Claim 1

Independent Claim 90 words

An aluminum nitride sintered body produced by baking an aluminum nitride starting powder with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, said aluminum nitride starting powder being derived by direct nitriding of metallic aluminum and having an oxygen content of not greater than 1.8% by weight and a Si content of not greater than 0.2% by weight, and said aluminum nitride sintered body having a thermal conductivity of at least 100 W/mK and a relative density of at least 95%.

Claim 2

Dependent Claim 90 words

An aluminum nitride sintered body produced by baking an aluminum nitride starting powder with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, said aluminum nitride starting powder being derived by direct nitriding of metallic aluminum and having an oxygen content of not greater than 1.8% by weight and a Si content of not greater than 0.2% by weight, and said aluminum nitride sintered body having a thermal conductivity of at least 100 W/mK and a relative density of at least 95%.

Claim 3

Dependent Claim 18 words

An aluminum nitride sintered body according to claim 1, wherein the thermal conductivity is at least 120 W/mK.

Claim 4

Dependent Claim 54 words

An aluminum nitride sintered body according to claim 1, wherein the sintering additive comprises predominantly Y 2 O 3 or a precursor thereof whereby the sintered body consists of AlN grain phases and yttrium-containing grain boundary phases in which yttrium comprises a major proportion of the metallic elements present in the grain boundary phases.

Claim 5

Dependent Claim 99 words

An aluminum nitride sintered body according to claim 3, wherein the plot of the Y 2 O 3 -converted yttrium content in weight percent of the sintered body versus the residual oxygen content in weight percent thereof calculated by subtracting the amount of oxygen contained in the Y 2 O 3 -converted yttrium content from the total oxygen content of the sintered body is located within the region defined by lines Q-R-S-T-Q in FIG. 1 (excluding the cases where the plot is on one of the lines), said sintered body having a thermal conductivity of at least 100 W/mK.

Claim 6

Dependent Claim 110 words

An aluminum nitride sintered body according to claim 3, wherein the plot of the Y 2 O 3 -converted yttrium content in weight percent of the sintered body versus the residual oxygen content in weight percent thereof calculated by subtracting the amount of oxygen contained in the Y 2 O 3 -converted yttrium content from the total oxygen content of the sintered body is located within the region defined by lines A-B-C-D-E-F-G-H-A in FIG. 1 (including the cases where the plot is on one of the lines but excluding the case where the plot is on point C), said sintered body having a thermal conductivity of at least 120 W/mK.

Claim 7

Dependent Claim 99 words

An aluminum nitride sintered body according to claim 3, wherein the plot of the Y 2 O 3 -converted yttrium content in weight percent of the sintered body versus the residual oxygen content in weight percent thereof calculated by subtracting the amount of oxygen contained in the Y 2 O 3 -converted yttrium content from the total oxygen content of the sintered body is located within the region defined by lines I-J-K-N-I in FIG. 1 (including the cases where the plot is on one of the lines), said sintered body having a thermal conductivity of at least 140 W/mK.

Claim 8

Dependent Claim 99 words

An aluminum nitride sintered body according to claim 3, wherein the plot of the Y 2 O 3 -converted yttrium content in weight percent of the sintered body versus the residual oxygen content in weight percent thereof calculated by subtracting the amount of oxygen contained in the Y 2 O 3 -converted yttrium content from the total oxygen content of the sintered body is located within the region defined by lines O-P-L-M-O in FIG. 1 (including the cases where the plot is on one of the lines), said sintered body having a thermal conductivity of at least 160 W/mK.

Claim 9

Dependent Claim 133 words

An aluminum nitride sintered body according to claim 3, wherein the weight ratio of the Al 2 O 3 -converted residual oxygen content expressed in weight percent as Al 2 O 3 to the Y 2 O 3 -converted yttrium content [Al 2 O 3 /Y 2 O 3 ] in the sintered body, and the values of the Al 2 O 3 -converted residual oxygen content [Al 2 O 3 ] and the Y 2 O 3 -converted yttrium content [Y 2 O 3 ] therein meet the following requirements: 0.2≦[Al.sub.2 O.sub.3 /Y.sub.2 O.sub.3 ]≦2.4, 1.1≦[Al.sub.2 O.sub.3 ]≦12.0 (in weight percent), and 2.0<[Y.sub.2 O.sub.3 ]<12.0 (in weight percent), said sintered body having a thermal conductivity of at least 100 W/mK and a three-point bending strength of at least 30 kg/mm 2 .

