Method of removing short-circuit portion in photoelectric conversion device
Assignee: Canon Inc
•
Filing: 1993-08-02
•
Granted: 1994-06-14
•
Expires: 2013-08-02
Abstract
Abstract A method of removing any short-circuit defect existing in a photoelectric conversion device such as solar batteries having a semiconductor layer which is disposed between an upper transparent electrode and a lower electrode and which produces an electromotive force when irradiated with a light. The method comprises applying a voltage between the photoelectric conversion device and a counter electrode across an electrolytic solution containing hydrogen ions and/or hydronium ions. The electrolytic solution is an aqueous solution of an electrolyte or electrolytes selected from a group consisting of inorganic acids, organic acids, inorganic bases, organic bases and salts of metals having standard electrode potential levels which are minus relative to the standard hydrogen electrode potential and which have absolute values greater than hydrogen super voltage.
Inventors
- 👤 Souichiro Kawakami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:09
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/135; H10F71/10; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S136/00; Y10S136/29
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
153 words
A method for removing a short-circuit portion in a photoelectric conversion device producing a photoelectromotive force comprising the steps of: (i) forming a semiconductor layer, between a lower electrode and an upper electrode said semiconductor layer generating photoelectromotive force upon absorption of light; (ii) preparing an electrolyte solution and immersing said photoelectric conversion device in said electrolyte solution, said electrolyte solution comprising hydrogen ions or hydronium ions or hydrogen ions and hydronium ions and having a specific electric conductivity in the range of 0.001 S/cm to 10 S/cm which causes an electrochemical reaction which selectively removes said short circuit portion; (iii) immersing a counter electrode across from said photoelectric conversion device said electrolyte solution; and (iv) applying a voltage between said photoelectric conversion device and said counter electrode such that the lower electrode of the photoelectric conversion device serves as a cathode, thereby causing solution of the short-circuit portion into said electolyte solution.
Claim 2
Independent Claim
153 words
A method for removing a short-circuit portion in a photoelectric conversion device producing a photoelectromotive force comprising the steps of: (i) forming a semiconductor layer, between a lower electrode and an upper electrode said semiconductor layer generating photoelectromotive force upon absorption of light; (ii) preparing an electrolyte solution and immersing said photoelectric conversion device in said electrolyte solution, said electrolyte solution comprising hydrogen ions or hydronium ions or hydrogen ions and hydronium ions and having a specific electric conductivity in the range of 0.001 S/cm to 10 S/cm which causes an electrochemical reaction which selectively removes said short circuit portion; (iii) immersing a counter electrode across from said photoelectric conversion device said electrolyte solution; and (iv) applying a voltage between said photoelectric conversion device and said counter electrode such that the lower electrode of the photoelectric conversion device serves as a cathode, thereby causing solution of the short-circuit portion into said electolyte solution.
Claim 3
Dependent Claim
66 words
A method according to claim 1, wherein said electrolyte solution contains at least on electrolyte selected from a group consisting of an inorganic acid, an organic acid, an inorganic base, an organic base and a salt of a metal having a standard electrode potential level which is minus relative to the standard hydrogen electrode potential and which has an absolute value greater than hydrogen over voltage.
Claim 4
Dependent Claim
23 words
A method according to claim 1, wherein the concentration of the electrolyte in said electrolyte solution is from 2×10 -4 mol/1 to 5.0mol/1.
Claim 5
Dependent Claim
23 words
A method according to claim 2, wherein the concentration of the electrolyte in said electrolyte solution is from 2×10 -4 mol/1 to 5.0mol/1.
Claim 6
Independent Claim
27 words
A method according to claims 1, wherein said voltage is not lower than the hydrogen generating potential of said electrolyte solution and no greater than 10.0 V.
Claim 7
Dependent Claim
27 words
A method according to claim 2, wherein said voltage is not lower than the hydrogen generating potential of said electrolyte solution and no greater than 10.0 V.
Claim 8
Dependent Claim
30 words
A method according to claim 1, wherein the mean value of the current density flowing in said photoelectric conversion device is from 0.1 mA/cm 2 to 1 A/cm 2 .
Claim 9
Dependent Claim
30 words
A method according to claim 2, wherein the mean value of the current density flowing in said photoelectric conversion device is from 0.1 mA/cm 2 to 1 A/cm 2 .
Claim 10
Dependent Claim
30 words
A method according to claim 3, wherein the mean value of the current density flowing in said photoelectric conversion device is from 0.1 mA/cm 2 to 1 A/cm 2 .
