Patterning of indium-tin oxide via selective reactive ion etching
Assignee: General Electric Co
•
Filing: 1991-11-14
•
Granted: 1994-06-07
•
Expires: 2011-11-14
Abstract
Abstract Indium-tin oxide is selective etched relative to silicon, molybdenum, aluminum, titanium, silicon oxide and silicon nitride using an organic radical and oxygen containing plasma which contains sufficient oxygen to prevent deposition of undesirable films on non-etching portions of the component being etched and on the reactor surfaces. The plasma lacks halogenated gases. A minimum differential etch rate of 8:1 of indium-tin oxide to silicon results with the other materials etching slower than silicon or not at all.
Inventors
- 👤 Richard J. Saia
- 👤 Robert F. Kwasnick
- 👤 Ching-Yeu Wei
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:35
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/138; C; C04; C04B; C04B41/00; C04B41/53; C04B41/5338; C04B41/5346; C04B41/80; C04B41/91; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
86 words
In a method of etching indium-tin oxide by masking the indium-tin oxide to leave it exposed in the areas it is desired to remove, the improvement comprising: etching said indium-tin oxide in a plasma lacking halogenated gases and including an oxidizing agent and a non-halogenated source of organic radicals which react with said indium-tin oxide to form volatile metallorganic compounds, said oxidizing agent and said organic radicals being present in relative concentrations which prevent deposition of a carbonaceous film on non-indium-tin oxide portions of said structure.
Claim 2
Dependent Claim
86 words
In a method of etching indium-tin oxide by masking the indium-tin oxide to leave it exposed in the areas it is desired to remove, the improvement comprising: etching said indium-tin oxide in a plasma lacking halogenated gases and including an oxidizing agent and a non-halogenated source of organic radicals which react with said indium-tin oxide to form volatile metallorganic compounds, said oxidizing agent and said organic radicals being present in relative concentrations which prevent deposition of a carbonaceous film on non-indium-tin oxide portions of said structure.
Claim 3
Dependent Claim
12 words
The improvement recited in claim 1 wherein: said oxidizing agent is oxygen.
Claim 4
Dependent Claim
16 words
The improvement recited in claim 2 wherein: some of said organic radicals are derived from acetone.
Claim 5
Dependent Claim
16 words
The improvement recited in claim 3 wherein: said plasma further comprises ions of an inert gas.
Claim 6
Dependent Claim
20 words
The improvement recited in claim 4 wherein: said inert gas is selected from the group consisting of nitrogen and argon.
Claim 7
Dependent Claim
13 words
The improvement recited in claim 1 wherein said organic radicals comprise methyl radicals.
Claim 8
Dependent Claim
20 words
The improvement recited in claim 1 wherein: said plasma is derived from a gas mixture comprising acetone, argon and oxygen.
Claim 9
Dependent Claim
41 words
The improvement recited in claim 7 wherein: said acetone comprises between 20% and 40% of said gas mixture; said argon comprises between 35% and 50% of said gas mixture; and said oxygen comprises between 15% and 30% of said gas mixture.
Claim 10
Dependent Claim
26 words
The improvement recited in claim 8 wherein: said oxygen is present at a partial pressure between 75% and 80% of the partial pressure of said acetone.
Claim 11
Dependent Claim
19 words
The improvement recited in claim 9 wherein: said oxygen partial pressure is substantially 75% of the acetone partial pressure.
Claim 12
Dependent Claim
50 words
The improvement recited in claim 1 wherein: said indium-tin oxide is to be completely removed in the areas from which it is to be removed and the material exposed by complete removal of said indium-tin oxide comprises at least one of silicon oxide, silicon nitride, titanium, molybdenum, aluminum and silicon.
Claim 13
Dependent Claim
124 words
In a method of selectively etching indium-tin oxide by masking the indium-tin oxide to leave it exposed in areas from which it is desired to remove said indium-tin oxide, the improvement comprising: initially etching said exposed indium-tin oxide in a first etchant to remove a significant portion of the indium-tin oxide to be removed; and further etching said indium-tin oxide in a plasma lacking halogenated gases and including an oxidizing agent and a non-halogenated source of organic radicals which react with said indium-tin oxide to form volatile metallorganic compounds, said oxidizing agent and said organic radicals being present in relative concentrations which prevent deposition of carbonaceous material on non-indium-tin oxide portions of said structure to expose the material underlying the indium-tin oxide being removed.
Claim 14
Dependent Claim
124 words
In a method of selectively etching indium-tin oxide by masking the indium-tin oxide to leave it exposed in areas from which it is desired to remove said indium-tin oxide, the improvement comprising: initially etching said exposed indium-tin oxide in a first etchant to remove a significant portion of the indium-tin oxide to be removed; and further etching said indium-tin oxide in a plasma lacking halogenated gases and including an oxidizing agent and a non-halogenated source of organic radicals which react with said indium-tin oxide to form volatile metallorganic compounds, said oxidizing agent and said organic radicals being present in relative concentrations which prevent deposition of carbonaceous material on non-indium-tin oxide portions of said structure to expose the material underlying the indium-tin oxide being removed.