Claim 10

Dependent Claim 83 words

An aluminum nitride sintered body according to claim 8, wherein the weight ratio [Al 2 O 3 /Y 2 O 3 ] and the values of [Al 2 O 3 ] and [Y 2 O 3 ] meet the following requirements: 0.2≦[Al.sub.2 O.sub.3 /Y.sub.2 O.sub.3 ]≦1.7, 1.1≦[Al.sub.2 O.sub.3 ]≦11.0 (in weight percent), and 3.9≦[Y.sub.2 O.sub.3 ]≦9.0 (in weight percent), said sintered body having a thermal conductivity of at least 120 W/mK and a three-point bending strength of at least 35 kg/mm 2 .

Claim 11

Dependent Claim 83 words

An aluminum nitride sintered body according to claim 8, wherein the weight ratio [Al 2 O 3 /Y 2 O 3 ] and the values of [Al 2 O 3 ] and [Y 2 O 3 ] meet the following requirements: 0.6≦[Al.sub.2 O.sub.3 /Y.sub.2 O.sub.3 ]≦1.4, 3.2≦[Al.sub.2 O.sub.3 ]≦7.0 (in weight percent), and 3.9≦[Y.sub.2 O.sub.3 ]≦7.0 (in weight percent), said sintered body having a thermal conductivity of at least 140 W/mK and a three-point bending strength of at least 40 kg/mm 2 .

Claim 12

Dependent Claim 83 words

An aluminum nitride sintered body according to claim 8, wherein the weight ratio [Al 2 O 3 /Y 2 O 3 ] and the values of [Al 2 O 3 ] and [Y 2 O 3 ] meet the following requirements: 0.6≦[Al.sub.2 O.sub.3 /Y.sub.2 O.sub.3 ]≦1.2, 3.2≦[Al.sub.2 O.sub.3 ]≦6.0 (in weight percent), and 4.5≦[Y.sub.2 O.sub.3 ]≦6.0 (in weight percent), said sintered body having a thermal conductivity of at least 160 W/mK and a three-point bending strength of at least 40 kg/mm 2 .

Claim 13

Dependent Claim 63 words

An aluminum nitride sintered body according to claim 3, wherein the weight ratio of the Si content to the Y content [Si/Y] in the sintered body and the Si content [Si] and the Y content [Y] therein meet the following requirements: [Si/Y]≦1.32, [Si]≦1.3 (in weight percent), and 1.6<[Y]<9.4 (in weight percent), said sintered body having a thermal conductivity of at least 100 W/mK.

Claim 14

Dependent Claim 50 words

An aluminum nitride sintered body according to claim 12, wherein the weight ratio [Si/Y] in the sintered body and the values of [Si] and [Y] meet the following requirements: [Si/Y]≦0.21, [Si]≦0.9≦(in weight percent), and 3.1≦[Y]≦7.1 (in weight percent), said sintered body having a thermal conductivity of at least 120 W/mK.

Claim 15

Dependent Claim 51 words

An aluminum nitride sintered body according to claim 12, wherein the weight ratio [Si/Y] in the sintered body and the values of [Si] and [Y] meet the following requirements: [Si/Y]≦0.12, [Si]≦0.5 (in weight percent), and 3.1≦[Y]5.5 (in weight percent), said sintered body having a thermal conductivity of at least 140 W/mK.

Claim 16

Dependent Claim 51 words

An aluminum nitride sintered body according to claim 12, wherein the weight ratio [Si/Y] in the sintered body and the values of [Si] and [Y] meet the following requirements: [Si/Y]≦0.05, [Si]≦0.2 (in weight percent), and 3.5≦[Y]≦4.7 (in weight percent), said sintered body having a thermal conductivity of at least 160 W/mK.