Claim 11
Independent Claim
171 words
A method of removing a short-circuit portion in a photoelectromotive force producing a photoelectric conversion device comprising the steps of: (i) forming said photoelectric conversion device on a flexible substrate; (ii) forming a semiconductor layer between a lower electrode and an upper electrode, said semiconductor layer generating photoelectric conversion force upon absorption of light; (iii) preparing an electrolyte solution and immersing said photoelectromotive device in said electrolyte solution, said electrolyte solution comprising hydrogen ions or hydronium ions or hydrogen ions and hydronium ions and having a specific electric conductivity in the range of 0.001 Scm to 10 S/cm which causes an electrochemical reaction which selectively removes said short circuit portion; (iv) immersing a counter electrode across from photoelectric conversion device in said electrolyte solution; (v) feeding said flexible substrate onto a means for taking up said substrate; and (vi) applying a voltage between said photoelectric conversion device and said counter electrode such that said counter electrode serves an a anode, thereby causing solution of the short-circuit portion into said electrolyte solution.
Claim 12
Independent Claim
171 words
A method of removing a short-circuit portion in a photoelectromotive force producing a photoelectric conversion device comprising the steps of: (i) forming said photoelectric conversion device on a flexible substrate; (ii) forming a semiconductor layer between a lower electrode and an upper electrode, said semiconductor layer generating photoelectric conversion force upon absorption of light; (iii) preparing an electrolyte solution and immersing said photoelectromotive device in said electrolyte solution, said electrolyte solution comprising hydrogen ions or hydronium ions or hydrogen ions and hydronium ions and having a specific electric conductivity in the range of 0.001 Scm to 10 S/cm which causes an electrochemical reaction which selectively removes said short circuit portion; (iv) immersing a counter electrode across from photoelectric conversion device in said electrolyte solution; (v) feeding said flexible substrate onto a means for taking up said substrate; and (vi) applying a voltage between said photoelectric conversion device and said counter electrode such that said counter electrode serves an a anode, thereby causing solution of the short-circuit portion into said electrolyte solution.
Claim 13
Dependent Claim
66 words
A method according to claim 10, wherein said electrolyte solution contains at least one electrolyte selected form the group consisting of an inorganic acid, an organic acid, an inorganic base, an organic base and a salt of a metal having a standard electrode potential level which is minus relative to the standard hydrogen electrode potential and which has an absolute value greater than hydrogen over voltage.
Claim 14
Dependent Claim
23 words
A method according to claim 10, wherein the concentration of the electrolyte in said electrolyte solution is from 2×10 -4 mol/1 to 5.0mol/1.
Claim 15
Dependent Claim
23 words
A method according to claim 11, wherein the concentration of the electrolyte in said electrolyte solution is from 2×10 -4 mol/1 to 5.0mol/1.
Claim 16
Dependent Claim
27 words
A method according to claim 10, wherein said voltage is not lower than the hydrogen generating potential of said electrolyte solution and no greater than 10.0 V.
Claim 17
Dependent Claim
27 words
A method according to claim 11, wherein said voltage is not lower than the hydrogen generating potential of said electrolyte solution and no greater than 10.0 V.
Claim 18
Dependent Claim
30 words
A method according to claim 10, wherein the mean value of the current density flowing in said photoelectric conversion device is from 0.1 mA/cm 2 to 1 A/cm 2 .
Claim 19
Dependent Claim
30 words
A method according to claim 11, wherein the mean value of the current density flowing in said photoelectric conversion device is from 0.1 Ma/cm 2 to 1 A/cm 2 .
Claim 20
Dependent Claim
30 words
A method according to claim 12, wherein the mean value of the current density flowing in said photoelectric conversion device is from 0.1 mA/cm 2 to 1 A/cm 2 .
Claim 21
Dependent Claim
24 words
A method according to claim 10, wherein said substrate is fed from a first feed roll and taken up by a second feed roll.
References Cited (Backward Citations)
JPS5994473A
Cited
US4451970A
Cited
US4464823A
Cited
US4510674A
Cited
US4510675A
Cited
JPS6253958A
Cited
US4729970A
Cited
US4900691A
Cited
US5084400A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-13 | 1997-12-13 | 1998-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-13 | 2001-12-13 | 2002-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-13 | 2005-12-13 | 2006-06-14 | $7700.00 | Window Closed / Lapsed |