Claim 15
Dependent Claim
18 words
The improvement recited in claim 12 wherein: said initial etching is performed in a plasma comprising chlorine ions.
Claim 16
Dependent Claim
16 words
The improvement recited in claim 13 wherein: said chlorine ions are derived from a chlorinated gas.
Claim 17
Dependent Claim
23 words
The improvement recited in claim 14 wherein: said chlorinated gas comprises one or more of Cl 2 , HCl and CCl 4 .
Claim 18
Dependent Claim
16 words
The improvement recited in claim 14 wherein: said plasma further comprises ions of an inert gas.
Claim 19
Dependent Claim
20 words
The improvement recited in claim 16 wherein: said inert gas is selected from the group consisting of nitrogen and argon.
Claim 20
Dependent Claim
12 words
The improvement recited in claim 13 wherein: said oxidizing agent is oxygen.
Claim 21
Dependent Claim
16 words
The improvement recited in claim 18 wherein: some of said organic radicals are derived from acetone.
Claim 22
Independent Claim
104 words
A method of providing a pattern of indium-tin oxide coated areas on a substrate comprising the steps of: depositing an indium-tin oxide film directly on said substrate; masking said indium-tin oxide to leave it exposed in the areas it is desired to remove; etching said indium-tin oxide in a plasma to expose the material underlying the indium-tin oxide being removed, said plasma lacking halogenated gases and including a non-halogenated source of organic radicals which react with said indium-tin oxide to form volatile metallorganic compounds and an oxidizing agent in relative concentrations which prevent deposition of carbonaceous material on non-indium-tin oxide portions of said structure.
Claim 23
Independent Claim
104 words
A method of providing a pattern of indium-tin oxide coated areas on a substrate comprising the steps of: depositing an indium-tin oxide film directly on said substrate; masking said indium-tin oxide to leave it exposed in the areas it is desired to remove; etching said indium-tin oxide in a plasma to expose the material underlying the indium-tin oxide being removed, said plasma lacking halogenated gases and including a non-halogenated source of organic radicals which react with said indium-tin oxide to form volatile metallorganic compounds and an oxidizing agent in relative concentrations which prevent deposition of carbonaceous material on non-indium-tin oxide portions of said structure.
Claim 24
Dependent Claim
13 words
The method recited in claim 20 wherein: said organic radicals include methyl radicals.
Claim 25
Dependent Claim
31 words
The method recited in claim 20 further comprising, after said masking step and prior to said etching step, the step of: partially etching said indium-tin oxide in a faster etching plasma.
Claim 26
Independent Claim
136 words
A method of providing a pattern of indium-tin oxide coated areas on a substrate comprising the steps of: depositing a indium-tin oxide film directly on said substrate; masking said indium-tin oxide to leave it exposed in the areas where it is desired to remove said indium-tin oxide; pre-etching said exposed indium-tin oxide in a first etchant to remove a significant portion of the indium-tin oxide to be removed; and finish etching said indium-tin oxide in a plasma lacking halogenated gases and including organic radicals derived from a non-halogenated source and further including an oxidizing agent in relative concentrations which prevent deposition of carbonaceous material on non-indium-tin oxide portions of said structure to expose the material underlying the indium-tin oxide being removed; said plasma being capable of reacting with said indium-tin oxide to form volatile metallorganic compounds.
Claim 27
Independent Claim
136 words
A method of providing a pattern of indium-tin oxide coated areas on a substrate comprising the steps of: depositing a indium-tin oxide film directly on said substrate; masking said indium-tin oxide to leave it exposed in the areas where it is desired to remove said indium-tin oxide; pre-etching said exposed indium-tin oxide in a first etchant to remove a significant portion of the indium-tin oxide to be removed; and finish etching said indium-tin oxide in a plasma lacking halogenated gases and including organic radicals derived from a non-halogenated source and further including an oxidizing agent in relative concentrations which prevent deposition of carbonaceous material on non-indium-tin oxide portions of said structure to expose the material underlying the indium-tin oxide being removed; said plasma being capable of reacting with said indium-tin oxide to form volatile metallorganic compounds.
Claim 28
Dependent Claim
12 words
The improvement recited in claim 23 wherein: said oxidizing agent is oxygen.
Claim 29
Dependent Claim
16 words
The improvement recited in claim 24 wherein: some of said organic radicals are derived from acetone.
Claim 30
Dependent Claim
16 words
The improvement recited in claim 25 wherein: said plasma further comprises ions of an inert gas.
