Rubber composition

Claim 2

A rubber composition obtained by curing with a peroxide a blend consisting of 100 parts by weight of an acrylic elastomer and from 20 to 100 parts by weight of a polyvinylidene fluoride resin relative to 100 parts by weight of the acrylic elastomer, wherein the acrylic elastomer comprises from 80 to 100% by weight of an alkoxyalkyl acrylate, from 0 to 20% by weight of acrylonitrile, from 0 to 5% by weight of a vinyl fatty acid.

Claim 3

The rubber composition according to claim 1, wherein the acrylic elastomer comprises from 85 to 95% by weight of an alkoxyalkyl acrylate and from 5 to 15% by weight of acrylonitrile.

Claim 4

The rubber composition according to claim 1, wherein the alkoxyalkyl acrylate is 2-methoxymethyl acrylate, 2-ethoxymethyl acrylate, 2-methoxyethyl acrylate, 2 -ethoxyethyl acrylate or 2-butoxyethyl acrylate.

Claim 5

The rubber composition according to claim 1, wherein the polyvinylidene fluoride resin is a homopolymer of vinylidene fluoride or a copolymer of vinylidene fluoride with other copolymerizable monomer selected from the group consisting of hexafluoropropylene, pentafluoropropylene trifluoroethylene, trifluorchloroethylene, tetrafluoroethylene, vinyl fluoride, perfluoro (methyl vinyl ether), perfluoro(propyl vinyl ether), other olefins and acrylic acid esters.

Claim 6

The rubber composition according to claim 1, wherein the blend is cured with from 1 to 10 parts by weight of the peroxide relative to 100 parts by weight of the acrylic elastomer.

Claim 7

A rubber composition consisting of a blend obtained by curing with a peroxide 100 parts by weight of an acrylic elastomer, from 20 to 100 parts by weight of a polyvinylidene fluoride resin relative to 100 parts by weight of the acrylic elastomer from 5 to 300 parts by weight of an inorganic filler relative to 100 parts by weight of the acrylic elastomer, and fro m0 to 100 parts by weight of a plasticizer relative to 100 parts by weight of the acrylic elastomer, wherein the acrylic elastomer comprises from 80 to 100% by weight of an alkoxyalkyl acrylate, from 0 to 20% by weight of acrylonitrile, from 0 to 5% by weight of ethylene and from 0 to 5% by weight of a vinyl fatty acid.

Claim 8

A rubber composition consisting of a blend obtained by curing with a peroxide 100 parts by weight of an acrylic elastomer, from 20 to 100 parts by weight of a polyvinylidene fluoride resin relative to 100 parts by weight of the acrylic elastomer from 5 to 300 parts by weight of an inorganic filler relative to 100 parts by weight of the acrylic elastomer, and fro m0 to 100 parts by weight of a plasticizer relative to 100 parts by weight of the acrylic elastomer, wherein the acrylic elastomer comprises from 80 to 100% by weight of an alkoxyalkyl acrylate, from 0 to 20% by weight of acrylonitrile, from 0 to 5% by weight of ethylene and from 0 to 5% by weight of a vinyl fatty acid.

Claim 9

A process for producing a rubber composition of claim 1, which comprises preparing a compound storck consisting of the blend consisting of 100 parts by weight of an acrylic elastomer and from 20 to 100 parts by weight of a polyvinylidene fluoride resin relative to 100 parts of the acrylic elastomer, wherein the acrylic elastomer comprises from 80 to 100% by weight of an alkoxyalkyl acrylate, from 0 to 20% by weight of acrylonitrile, from 0 to 5% by weight of ethylene and frmo 0 to 5% by weight of a vinyl fatty acid and the peroxide at a temperature lower than the melting point of the polyvinylidene fluoride resin and curing the blend with the peroxide at a temperature of at least the melting point of the polyvinylidene fluoride resin.

Claim 10

The rubber composition according to claim 7, which is formed into a hose, a diaphragm, a packing or a gasket to be in contact with a fuel oil.