Polyethylene terephthalate film for magnetic recording medium containing three different kinds of particles
Assignee: Mitsubishi Chemical Corp
•
Filing: 1992-02-21
•
Granted: 1994-05-24
•
Expires: 2012-02-21
Abstract
Abstract Disclosed herein is a polyethylene terephthalate film for magnetic recording medium, which contains 0.1 to 1.0% by weight based on the film of aggregated silicon oxide particles having an average particle size of 0.03 to 0.2 μm, primary particle of which having an average particle size of 0.005 to 0.05 μm, 0.1 to 1.0% by weight based on the film of aggregated aluminium oxide particles having an average particle size of 0.03 to 0.2 μm, primary particle of which having an average particle size of 0.005 to 0.05 μm and 0.005 to 0.3% by weight based on the film of a crosslinked polymer having an average particle size of 0.2 to 0.8 μm, said film having a center line average surface roughness of 0.003 to 0.015 μm and a sum of F-5 values in both the machine direction and the transverse direction of at least 25.0 kg/mm 2 . The film has a flat surface and is excellent in slipperiness, abrasion resistance, scratch resistance and protuberance resistance, which can be used as a base film for high-density magnetic recording medium.
Inventors
- 👤 Chikakazu Kawaguchi
- 👤 Yoshio Meguro
- 👤 Takashi Harada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:34
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; G; G11; G11B; G11B5/00; G11B5/62; G11B5/73; G11B5/739; G11B5/73923; G11B5/73927; G11B5/73935; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24372; Y10T428/25; Y10T428/254; Y10T428/256; Y10T428/257; Y10T428/259; Y10T428/31504; Y10T428/31786; Y10T428/31794
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
148 words
A polyethylene terephthalate film for magnetic recording medium, which contains 0.1 to 1.0% by weight based on the film of aggregated silicon oxide particles having an average particle size of 0.03 to 0.2 μm, the primary particle of which has an average particle size of 0.005 to 0.05 μm, 0.1 to 1.0% by weight based on the film of aggregated aluminium oxide particles having an average particle size of 0.03 to 0.2 μm, the primary particle of which has an average particle size of 0.005 to 0.05 μm, and 0.005 to 0.3% by weight based on the film of a crosslinked polymer having an average particle size of 0.2 to 0.8 μm, said film having a center line average surface roughness of 0.003 to 0.015 μm and a sum of F-5 values in both the machine direction and the transverse direction of at least 25.0 kg/mm 2 .
Claim 2
Dependent Claim
148 words
A polyethylene terephthalate film for magnetic recording medium, which contains 0.1 to 1.0% by weight based on the film of aggregated silicon oxide particles having an average particle size of 0.03 to 0.2 μm, the primary particle of which has an average particle size of 0.005 to 0.05 μm, 0.1 to 1.0% by weight based on the film of aggregated aluminium oxide particles having an average particle size of 0.03 to 0.2 μm, the primary particle of which has an average particle size of 0.005 to 0.05 μm, and 0.005 to 0.3% by weight based on the film of a crosslinked polymer having an average particle size of 0.2 to 0.8 μm, said film having a center line average surface roughness of 0.003 to 0.015 μm and a sum of F-5 values in both the machine direction and the transverse direction of at least 25.0 kg/mm 2 .
Claim 3
Dependent Claim
22 words
A film according to claim 1, wherein the silicon oxide particles are contained in an amount of 0.2 to 0.5% by weight.
Claim 4
Dependent Claim
22 words
A film according to claim 1, wherein the aluminium oxide particles are contained in an amount of 0.2 to 0.5% by weight.
Claim 5
Dependent Claim
16 words
A film according to claim 1, wherein the crosslinked polymer particles have a substantially spherical shape.
Claim 6
Dependent Claim
26 words
A film according to claim 1, wherein the crosslinked polymer particles are particles of a polymer having a glass transition temperature of 110° C. or less.
Claim 7
Dependent Claim
20 words
The film of claim 1 in which the crosslinked polymer has an average particle size of 0.5 to 0.8 μm.
Claim 8
Dependent Claim
20 words
The film of claim 1 in which the crosslinked polymer has an average particle size of 0.6 to 0.8 μm.
Claim 9
Dependent Claim
22 words
The film of claim 1 in which the aggregated aluminum oxide particles have an average particle size of 0.03 to 0.10 μm.
Claim 10
Dependent Claim
22 words
The film of claim 1 in which the aggregated aluminum oxide particles have an average particle size of 0.03 to 0.08 μm.
Claim 11
Dependent Claim
22 words
The film of claim 1 in which the aggregated silicon oxide particles have an average particle size of 0.03 to 0.12 μm.
References Cited (Backward Citations)
US4767657A
Cited
US4568616A
Cited
US4639389A
Cited
US4720412A
Cited
US4865898A
Cited
US4818581A
Cited
EP0345644A2
Cited
EP0378154A1
Cited
US5085915A
Cited
US5096773A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-23 | 1997-11-22 | 1998-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-23 | 2001-11-22 | 2002-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-23 | 2005-11-22 | 2006-05-24 | $7700.00 | Window Closed / Lapsed |