten hexafluorine and silane (WF 6 /SiH 4 ) as the active agents to a thickness of between about 1500 to 2000 Angstroms.
Claim 31
Dependent Claim
71 words
The method of claim 17 wherein said source and drain regions are formed by an N-implantation of P31 with a dosage of between about 2 to 3 E 13 atoms/cm 2 and an energy of between about 45 to 55 Kev followed by an N+ implantation of Arsenic with a dosage of between about 4.5 to 5.5 E 15 atoms/cm 2 and an energy of between about 70 to 90 Kev.
Claim 32
Dependent Claim
58 words
The method of claim 17 wherein said insulating layer is formed of a first layer of undoped silicon oxide with a thickness of between about 1800 to 2200 Angstroms and a second layer of phosphosilicate glass with a thickness of between about 6400 to 7000 Angstroms for a total insulator thickness of between about 8200 to 9200 Angstroms.
Claim 33
Dependent Claim
13 words
The method of claim 17 wherein said metal layer is composed of aluminum.
Claim 34
Dependent Claim
13 words
The method of claim 17 wherein said metal layer is composed of AlSiCu.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-11 | 1998-01-10 | 1998-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-11 | 2002-01-10 | 2002-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-11 | 2006-01-10 | 2006-07-12 | $7700.00 | Window Closed / Lapsed |