Process for producing phosphorescent yarn and yarn produced by the process
Assignee: Afterglow Accent Yarns Inc
•
Filing: 1992-11-25
•
Granted: 1994-06-14
•
Expires: 2012-11-25
Abstract
Abstract Thermoplastic polymeric material in pelletized or chip form are initially coated with a wetting agent in a mixer, then a powdered phosphorescent pigment is added to the mixer and mixing continued until the pellets are substantially uniformly coated with phosphorescent powder. The coated polymeric material is then fed to an extruder where it is heated to form a melt and mixed to distribute the phosphorous material uniformly throughout the melt before being extruded to form phosphorescent textile fibers, filaments, yarns, tapes or fibrillated films having highly uniform phosphorescent properties.
Inventors
- 👤 Willard Owens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 15:01
CPC Classifications
D; D02; D02G; D02G3/00; D02G3/22; D02G3/34; D02G3/346; D01; D01F; D01F1/00; D01F1/02; D01F1/04; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2915
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
143 words
In a melt spin process for forming synthetic textile fiber filaments from a thermoplastic polymer in which the polymer in pellet form is fed into an extruder where it is heated and mixed to form a melt and the melt is extruded to form the filaments or fibers, the improvement comprising, initially combining predetermined amounts of polymer pellets and a wetting agent in a mixer and mixing to substantially uniformly wet the surface of the solid pellets, adding solid phosphorescent pigment in powdered form in an amount of from about 2% to about 15% by weight in the mixer and continuing to mix until the polymer pellets are substantially uniformly covered with pigment, and mixing and heating the pigment coated polymer in an extruder to form and extrude the melt whereby a highly uniform distribution of phosphorescent pigment is obtained throughout the filaments.
Claim 2
Dependent Claim
143 words
In a melt spin process for forming synthetic textile fiber filaments from a thermoplastic polymer in which the polymer in pellet form is fed into an extruder where it is heated and mixed to form a melt and the melt is extruded to form the filaments or fibers, the improvement comprising, initially combining predetermined amounts of polymer pellets and a wetting agent in a mixer and mixing to substantially uniformly wet the surface of the solid pellets, adding solid phosphorescent pigment in powdered form in an amount of from about 2% to about 15% by weight in the mixer and continuing to mix until the polymer pellets are substantially uniformly covered with pigment, and mixing and heating the pigment coated polymer in an extruder to form and extrude the melt whereby a highly uniform distribution of phosphorescent pigment is obtained throughout the filaments.
Claim 3
Dependent Claim
13 words
The process defined in claim 1 wherein said phosphorescent pigment comprises zinc sulfide.
Claim 4
Dependent Claim
19 words
The process defined in claim 2 wherein said polymer is selected from the group comprising polypropylene, nylon and polyesters.
Claim 5
Dependent Claim
36 words
The process defined in claim 1 wherein said polymer is nylon and wherein the step of adding solid phosphorescent pigment comprises adding from about 3% to about 12%, by weight of zinc sulfide to the polymer.
Claim 6
Dependent Claim
32 words
The process defined in claim 4 wherein the step of adding said wetting agent comprises adding from about 0.3% to about 5% of an oil compatible with nylon as the wetting agent.
Claim 7
Dependent Claim
13 words
The process defined in claim 5 wherein said wetting agent is mineral oil.
Claim 8
Dependent Claim
22 words
The process defined in claim 6 wherein the mean particle size of said zinc sulphide is no greater than about 30 microns.
Claim 9
Dependent Claim
35 words
The process defined in claim 1 wherein said polymer is polypropylene and wherein the step of adding phosphorescent pigment comprises adding from about 2% to about 5% by weight of zinc sulfide to the polymer.
Claim 10
Dependent Claim
31 words
The process defined in claim 8 wherein the step of adding said wetting agent comprises adding from about 0.1% to about 3% by weight of an oil compatible with the polypropylene.
Claim 11
Dependent Claim
13 words
The process defined in claim 9 wherein said wetting agent is mineral oil.
Claim 12
Dependent Claim
22 words
The process defined in claim 10 wherein the mean particle size of said zinc sulphide is no greater than about 30 microns.
Claim 13
Dependent Claim
26 words
The process defined in claim 1 wherein the step of extruding the melt comprises simultaneously melt spinning a plurality of filament to form a spun yarn.