Claim 17

Dependent Claim 65 words

An aluminum nitride sintered body according to claim 3, wherein the metallic composition of the grain boundary phases in the sintered body comprises 60%-91% by weight of Y, 8%-35% by weight of Al, and not greater than 10% by weight of Si based on the total metallic content in the grain boundary phases, said sintered body having a thermal conductivity of at least 140 W/mK.

Claim 18

Dependent Claim 65 words

An aluminum nitride sintered body according to claim 3, wherein the metallic composition of the grain boundary phases in the sintered body comprises 70%-91% by weight of Y, 8%-25% by weight of Al, and not greater than 3% by weight of Si based on the total metallic content in the grain boundary phases, said sintered body having a thermal conductivity of at least 160 W/mK.

Claim 19

Dependent Claim 149 words

An aluminum nitride sintered body according to claim 5, wherein the weight ratio of the Al 2 O 3 -converted residual oxygen content that is the residual oxygen content expressed in weight percent as Al 2 O 3 to the Y 2 O 3 -converted yttrium content [Al 2 O 3 /Y 2 O 3 ] in the sintered body, and the Al 2 O 3 -converted residual oxygen content [Al 2 O 3 ] meet the following requirements: 0.2≦[Al.sub.2 O.sub.3 /Y.sub.2 O.sub.3 ]≦1.7, and 1.1≦[Al.sub.2 O.sub.3 ]≦11.0 (in weight percent), and wherein the weight ratio of the Si content to the Y content [Si/Y] in the sintered body and the Si content [Si] therein meet the following requirements: [Si/Y]≦0.21, and [Si]≦0.9 (in weight percent), said sintered body having a thermal conductivity of at least 120 W/mK and a three-point bending strength of at least 35 kg/mm 2 .

Claim 20

Dependent Claim 125 words

A process for producing an aluminum nitride sintered body having a thermal conductivity of at least 100 W/mK and a relative density of at least 95%, comprising mixing a minor amount of a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table with an aluminum nitride starting powder prepared by direct nitriding of metallic aluminum and having a purity of at least 99%, an oxygen content of lower than 1.8% by weight and an Si content of not greater than 0.2% by weight to form a powder mixture, shaping the powder mixture, and baking the shaped mixture at a temperature in the range of 1500°-2100° C. in a non-oxidizing atmosphere for a time sufficient to sinter the mixture.

Claim 21

Dependent Claim 125 words

A process for producing an aluminum nitride sintered body having a thermal conductivity of at least 100 W/mK and a relative density of at least 95%, comprising mixing a minor amount of a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table with an aluminum nitride starting powder prepared by direct nitriding of metallic aluminum and having a purity of at least 99%, an oxygen content of lower than 1.8% by weight and an Si content of not greater than 0.2% by weight to form a powder mixture, shaping the powder mixture, and baking the shaped mixture at a temperature in the range of 1500°-2100° C. in a non-oxidizing atmosphere for a time sufficient to sinter the mixture.

Claim 22

Dependent Claim 30 words

A process according to claim 19, wherein any pulverization of the starting powder or the powder mixture or both is conducted in a non-oxidizing atmosphere or in an organic solvent.

Claim 23

Dependent Claim 33 words

A process according to claim 19, wherein the powder mixture has an average particle diameter of not greater than 2.5 μm and an oxygen content of not greater than about 6% by weight.

Claim 24

Dependent Claim 60 words

A process according to claim 19, wherein the sintering additive comprises predominantly Y 2 O 3 or a precursor thereof and is used in such an amount that the powder mixture contains yttrium in an amount of from about 2% to about 12% by weight calculated as Y 2 O 3 based on the total weight of the powder mixture.

Claim 25

Dependent Claim 57 words

A process according to claim 22, wherein the residual oxygen content calculated by subtracting the amount of oxygen which will combine with the yttrium content in the powder mixture in the form of Y 2 O 3 from the total oxygen content of the powder mixture is in the range of from 0.38% to 6.69% by weight.

Claim 26

Dependent Claim 71 words

A process according to claim 22, wherein the residual oxygen content calculated by subtracting the amount of oxygen which will combine with the yttrium content in the powder mixture in the form of Y 2 O 3 from the total oxygen content of the powder mixture is in the range of from 0.38% to 4.92% by weight, and wherein the sintered body has a thermal conductivity of at least 120 W/mK.