Claim 31
Dependent Claim
20 words
The improvement recited in claim 26 wherein: said inert gas is selected from the group consisting of nitrogen and argon.
Claim 32
Independent Claim
65 words
A method of etching indium-tin oxide comprising: inserting said indium-tin oxide in a plasma etching system; providing non-halogenated source materials to create a plasma lacking halogenated gases and containing methyl radicals and oxidizing radicals; and activating said plasma etching system to create a plasma containing methyl radicals and oxidizing radicals for a period of time sufficient to remove a desired quantity of said indium-tin oxide.
Claim 33
Independent Claim
65 words
A method of etching indium-tin oxide comprising: inserting said indium-tin oxide in a plasma etching system; providing non-halogenated source materials to create a plasma lacking halogenated gases and containing methyl radicals and oxidizing radicals; and activating said plasma etching system to create a plasma containing methyl radicals and oxidizing radicals for a period of time sufficient to remove a desired quantity of said indium-tin oxide.
Claim 34
Independent Claim
76 words
A method of etching indium-tin oxide comprising: inserting said indium-tin oxide in a plasma etching system; providing non-halogenated source materials to create a plasma lacking halogenated gases and containing oxidizing radicals and organic radicals with which said indium-tin oxide can form volatile metallorganic compounds; and activating said plasma etching system to create a plasma containing said organic radicals and oxidizing radicals for a period of time sufficient to remove a desired quantity of said indium-tin oxide.
Claim 35
Independent Claim
76 words
A method of etching indium-tin oxide comprising: inserting said indium-tin oxide in a plasma etching system; providing non-halogenated source materials to create a plasma lacking halogenated gases and containing oxidizing radicals and organic radicals with which said indium-tin oxide can form volatile metallorganic compounds; and activating said plasma etching system to create a plasma containing said organic radicals and oxidizing radicals for a period of time sufficient to remove a desired quantity of said indium-tin oxide.
Claim 36
Dependent Claim
114 words
In a method of etching a metal oxide containing film in which the metal oxide is capable of forming volatile metallorganic compounds and in which the metal oxide containing film is masked to leave it exposed in those areas from which it is desired to remove said film, the improvement comprising: etching said metal oxide containing film in a plasma lacking halogenated gases and including oxygen and a non-halogenated source of organic radicals comprising acetone which react with said metal oxide to form volatile metalorganic compounds, said oxidizing agent and said organic radicals being present in relative concentrations which prevent deposition of a carbonaceous film on surfaces which do not etch in said plasma.
Claim 37
Dependent Claim
114 words
In a method of etching a metal oxide containing film in which the metal oxide is capable of forming volatile metallorganic compounds and in which the metal oxide containing film is masked to leave it exposed in those areas from which it is desired to remove said film, the improvement comprising: etching said metal oxide containing film in a plasma lacking halogenated gases and including oxygen and a non-halogenated source of organic radicals comprising acetone which react with said metal oxide to form volatile metalorganic compounds, said oxidizing agent and said organic radicals being present in relative concentrations which prevent deposition of a carbonaceous film on surfaces which do not etch in said plasma.
Claim 38
Dependent Claim
16 words
The improvement recited in claim 30 wherein: said plasma further comprises ions of an inert gas.
Claim 39
Dependent Claim
20 words
The improvement recited in claim 4 wherein: said inert gas is selected from the group consisting of nitrogen and argon.
Claim 40
Dependent Claim
20 words
The improvement recited in claim 1 wherein: said plasma is derived from a gas mixture comprising acetone, argon and oxygen.
Claim 41
Dependent Claim
14 words
The improvement recited in claim 1 wherein: said metal oxide film comprises indium-tin oxide.
Claim 42
Dependent Claim
14 words
The improvement recited in claim 1 wherein: said metal oxide film comprises indium oxide.
Claim 43
Dependent Claim
14 words
The improvement recited in claim 1 wherein: said metal oxide film comprises tin oxide.
Claim 44
Dependent Claim
65 words
In a method of plasma etching a metal oxide, the improvement comprising: providing non-halogenated source material to create a plasma lacking halogenated gases and comprising organic radicals and oxygen ions, said oxygen ions and said organic radicals being present in relative concentrations which prevent deposition of a carbonaceous film on surfaces which do not etch in said plasma, said source material comprising acetone and oxygen.
Claim 45
Dependent Claim
65 words
In a method of plasma etching a metal oxide, the improvement comprising: providing non-halogenated source material to create a plasma lacking halogenated gases and comprising organic radicals and oxygen ions, said oxygen ions and said organic radicals being present in relative concentrations which prevent deposition of a carbonaceous film on surfaces which do not etch in said plasma, said source material comprising acetone and oxygen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-06 | 1997-12-06 | 1998-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-06 | 2001-12-06 | 2002-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-06 | 2005-12-06 | 2006-06-07 | $7700.00 | Window Closed / Lapsed |