Claim 14
Dependent Claim
15 words
The process defined in claim 12 wherein said yarn is a bulked continuous filament yarn.
Claim 15
Dependent Claim
26 words
Phosphorescent synthetic textile filaments formed by the process defined in claim 1, said filaments having a denier within the range of about 5 to about 100.
Claim 16
Dependent Claim
48 words
The phosphorescent synthetic textile filaments defined in claim 14 wherein the thermoplastic polymer is polypropylene and wherein said textile filaments contain from about 2% to about 7% by weight of phosphorescent material and wherein the filaments have a denier within the range of about 10 to about 60.
Claim 17
Dependent Claim
44 words
The phosphorescent synthetic textile filaments defined in claim 15 wherein said phosphorescent material is present in the amount of from about 3% to about 5%, by weight and wherein the mean particle size of the phosphorescent material is no greater than about 30 microns.
Claim 18
Dependent Claim
31 words
The phosphorescent synthetic textile filaments defined in claim 14 wherein said thermoplastic polymer is nylon and wherein said phosphorescent material has a mean particle size no greater than about 30 microns.
Claim 19
Dependent Claim
25 words
The phosphorescent synthetic textile filaments defined in claim 17 wherein said phosphorescent material is present in an amount of from about 3% to about 10%.
Claim 20
Dependent Claim
25 words
The phosphorescent spun polymeric textile filaments defined in claim 18 wherein said filaments have a denier within the range of about 10 to about 60.
Claim 21
Dependent Claim
29 words
Phosphorescent synthetic textile yarn formed by the process defined in claim 12, the filaments of said yarn having a denier within the range of about 5 to about 100.
Claim 22
Dependent Claim
50 words
The phosphorescent synthetic textile yarn defined in claim 20 wherein the thermoplastic polymer is polypropylene and wherein said filaments of said yarn contain from about 2% to about 7% by weight of phosphorescent material and wherein the filaments have a denier within the range of about 10 to about 60.
Claim 23
Dependent Claim
44 words
The phosphorescent synthetic textile yarn defined in claim 21 wherein said phosphorescent material is present in an amount of from about 3% to about 5%, by weight and wherein the mean particle size of the phosphorescent material is no greater than about 30 microns.
Claim 24
Dependent Claim
31 words
The phosphorescent synthetic textile yarn defined in claim 20 wherein said thermoplastic polymer is nylon and wherein said phosphorescent material has a mean particle size no greater than about 30 microns.
Claim 25
Dependent Claim
25 words
The phosphorescent synthetic textile yarn defined in claim 23 wherein said phosphorescent material is present in an amount of from about 3% to about 10%.
Claim 26
Dependent Claim
63 words
A phosphorescent spun polymeric textile yarn containing a phosphorescent pigment in an amount of about 2% to about 15% by weight substantially uniformly dispersed throughout the yarn filaments, said yarn having a filament denier within the range of about 5 to about 100, and said phosphorescent pigment being a finely divided solid having a mean particle size no greater than about 30 microns.
Claim 27
Dependent Claim
63 words
A phosphorescent spun polymeric textile yarn containing a phosphorescent pigment in an amount of about 2% to about 15% by weight substantially uniformly dispersed throughout the yarn filaments, said yarn having a filament denier within the range of about 5 to about 100, and said phosphorescent pigment being a finely divided solid having a mean particle size no greater than about 30 microns.
Claim 28
Dependent Claim
23 words
The phosphorescent spun polymeric yarn defined in claim 25 wherein said filament denier is within the range of about 10 to about 60.
Claim 29
Dependent Claim
31 words
The phosphorescent spun polymeric yarn defined in claim 26 wherein said polymer is nylon and wherein said pigment is present in an amount of about 3% to about 12%, by weight.
Claim 30
Dependent Claim
33 words
The phosphorescent spun polymeric yarn defined in claim 26 wherein the polymer is polypropylene and wherein said phosphorescent material is present in an amount of from about 3% to about 5%, by weight.
References Cited (Backward Citations)
US2084526A
Cited
US2382355A
Cited
GB609197A
Cited
US2457808A
Cited
US2635969A
Cited
US2787558A
Cited
US3193536A
Cited
US3291668A
Cited
US4546042A
Cited
US4781647A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-13 | 1997-12-13 | 1998-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-13 | 2001-12-13 | 2002-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-13 | 2005-12-13 | 2006-06-14 | $7700.00 | Window Closed / Lapsed |