Method of forming a fluorescent screen
Assignee: Samsung SDI Co Ltd
•
Filing: 1993-07-09
•
Granted: 1994-06-21
•
Expires: 2013-07-09
Abstract
Abstract The present invention discloses a phosphor slurry composition for color Braun tubes comprising deionized water, phosphor powder, polyvinyl alcohol, sodium dichromate, ethyl silicate and zinc sulfate. A color Braun tube manufactured using a phosphor slurry composition of the present invention shows an excellent mirror reflection effect and high luminescent brightness.
Inventors
- 👤 Ikchull Ihm
- 👤 Minho Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:29
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/02; C09K11/08; C09K11/025
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
116 words
A method of forming a fluorescent screen comprising the steps of: coating a panel of a Braun tube with a photosetting resin which has a photoadhesive property when exposed to ultraviolet light; drying the coating; exposing the coating to said light to form an adhesive film; and coating said film with a phosphor slurry composition, said composition being prepared by subjecting a mixture comprising: a) 100 parts by weight of phosphor powder, b) 120-130 parts by weight of polyvinyl alcohol, c) 5-6 parts by weight of sodium dichromate, d) 0.0009-0.5 parts by weight of ethyl silicate, e) 0.002-0.04 parts by weight of zinc sulfate and f) 120-130 parts by weight of deionized water, to ball milling.
Claim 2
Independent Claim
116 words
A method of forming a fluorescent screen comprising the steps of: coating a panel of a Braun tube with a photosetting resin which has a photoadhesive property when exposed to ultraviolet light; drying the coating; exposing the coating to said light to form an adhesive film; and coating said film with a phosphor slurry composition, said composition being prepared by subjecting a mixture comprising: a) 100 parts by weight of phosphor powder, b) 120-130 parts by weight of polyvinyl alcohol, c) 5-6 parts by weight of sodium dichromate, d) 0.0009-0.5 parts by weight of ethyl silicate, e) 0.002-0.04 parts by weight of zinc sulfate and f) 120-130 parts by weight of deionized water, to ball milling.
References Cited (Backward Citations)
US3887753A
Cited
JPS4921831A
Cited
SU990791A1
Cited
JPS5720651A
Cited
JPS5919156A
Cited
JPS62110230A
Cited
JPH01213387A
Cited
JPH02242880A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-20 | 1997-12-20 | 1998-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-20 | 2001-12-20 | 2002-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-20 | 2005-12-20 | 2006-06-21 | $7700.00 | Window Closed / Lapsed |