Abstract
Abstract Controlled porosity composite sheets comprising a melt-blown polypropylene fiber web having a spunbonded polypropylene fiber sheet laminated to at least one side thereof are made by calendering an assembly of the component webs in such a manner that, when a two-layer composite sheet is made, the web of melt-blown fibers is in contact with a metal roll heated to 140°-170° C. operating against an unheated resilient roll; and, when a three-layer composite sheet is made, the spunbonded web in contact with the heated metal roll has a dtex per fiber value of less than 6. These composite sheets have a Gurley-Hill porosity of about 5-75 seconds, excellent mechanical and tear strengths, high water vapor penetration rate, and low liquid water permeability. They are particularly suitable for making housewrap sheets and sheets for sterile packaging. In the sterile packaging field, they are significantly better than medical paper used for the same purpose.
Inventors
- 👤 Hyun S. Lim
- 👤 Hyunkook Shin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 02:59
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B37/00; B32B37/06; B32B5/02; B32B5/024; D; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/559; D04H1/56; D04H13/00; B32B2262/00; B32B2262/02; B32B2262/0253; B32B2307/00; B32B2307/50; B32B2307/582; B32B2307/5825; B32B2307/70; B32B2307/714; B32B2307/7145; B32B2307/724; B32B2307/726; B32B2307/7265; B32B2439/00; B32B2439/80; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T442/00; Y10T442/60; Y10T442/608; Y10T442/614; Y10T442/62; Y10T442/659; Y10T442/66
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
166 words
A high-strength, tear-resistant, calendered, composite sheet having an opacity, as determined by TAPPI test T-519 om-86, of at least 75%, having low air permeability expressed as Gurley-Hill porosity of 5-75 seconds, high water vapor transmission rate of at least 500 g/m 2 in 24 hours according to ASTM standard E96, method B, low liquid water permeability expressed by a hydrostatic head pressure of at least 0.75 m according to AATCC standard 127-1985, and barrier properties against bacteria that are significantly better than those of medical paper used for sterile packaging, which sheet comprises one melt-blown polypropylene fiber web and a spunbonded polypropylene fiber sheet laminated to at least one side thereof, the melt-blown fibers having an average diameter of 1-10 μm, the melt-blown fiber web itself having an average weight of about 17-40.7 g/m 2 , and the fibers of the spunbonded sheet having an average diameter of at least 20 μm, the spunbonded sheet itself having an average weight of about 17-100 g/m 2 .
Claim 2
Dependent Claim
166 words
A high-strength, tear-resistant, calendered, composite sheet having an opacity, as determined by TAPPI test T-519 om-86, of at least 75%, having low air permeability expressed as Gurley-Hill porosity of 5-75 seconds, high water vapor transmission rate of at least 500 g/m 2 in 24 hours according to ASTM standard E96, method B, low liquid water permeability expressed by a hydrostatic head pressure of at least 0.75 m according to AATCC standard 127-1985, and barrier properties against bacteria that are significantly better than those of medical paper used for sterile packaging, which sheet comprises one melt-blown polypropylene fiber web and a spunbonded polypropylene fiber sheet laminated to at least one side thereof, the melt-blown fibers having an average diameter of 1-10 μm, the melt-blown fiber web itself having an average weight of about 17-40.7 g/m 2 , and the fibers of the spunbonded sheet having an average diameter of at least 20 μm, the spunbonded sheet itself having an average weight of about 17-100 g/m 2 .
Claim 3
Dependent Claim
18 words
A composite sheet of claim 1 for use as a housewrap, which has a Gurley-Hill porosity 30-75 seconds.
Claim 4
Dependent Claim
43 words
A composite sheet of claim 2 which has a water vapor transmission rate according to ASTM E96, method B of at least 500 g/m 2 in 24 hours and a liquid water permeability expressed as hydrostatic head pressure of at least 0.9 m.
Claim 5
Dependent Claim
44 words
A composite sheet of claim 1 for use in sterile packaging, which has a Gurley-Hill porosity of 5-50 seconds, which under standardized bacterial test chamber conditions provides an effective barrier to bacteria such that at least 60% of test samples show no bacteria present.
Claim 6
Dependent Claim
13 words
A composite sheet of claim 1 wherein the melt-blown web is electrostatically charged.
Claim 7
Dependent Claim
13 words
A composite sheet of claim 4 wherein the melt-blown web is electrostatically charged.
Claim 8
Dependent Claim
24 words
A two-layer composite sheet of claim 1 wherein the fibers of the spunbonded sheet have a dtex per filament value of at least 10.
Claim 9
Dependent Claim
26 words
A three-layer composite sheet of claim 1 wherein at least one of the spunbonded layers is made of fibers of less than 6 dtex per filament.
Claim 10
Dependent Claim
11 words
A microfiltration element made of a composite sheet of claim 1.
Claim 11
Dependent Claim
180 words
A process for forming a composite sheet by calendering an assembly consisting of a melt-blown polypropylene fiber web and a spunbonded polypropylene fiber sheet laminated to at least one side thereof, the melt-blown fibers having an average diameter of 1-10 μm, the melt-blown fiber web itself having an average weight of about 17-40.7 g/m 2 , and the fibers of the spunbonded sheet having an average diameter of at least 20 μm, the spunbonded sheet itself having an average weight of about 17-100 g/m 2 , in a calender comprising a smooth metal roll heated to a temperature of 140°-170° C., operating against an unheated, resilient roll having a Shore D hardness of 75-85, at a nip loading of about 1.75×10 -5 -3.5×10 -5 N/m; with the proviso that when forming a two-layer composite sheet, only the melt-blown fiber web is in direct contact with the heated metal roll; and when forming a three-layer composite sheet, the spunbonded sheet in contact with the heated metal roll is made of filaments having a dtex-per- filament (DTPF) value of less than 6.
Claim 12
Dependent Claim
180 words
A process for forming a composite sheet by calendering an assembly consisting of a melt-blown polypropylene fiber web and a spunbonded polypropylene fiber sheet laminated to at least one side thereof, the melt-blown fibers having an average diameter of 1-10 μm, the melt-blown fiber web itself having an average weight of about 17-40.7 g/m 2 , and the fibers of the spunbonded sheet having an average diameter of at least 20 μm, the spunbonded sheet itself having an average weight of about 17-100 g/m 2 , in a calender comprising a smooth metal roll heated to a temperature of 140°-170° C., operating against an unheated, resilient roll having a Shore D hardness of 75-85, at a nip loading of about 1.75×10 -5 -3.5×10 -5 N/m; with the proviso that when forming a two-layer composite sheet, only the melt-blown fiber web is in direct contact with the heated metal roll; and when forming a three-layer composite sheet, the spunbonded sheet in contact with the heated metal roll is made of filaments having a dtex-per- filament (DTPF) value of less than 6.
Claim 13
Dependent Claim
37 words
A process of claim 7 wherein a two-layer composite sheet is made, and the melt-blown fibers of the web in contact with the heated metal roll have a dtex per fiber value of at least about 10.
Claim 14
Dependent Claim
16 words
A process of claim 7 wherein the temperature of the heated metal roll is 140°-150° C.
Claim 15
Dependent Claim
36 words
A process of claim 7 wherein the layer in contact with the heated metal roll is preheated, prior to such contact, to a temperature of about 20° C. below the temperature of the heated metal roll.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-02 | 1997-11-01 | 1998-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-02 | 2001-11-01 | 2002-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-02 | 2005-11-01 | 2006-05-03 | $7700.00 | Window Closed / Lapsed |