Method for thinning SOI films having improved thickness uniformity

Claim 1

A method of thinning SOI films for providing ultra-thin active device regions having excellent thickness uniformity and further having self-aligned isolation regions between the active device regions, said method comprising the steps of: a) providing a substrate having an isolation layer of a first thickness formed thereon and further having a single crystal silicon layer of a second thickness formed upon the isolation layer; b) growing a thermal oxide layer of a third thickness upon the silicon layer, patterning the thermal oxide layer in desired regions corresponding to polish stop regions between said active device regions, and etching the patterned thermal oxide layer in the desired regions; c) etching the silicon layer according to the patterned thermal oxide layer with a high selectivity Si:SiO 2 etch on the order of 100:1 such that the insulation layer is not significantly etched, whereby grooves are created in the silicon layer; d) depositing a layer of insulative polish stop material upon exposed surfaces of the thermal oxide, silicon, and isolation layers, the layer of polish stop material forming top, sidewall, and bottom polish stop material thereon, respectively, partially filling the grooves and further wherein the bottom polish stop material is of a prescribed thickness corresponding to a desired thickness of the active device regions yet to be completed; e) depositing polysilicon upon the layer of polish stop material to further completely fill the grooves; f) planarizing said polysilicon layer down to the top polish stop material; g) etching away the top polish stop material and the oxide layer using RIE; and h) chemically-mechanically polishing the silicon, sidewall polish stop material, and polysilicon down to the bottom polish stop material, whereby the bottom polish stop material serves as a visual polishing stop indicator and a self-aligned isolation region to adjacent active device regions, the active device regions having uniform thickness corresponding to the thickness of the bottom polish stop material.

Claim 2

A method of thinning SOI films for providing ultra-thin active device regions having excellent thickness uniformity and further having self-aligned isolation regions between the active device regions, said method comprising the steps of: a) providing a substrate having an isolation layer of a first thickness formed thereon and further having a single crystal silicon layer of a second thickness formed upon the isolation layer; b) growing a thermal oxide layer of a third thickness upon the silicon layer, patterning the thermal oxide layer in desired regions corresponding to polish stop regions between said active device regions, and etching the patterned thermal oxide layer in the desired regions; c) etching the silicon layer according to the patterned thermal oxide layer with a high selectivity Si:SiO 2 etch on the order of 100:1 such that the insulation layer is not significantly etched, whereby grooves are created in the silicon layer; d) depositing a layer of insulative polish stop material upon exposed surfaces of the thermal oxide, silicon, and isolation layers, the layer of polish stop material forming top, sidewall, and bottom polish stop material thereon, respectively, partially filling the grooves and further wherein the bottom polish stop material is of a prescribed thickness corresponding to a desired thickness of the active device regions yet to be completed; e) depositing polysilicon upon the layer of polish stop material to further completely fill the grooves; f) planarizing said polysilicon layer down to the top polish stop material; g) etching away the top polish stop material and the oxide layer using RIE; and h) chemically-mechanically polishing the silicon, sidewall polish stop material, and polysilicon down to the bottom polish stop material, whereby the bottom polish stop material serves as a visual polishing stop indicator and a self-aligned isolation region to adjacent active device regions, the active device regions having uniform thickness corresponding to the thickness of the bottom polish stop material.

Claim 10

A method of thinning SOI films for providing ultra-thin active device regions having excellent thickness uniformity and further having self-aligned isolation regions between the active device regions, said method comprising the steps of: a) providing a substrate having an isolation layer of a first thickness formed thereon and further having a single crystal silicon layer of a second thickness formed upon the isolation layer; b) growing a thermal oxide layer of a third thickness upon the silicon layer, patterning the thermal oxide layer in desired regions corresponding to polish stop regions between said active device regions, and etching the patterned thermal oxide layer in the desired regions; c) etching the silicon layer according to the patterned thermal oxide layer with a high selectivity Si:SiO 2 etch on the order of 100:1 such that the insulation layer is not significantly etched, whereby grooves are created in the silicon layer; d) growing a thin buffer oxide upon the sidewall edges of the grooves in the silicon layer; e) depositing a layer of insulative polish stop material upon exposed surfaces of the thermal oxide, buffer oxide, and isolation layers, the layer of polish stop material forming top, sidewall, and bottom polish stop material thereon, respectively, partially filling the grooves and further wherein the bottom polish stop material is of a prescribed thickness corresponding to a desired thickness of the active device regions yet to be completed; f) depositing polysilicon upon the layer of polish stop material to further completely fill the grooves; g) planarizing said polysilicon layer down to the top polish stop material; h) etching away the top polish stop material and the oxide layer using RIE; and i) chemically-mechanically polishing the silicon, sidewall buffer oxide, sidewall polish stop material, and polysilicon down to the bottom polish stop material, whereby the bottom polish stop material serves as a visual polishing stop indicator and a self-aligned isolation region to adjacent active device regions, the active device regions having uniform thickness corresponding to the thickness of the bottom polish stop material.

Claim 11

A method of thinning SOI films for providing ultra-thin active device regions having excellent thickness uniformity and further having self-aligned isolation regions between the active device regions, said method comprising the steps of: a) providing a substrate having an isolation layer of a first thickness formed thereon and further having a single crystal silicon layer of a second thickness formed upon the isolation layer; b) growing a thermal oxide layer of a third thickness upon the silicon layer, patterning the thermal oxide layer in desired regions corresponding to polish stop regions between said active device regions, and etching the patterned thermal oxide layer in the desired regions; c) etching the silicon layer according to the patterned thermal oxide layer with a high selectivity Si:SiO 2 etch on the order of 100:1 such that the insulation layer is not significantly etched, whereby grooves are created in the silicon layer; d) growing a thin buffer oxide upon the sidewall edges of the grooves in the silicon layer; e) depositing a layer of insulative polish stop material upon exposed surfaces of the thermal oxide, buffer oxide, and isolation layers, the layer of polish stop material forming top, sidewall, and bottom polish stop material thereon, respectively, partially filling the grooves and further wherein the bottom polish stop material is of a prescribed thickness corresponding to a desired thickness of the active device regions yet to be completed; f) depositing polysilicon upon the layer of polish stop material to further completely fill the grooves; g) planarizing said polysilicon layer down to the top polish stop material; h) etching away the top polish stop material and the oxide layer using RIE; and i) chemically-mechanically polishing the silicon, sidewall buffer oxide, sidewall polish stop material, and polysilicon down to the bottom polish stop material, whereby the bottom polish stop material serves as a visual polishing stop indicator and a self-aligned isolation region to adjacent active device regions, the active device regions having uniform thickness corresponding to the thickness of the bottom polish stop material.