Claim 27

Dependent Claim 71 words

A process according to claim 22, wherein the residual oxygen content calculated by subtracting the amount of oxygen which will combine with the yttrium content in the powder mixture in the form of Y 2 O 3 from the total oxygen content of the powder mixture is in the range of from 1.28% to 3.67% by weight, and wherein the sintered body has a thermal conductivity of at least 140 W/mK.

Claim 28

Dependent Claim 71 words

A process according to claim 22, wherein the residual oxygen content calculated by subtracting the amount of oxygen which will combine with the yttrium content in the powder mixture in the form of Y 2 O 3 from the total oxygen content of the powder mixture is in the range of from 1.41% to 3.15% by weight, and wherein the sintered body has a thermal conductivity of at least 160 W/mK.

Claim 29

Dependent Claim 68 words

A process according to claim 22, wherein the powder mixture contains yttrium in an amount of not greater than 3% by weight calculated as Y 2 O 3 and further contains Al 2 O 3 which is added in such an amount that the powder mixture contains not greater than 2% by weight of Al 2 O 3 , said aluminum nitride sintered body having improved bending strength.

Claim 30

Dependent Claim 72 words

A process according to claim 27, wherein the powder mixture contains yttrium in an amount of greater than 3% and not greater than 9% by weight calculated as Y 2 O 3 and further contains Al 2 O 3 which is added in such an amount that the powder mixture contains not greater than 5% by weight of Al 2 O 3 , said aluminum nitride sintered body having improved bending strength.

Claim 31

Dependent Claim 71 words

A process according to claim 22, wherein the powder mixture contains yttrium in an amount of greater than 9% and lower than 12% by weight calculated as Y 2 O 3 and further contains Al 2 O 3 which is added in such an amount that the powder mixture contains not greater than 7% by weight of Al 2 O 3 , said aluminum nitride sintered body having improved bending strength.

Claim 32

Dependent Claim 84 words

A process according to claim 19, wherein at least one binder selected from butyral polymers and acrylate polymers, an organic solvent, and optionally a plasticizer are added to the powder mixture to form a slurry comprising the powder mixture, the slurry is shaped into a sheet, and subsequent to drying and binder removal, the resulting green sheet is baked at a temperature of 1750°-1950° C. in a non-oxidizing atmosphere by a technique selected from pressureless sintering, gas-pressure sintering, hot isostatic pressing, and combinations thereof.

Claim 33

Dependent Claim 65 words

A process according to claim 30, wherein the aluminum nitride starting powder has a particle size distribution in which from 22% to 45% by volume of the powder is made up of particles having a diameter equal to or larger than 3 μm and from 55% to 78% by volume of the powder is made up of particles having a diameter smaller than 3 μm.

Claim 34

Dependent Claim 27 words

A process according to claim 19, wherein the baking of the shaped powder mixture is conducted by means of pressureless sintering at a temperature of 1750°-1950° C.

Claim 35

Dependent Claim 27 words

A process according to claim 19, wherein the baking of the shaped powder mixture is conducted by means of hot pressing at a temperature of 1600°-1800° C.

Claim 36

Dependent Claim 27 words

A process according to claim 19, wherein the baking of the shaped powder mixture is conducted by means of gas-pressure sintering at a temperature of 1880°-1970° C.

Claim 37

Dependent Claim 28 words

A process according to claim 19, wherein the baking of the shaped powder mixture is conducted by means of hot isostatic pressing at a temperature of 1500°-2000° c.

Claim 38

Independent Claim 162 words

A method of making an aluminum nitride-based green sheet having improved green strength, which comprises mixing an aluminum nitride starting powder derived by direct nitriding of metallic aluminum and having a purity of at least 99%, an oxygen content of lower than 1.8% by weight and an Si content of not greater than 0.7% by weight with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, an organic polymeric binder, and optionally a plasticizer in an organic solvent to form a slurry, and shaping the slurry into a sheet followed by drying of the sheet, wherein the aluminum nitride starting powder has a particle size distribution in which from 22% to 45% by volume of the powder is made up of particles having a diameter equal to or larger than 3 μm and from 55% to 78% by volume of the powder is made up of particles having a diameter smaller than 3 μm.

