Method of improving slipperiness of polyester film using a monodispersed glycol suspension of inorganic oxide particles
Assignee: Nippon Shokubai Co Ltd
•
Filing: 1989-03-13
•
Granted: 1994-05-31
•
Expires: 2009-03-13
Abstract
Abstract A monodispersed glycol suspension having excellent dispersion stability, including a monodispersed suspension in a glycol of spherical fine particles of an amorphous inorganic oxide having an average particle diameter of 0.05 to 5 micrometers and a relative particle size standard deviation of 1.0 to 1.5 and containing glycol bonded to its surface. This monodispersed suspension is useful as a raw material for the production of a polyester film having improved slipperiness.
Inventors
- 👤 Tadahiro Yoneda
- 👤 Saburo Nakahara
- 👤 Mitsuo Takeda
- 👤 Midori Kamo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:52
CPC Classifications
B; B01; B01J; B01J13/00; B82; B82Y; B82Y30/00; C; C01; C01B; C01B13/00; C01B13/14; C01B13/32; C08; C08G; C08G67/00; C08G67/02; C08J; C08J5/00; C08J5/18; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/34; C08K9/00; C08K9/04; G; G11; G11B; G11B5/00; G11B5/62; G11B5/73; G11B5/739; G11B5/73923; G11B5/73927; G11B5/73935; C01P; C01P2002/00; C01P2002/02; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/30; C01P2004/32; C01P2004/51; C01P2004/52; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/64; C01P2006/00; C01P2006/12; C01P2006/22; C01P2006/80; C01P2006/82
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
106 words
In a method for improving the slipperiness of a polyester film which comprises using a glycol slurry of fine inorganic oxide particles as a raw material for polyester film formation and preparing a film containing 0.005 to 2% by weight, based on the polyester, of the fine particles, the improvement wherein the glycol slurry of the fine particles is a monodispersed suspension in a glycol of spherical fine particles of an amorphous inorganic oxide having an average particle diameter of 0.05 to 5 micrometers and a relative particle size standard deviation of 1.0 to 1.5 and containing glycol bonded to surfaces of the spherical fine particles.
Claim 2
Dependent Claim
106 words
In a method for improving the slipperiness of a polyester film which comprises using a glycol slurry of fine inorganic oxide particles as a raw material for polyester film formation and preparing a film containing 0.005 to 2% by weight, based on the polyester, of the fine particles, the improvement wherein the glycol slurry of the fine particles is a monodispersed suspension in a glycol of spherical fine particles of an amorphous inorganic oxide having an average particle diameter of 0.05 to 5 micrometers and a relative particle size standard deviation of 1.0 to 1.5 and containing glycol bonded to surfaces of the spherical fine particles.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein said bonded glycol is present in an amount of 0.003 to 5 millimoles per gram of the fine oxide particles.
Claim 4
Dependent Claim
21 words
The method of claim 1, wherein said fine oxide particles have a relative particle size standard deviation of 1.0 to 1.3.
Claim 5
Dependent Claim
22 words
The method of claim 1, wherein said inorganic oxide is composed mainly of silica, titania, alumina, zirconia or a composite oxide thereof.
Claim 6
Dependent Claim
18 words
The method of claim 1, wherein said glycol has 2 to 8 carbon atoms and 2 hydroxy groups.
Claim 7
Dependent Claim
11 words
The method of claim 5, wherein said glycol is ethylene glycol.
Claim 8
Dependent Claim
116 words
The method of claim 1, wherein said monodispersed suspension is prepared by a process which comprises at least the following three steps: (1) a first step of hydrolyzing a hydrolyzable organometallic compound in an aqueous solution of an alcohol, and, optionally, a glycol to be used in a second step, to obtain a suspension of fine particles of an amorphous hydrated inorganic oxide in said alcoholic solution, (2) a second step of substituting a glycol for said alcoholic solvent of the suspension to obtain a glycol suspension of the fine particles of hydrated inorganic oxide, and (3) a third step of heat-treating the glycol suspension to obtain a monodispersed glycol suspension of fine inorganic oxide particles.
Claim 9
Dependent Claim
23 words
The method of claim 7, wherein the said inorganic oxide is composed mainly of silica, titania, alumina, zirconia or a composite oxide thereof.
Claim 10
Dependent Claim
17 words
The method of claim 7, wherein the glycol has 2to 8 carbon atoms and 2 hydroxy groups.
Claim 11
Dependent Claim
11 words
The method of claim 9, wherein said glycol is ethylene glycol.
Claim 12
Dependent Claim
112 words
The method of claim 7, wherein said organometallic compound is a metal alkoxide of the formula M(OR) m wherein M is a metallic element, m is an integer corresponding to the valency of the element and R is an alkyl group having up to 8 carbon atoms; a low condensation product obtained by partially hydrolyzing a metal alkoxide of said formula M(OR) m ; a substituted alkoxide obtained by partially replacing the OR moieties of said metal alkoxide of said formula M(OR) m by a moiety capable of carboxyl compounds and beta-dicarbonyl group consisting of carboxyl compounds and beta-dicarbonyl compounds; or a low condensation product obtained by partially hydrolyzing said substituted alkoxide.
Claim 13
Dependent Claim
45 words
The method of claim 7, wherein, in said first step, an alcohol having a lower boiling point than the glycol is used, and, in the second step, the alcoholic solvent is distilled from the suspension in the alcoholic solution in the presence of the glycol.
Claim 14
Dependent Claim
42 words
The method of claim 7, wherein the heat treatment temperature T (° C.) in said third step is 70≦T≦TB+10 wherein TB represents the boiling point (° C.) of the glycol under the pressure at which the heat-treatment is carried out, and TB≧70.
Claim 15
Dependent Claim
32 words
The method of claim 7, wherein a coupling agent is added to the resulting suspension in the alcoholic solution, after the first step, to subject the fine particles to a coupling treatment.
Claim 16
Dependent Claim
25 words
The method of claim 14, wherein said coupling agent is at least one coupling agent selected from the group consisting of silanes, titanates and aluminates.
References Cited (Backward Citations)
US2765242A
Cited
US2739076A
Cited
US2657149A
Cited
US2882177A
Cited
US2833723A
Cited
US2921913A
Cited
US3227657A
Cited
US3699049A
Cited
US3803046A
Cited
US3884870A
Cited
JPS523645A
Cited
JPS5647429A
Cited
JPS57196717A
Cited
JPS62207356A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-30 | 1997-11-29 | 1998-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-30 | 2001-11-29 | 2002-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-30 | 2005-11-29 | 2006-05-31 | $7700.00 | Window Closed / Lapsed |