Lithium secondary battery using a non-aqueous solvent
Assignee: Mitsubishi Gas Chemical Co Inc
•
Filing: 1992-12-17
•
Granted: 1994-07-05
•
Expires: 2012-12-17
Abstract
Abstract The invention provides for a lithium secondary battery using a non-aqueous solvent wherein the anode material is prepared by the pyrolysis of organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitro compound or with a nitrating agent. The anode material contains at least the elements carbon and nitrogen, the nitrogen content ranging from 0.5% to 6% by weight. Eighty percent or more of this nitrogen is bound to carbon by either C--N or C═N bonds. The ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Inventors
- 👤 Yuzuru Takahashi
- 👤 Kenichi Nakamura
- 👤 Jitsuo Oishi
- 👤 Hiroaki Shigeta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:19
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/36; H01M4/58; H01M4/583; H01M4/587; H01M10/00; H01M10/05; H01M10/052; H01M10/0525; H01M4/13; H01M4/131; H01M4/133; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
115 words
A lithium secondary battery using a non-aqueous solvent wherein the anode material is prepared by the pyrolysis of organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitrocompound or with a nitrating agent, the anode material containing at least the elements carbon and nitrogen; the nitrogen content ranging from 0.5% to 6% by weight and 80% or more of this nitrogen is bound to carbon by either C--N or C═N bonds; and the ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Claim 2
Dependent Claim
115 words
A lithium secondary battery using a non-aqueous solvent wherein the anode material is prepared by the pyrolysis of organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitrocompound or with a nitrating agent, the anode material containing at least the elements carbon and nitrogen; the nitrogen content ranging from 0.5% to 6% by weight and 80% or more of this nitrogen is bound to carbon by either C--N or C═N bonds; and the ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Claim 3
Dependent Claim
31 words
A lithium secondary battery using a non-aqueous solvent according to claim 1 wherein the conjugated polycyclic compound is a pitch having a softening point of 170° C. or less or tar.
Claim 4
Dependent Claim
19 words
A lithium secondary battery using a non-aqueous solvent according to claim 2 wherein the nitrocompound is an aromatic nitrocompound.
Claim 5
Dependent Claim
18 words
A lithium secondary battery using a non-aqueous solvent according to claim 3 wherein the aromatic nitrocompound is dinitronaphthalene.
Claim 6
Dependent Claim
40 words
A lithium secondary battery using a non-aqueous solvent according to claim 1 wherein the anode material is prepared by pyrolyzing the organic compound starting materials at temperatures of from 800° C. to 1800° C. under an atmosphere of non-reactive gas,
Claim 7
Dependent Claim
36 words
A lithium secondary battery using a non-aqueous solvent according to claim 1 wherein the d 002 interlayer spacing of the pyrolyzed organic compound starting material is in the range of from 3.4 Å to 3.7 Å.
Claim 8
Dependent Claim
28 words
A lithium secondary battery using a non-aqueous solvent according to claim 1 wherein the crystallite size of the pyrolyzed organic compound starting material is 70 Å or less.
Claim 9
Dependent Claim
112 words
An anode material for a lithium secondary battery using a non-aqueous solvent prepared by pyrolyzing organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitrocompound or with a nitrating agent, the anode material containing at least the elements carbon and nitrogen; the nitrogen content ranging from 0.5% to 6% by weight and 80% or more of this nitrogen is bound to carbon by either C--N or C═N bonds; and the ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Claim 10
Dependent Claim
112 words
An anode material for a lithium secondary battery using a non-aqueous solvent prepared by pyrolyzing organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitrocompound or with a nitrating agent, the anode material containing at least the elements carbon and nitrogen; the nitrogen content ranging from 0.5% to 6% by weight and 80% or more of this nitrogen is bound to carbon by either C--N or C═N bonds; and the ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Claim 11
Dependent Claim
31 words
An anode material according to claim 8 wherein the conjugated polycyclic compound is a pitch having a softening point of 170° C. or less or tar and the nitrocompound is dinitronaphthalene.
Claim 12
Dependent Claim
121 words
An anode material is sheet form for use in the preparation of anodes for a secondary battery, which anode material is prepared by pyrolyzing organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitrocompound or with a nitrating agent, the anode material containing at least the elements carbon and nitrogen; the nitrogen content ranging from 0.5% to 6% by weight and 80% or more of this nitrogen is bound to carbon by either C--N or C═N bonds; and the ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Claim 13
Dependent Claim
121 words
An anode material is sheet form for use in the preparation of anodes for a secondary battery, which anode material is prepared by pyrolyzing organic compound starting materials obtained by reacting at least one conjugated polycyclic compound with a nitrocompound or with a nitrating agent, the anode material containing at least the elements carbon and nitrogen; the nitrogen content ranging from 0.5% to 6% by weight and 80% or more of this nitrogen is bound to carbon by either C--N or C═N bonds; and the ratio of the intensity of the x-ray photoelectron spectroscopy ("XPS") peak observed for the anode material at 401.2±0.2 eV to the intensity of peak observed for the anode material at 398.8±0.4 eV is 1.0:1 or more.
Claim 14
Dependent Claim
34 words
An anode material in sheet form according to claim 10 wherein the conjugated polycyclic compound is a pitch having a softening point of 170° C. or less or tar and the nitrocompound is dinitronaphthalene.
References Cited (Backward Citations)
JPS57208079A
Cited
JPS5893176A
Cited
JPS58102464A
Cited
US4423125A
Cited
JPS6054181A
Cited
JPS60221973A
Cited
US4615959A
Cited
US4725422A
Cited
US4702977A
Cited
US4668595A
Cited
JPH03137010A
Cited
US5093216A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-04 | 1998-01-03 | 1998-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-04 | 2002-01-03 | 2002-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-04 | 2006-01-03 | 2006-07-05 | $7700.00 | Window Closed / Lapsed |