Claim 39

Independent Claim 162 words

A method of making an aluminum nitride-based green sheet having improved green strength, which comprises mixing an aluminum nitride starting powder derived by direct nitriding of metallic aluminum and having a purity of at least 99%, an oxygen content of lower than 1.8% by weight and an Si content of not greater than 0.7% by weight with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, an organic polymeric binder, and optionally a plasticizer in an organic solvent to form a slurry, and shaping the slurry into a sheet followed by drying of the sheet, wherein the aluminum nitride starting powder has a particle size distribution in which from 22% to 45% by volume of the powder is made up of particles having a diameter equal to or larger than 3 μm and from 55% to 78% by volume of the powder is made up of particles having a diameter smaller than 3 μm.

Claim 40

Dependent Claim 62 words

A method according to claim 36, wherein the sintering additive comprises predominantly Y 2 O 3 or a precursor thereof and is used in such an amount that yttrium is present in a concentration of from about 2% to about 12% by weight calculated as Y 2 O 3 based on the total weight of the starting powder and the sintering additive.

Claim 41

Dependent Claim 17 words

A method according to claim 36, wherein the organic polymeric binder is a butyral or acrylate polymer.

Claim 42

Dependent Claim 13 words

A method according to claim 38, wherein the organic polymeric binder is polyvinylbutyral.

Claim 43

Dependent Claim 20 words

A method according to claim 38, wherein the organic polymeric binder is a copolymer comprising methyl methacrylate and ethyl acrylate.

Claim 44

Dependent Claim 11 words

A green sheet produced by a method according to claim 36.

Claim 45

Dependent Claim 11 words

A green sheet produced by a method according to claim 37.

Claim 46

Dependent Claim 18 words

An aluminum nitride sintered body according to claim 1, wherein the thermal conductivity is at least 140 W/mK.

Claim 47

Dependent Claim 18 words

An aluminum nitride sintered body according to claim 1, wherein the thermal conductivity is at least 160 W/mK.

Claim 48

Dependent Claim 22 words

A process according to claim 19, wherein said powder mixture consists essentially of said sintering additive and said aluminum nitride starting powder.

Claim 49

Dependent Claim 21 words

A process according to claim 19, wherein said powder mixture consists of said sintering additive and said aluminum nitride starting powder.

Claim 50

Dependent Claim 78 words

An aluminum nitride sintered body produced by baking an aluminum nitride starting powder having an average particle size of not more than 5 μm with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, said aluminum nitride starting powder being derived by direct nitriding of metallic aluminum and having an oxygen content of not greater than 1.8% by weight and an Si content of not greater than 0.2% by weight.

Claim 51

Dependent Claim 78 words

An aluminum nitride sintered body produced by baking an aluminum nitride starting powder having an average particle size of not more than 5 μm with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, said aluminum nitride starting powder being derived by direct nitriding of metallic aluminum and having an oxygen content of not greater than 1.8% by weight and an Si content of not greater than 0.2% by weight.

Claim 52

Dependent Claim 80 words

An aluminum nitride sintered body produced by baking an aluminum nitride starting power having an average particle size within a range of 1 to 3 μm with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, said aluminum nitride starting powder being derived by direct nitriding of metallic aluminum and having an oxygen content of not greater than 1.8% by weight and an Si content of not greater than 0.2% by weight.

Claim 53

Dependent Claim 80 words

An aluminum nitride sintered body produced by baking an aluminum nitride starting power having an average particle size within a range of 1 to 3 μm with a sintering additive selected from compounds of Group IIa, IIIa, and IIIb metals of the periodic table, said aluminum nitride starting powder being derived by direct nitriding of metallic aluminum and having an oxygen content of not greater than 1.8% by weight and an Si content of not greater than 0.2% by weight.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1997-05-23	1997-11-22	1998-05-24	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	2001-05-23	2001-11-22	2002-05-24	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2005-05-23	2005-11-22	2006-05-24	$7700.00	Window Closed / Lapsed

Aluminum nitride sintered body and production thereof

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag