Composite molding of resin-bonded magnet for machine parts and process for producing the same
Assignee: Kanegafuchi Chemical Industry Co Ltd
•
Filing: 1992-04-03
•
Granted: 1994-06-07
•
Expires: 2012-04-03
Abstract
Abstract A machine part used as a magnet roll for developing and a process for producing the same. The machine part constitutes a member of a developing machine for an electrophotographic process such as a copier and facsimile, and a laser printer as well. The machine part comprises a shaft having a resin-bonded magnet layer provided on the outer periphery thereof. The composite molding of a resin-bonded magnet is produced by molding and establishing a composition for a thermoplastic resin-bonded magnet comprising from 35 to 60 % by volume of a thermoplastic resin and from 40 to 65 % by volume of a hard ferrite powder into a cylinder of uniform thickness on the outer periphery of a shaft, obtained is a thin resin-bonded magnet layer having a surface roughness of 5 mu m or less and free of seams which have generated during molding, the thin resin-bonded magnet layer further having provided on the surface a plurality of magnetic poles at a small spacing.
Inventors
- 👤 Yasunori Matsunari
- 👤 Toshiaki Ishimaru
- 👤 Yasushi Kakehashi
- 👤 Shogo Miki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 05:49
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/06; G03G15/08; G03G15/09; G03G15/0921
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
198 words
A composite molding of a resin-bonded magnet for use as a machine part, said machine part comprising a shaft having a resin-bonded magnet layer provided on the outer periphery thereof, and being a magnet roll used for developing and which constitutes a member of a developing machine for an electrophotographic process, wherein, said composite molding of a resin-bonded magnet is produced by molding and establishing a composition for a thermoplastic resin-bonded magnet comprising from 35 to 60% by volume of a thermoplastic resin and from 40 to 65% by volume of a hard ferrite powder into a cylinder of uniform thickness on the outer periphery of a shaft having a thin layer of a thermoplastic resin adhesive thereon, said thermoplastic resin adhesive having a hot melt temperature lower than a melt molding temperature of the composition for the thermoplastic resin-bonded magnet, to thereby obtain a thin resin-bonded magnet layer having a surface roughness of 5 μm or less and free of seams which have generated during molding joined to the shaft by the thermoplastic resin adhesive, and said thin resin-bonded magnet layer has a surface further having provided thereon of plurality of magnetic poles at a small spacing.
Claim 2
Dependent Claim
198 words
A composite molding of a resin-bonded magnet for use as a machine part, said machine part comprising a shaft having a resin-bonded magnet layer provided on the outer periphery thereof, and being a magnet roll used for developing and which constitutes a member of a developing machine for an electrophotographic process, wherein, said composite molding of a resin-bonded magnet is produced by molding and establishing a composition for a thermoplastic resin-bonded magnet comprising from 35 to 60% by volume of a thermoplastic resin and from 40 to 65% by volume of a hard ferrite powder into a cylinder of uniform thickness on the outer periphery of a shaft having a thin layer of a thermoplastic resin adhesive thereon, said thermoplastic resin adhesive having a hot melt temperature lower than a melt molding temperature of the composition for the thermoplastic resin-bonded magnet, to thereby obtain a thin resin-bonded magnet layer having a surface roughness of 5 μm or less and free of seams which have generated during molding joined to the shaft by the thermoplastic resin adhesive, and said thin resin-bonded magnet layer has a surface further having provided thereon of plurality of magnetic poles at a small spacing.
Claim 3
Dependent Claim
27 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein said shaft is made of a magnetic metal.
Claim 4
Dependent Claim
34 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein said composition for the thermoplastic resin-bonded magnet has a dielectric constant of 9 or higher.
Claim 5
Dependent Claim
41 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein said hard ferrite powder is composed of fine grains 1.3 μm or less in average diameter and having obtained by wet grinding.
Claim 6
Dependent Claim
57 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein said hard ferrite powder is composed of fine grains 1.3 μm or less in average diameter, having obtained by wet grinding and further classified and passed through a sieve having a mesh opening of 24 mesh or finer.
Claim 7
Dependent Claim
27 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein said thermoplastic resin has a small permanent set.
Claim 8
Dependent Claim
34 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein said thermoplastic resin is composed of surface-roughened resin particles 1 mm or less in diameter.
Claim 9
Dependent Claim
44 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 1, wherein the surface of said resin-bonded magnet layer is smoothed by lathe turning or by surface machining which comprises a combination of lathe turning and polishing.
Claim 10
Dependent Claim
175 words
A composite molding of a resin-bonded magnet for use as a machine part, said machine part comprising a shaft having a resin-bonded magnet layer provided on the outer periphery thereof and being a field magnet rotor for use in motors, wherein, said composite molding of a resin-bonded magnet is produced by molding and establishing a composition for a thermoplastic resin-bonded magnet comprising from 30 to 70% by volume of a thermoplastic resin and from 30 to 70% by volume of a hard ferrite powder into a cylinder of uniform thickness on the outer periphery of a shaft having a thin layer of a thermoplastic resin adhesive thereon, said thermoplastic resin adhesive having a hot melt temperature lower than a melt molding temperature of the composition for the thermoplastic resin-bonded magnet, to thereby obtain a resin-bonded magnet layer free of seams which have generated during molding joined to the shaft by the thermoplastic resin adhesive, and said resin-bonded magnet layer has a surface having provided thereon a plurality of a magnetic poles at a small spacing.
Claim 11
Dependent Claim
175 words
A composite molding of a resin-bonded magnet for use as a machine part, said machine part comprising a shaft having a resin-bonded magnet layer provided on the outer periphery thereof and being a field magnet rotor for use in motors, wherein, said composite molding of a resin-bonded magnet is produced by molding and establishing a composition for a thermoplastic resin-bonded magnet comprising from 30 to 70% by volume of a thermoplastic resin and from 30 to 70% by volume of a hard ferrite powder into a cylinder of uniform thickness on the outer periphery of a shaft having a thin layer of a thermoplastic resin adhesive thereon, said thermoplastic resin adhesive having a hot melt temperature lower than a melt molding temperature of the composition for the thermoplastic resin-bonded magnet, to thereby obtain a resin-bonded magnet layer free of seams which have generated during molding joined to the shaft by the thermoplastic resin adhesive, and said resin-bonded magnet layer has a surface having provided thereon a plurality of a magnetic poles at a small spacing.
Claim 12
Dependent Claim
35 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 9, wherein said hard ferrite powder is composed of fine grains 1.3 μm or less in average diameter.
Claim 13
Dependent Claim
34 words
The composite molding of a resin-bonded magnet for use as a machine part as claimed in claim 9, wherein said thermoplastic resin is composed of surface-roughened resin particles 1 mm or less in diameter.
References Cited (Backward Citations)
US1025616A
Cited
JPS53125497A
Cited
US4496303A
Cited
US4597661A
Cited
EP0128508A2
Cited
US4587699A
Cited
JPS60173964A
Cited
JPS60182705A
Cited
JPS60183708A
Cited
JPS60225179A
Cited
JPS60229078A
Cited
JPS61115305A
Cited
US4662311A
Cited
EP0217966A1
Cited
US4689163A
Cited
US4981635A
Cited
EP0429684A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-06 | 1997-12-06 | 1998-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-06 | 2001-12-06 | 2002-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-06 | 2005-12-06 | 2006-06-07 | $7700.00 | Window Closed / Lapsed |