Consolidated member and method and preform for making
Assignee: General Electric Co
•
Filing: 1992-04-06
•
Granted: 1994-04-26
•
Expires: 2012-04-06
Abstract
Abstract A method of making a consolidated, reinforced composite member from a matrix mixture including a consolidation shrinkable discontinuous ceramic material, for example ceramic particles, and a selected amount of a particulate inorganic filler which will exhibit net expansion relative to the discontinuous material, the mixture being interspersed about reinforcing fibers. Subsequent consolidation of a preform of such materials can be conducted substantially at ambient pressure, without application of additional pressure, to provide an improved reinforced composite article.
Inventors
- 👤 Michael G. Harrison
- 👤 Michael L. Millard
- 👤 Andrew Szweda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:44
CPC Classifications
F; F01; F01D; F01D5/00; F01D5/12; F01D5/28; F01D5/284; B; B32; B32B; B32B18/00; C; C04; C04B; C04B33/00; C04B33/36; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/622; C04B35/626; C04B35/62605; C04B35/62625; C04B35/6263; C04B35/6264; C04B35/63; C04B35/6303; C04B35/6316; C04B35/632; C04B35/634; C04B35/63404; C04B35/6342; C04B35/63424; C04B35/63448; C04B35/63452; C04B35/6346; C04B35/63488; C04B35/636; C04B35/6365; C04B35/71; C04B35/78; C04B35/80; F01D5/282; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/34; C04B2235/349; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/522; C04B2235/5224; C04B2235/5228; C04B2235/524; C04B2235/5244; C04B2235/5248; C04B2235/5276; C04B2235/65; C04B2235/656; C04B2235/66; C04B2235/668; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/343; C04B2237/345; C04B2237/348; C04B2237/38; C04B35/6306; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/249928; Y10T428/24994; Y10T428/24995; Y10T428/25; Y10T428/251; Y10T428/259
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
228 words
In a method of making a consolidated, reinforced composite member comprising a matrix mixture having reduced tensile stresses and reinforcing fibers, the matrix mixture including a solvent, a plasticizer, a binder, a discontinuous ceramic material and a particulate inorganic filler having a lathy-type crystal shape, the steps of: providing the matrix mixture including a preselected amount of the discontinuous material which will consolidate, producing shrinkage and associated stresses when sintered, a preselected amount of the particulate inorganic filler which will exhibit net expansion when heated to counteract the stresses in the matrix mixture caused by shrinkage of the discontinuous material during sintering; providing a plurality of reinforcing fibers; interspersing the matrix mixture about the reinforcing fibers; laminating the matrix mixture and fibers into an article perform under a preselected pressure at a first temperature in the temperature range of 150°-400° F.; heating the article preform to a second temperature above the first temperature and below a preselected sintering temperature to remove at least the solvent and the binder from the matrix mixture; sintering the article preform at the preselected sintering temperature at ambient pressure at which the discontinuous material, in a substantially solid phase, consolidates to produce a substantially continuous matrix while the inorganic filler simultaneously expands to counteract stresses from consolidated of the discontinuous material so as to form a fiber-reinforced composite matrix with reduced tensile stresses.
Claim 2
Dependent Claim
228 words
In a method of making a consolidated, reinforced composite member comprising a matrix mixture having reduced tensile stresses and reinforcing fibers, the matrix mixture including a solvent, a plasticizer, a binder, a discontinuous ceramic material and a particulate inorganic filler having a lathy-type crystal shape, the steps of: providing the matrix mixture including a preselected amount of the discontinuous material which will consolidate, producing shrinkage and associated stresses when sintered, a preselected amount of the particulate inorganic filler which will exhibit net expansion when heated to counteract the stresses in the matrix mixture caused by shrinkage of the discontinuous material during sintering; providing a plurality of reinforcing fibers; interspersing the matrix mixture about the reinforcing fibers; laminating the matrix mixture and fibers into an article perform under a preselected pressure at a first temperature in the temperature range of 150°-400° F.; heating the article preform to a second temperature above the first temperature and below a preselected sintering temperature to remove at least the solvent and the binder from the matrix mixture; sintering the article preform at the preselected sintering temperature at ambient pressure at which the discontinuous material, in a substantially solid phase, consolidates to produce a substantially continuous matrix while the inorganic filler simultaneously expands to counteract stresses from consolidated of the discontinuous material so as to form a fiber-reinforced composite matrix with reduced tensile stresses.
Claim 3
Dependent Claim
36 words
The method of claim 1 in which the step of interspersing includes forming a plurality of plies, each ply comprising the matrix mixture about reinforcing fibers, the plies then shaped in relation to the composite member.
Claim 4
Dependent Claim
13 words
The method of claim 1 in which the discontinuous material comprises ceramic particles.
Claim 5
Dependent Claim
18 words
The method of claim 1 in which the reinforcing fibers comprise 10-50 volume percent of the composite member.
Claim 6
Dependent Claim
40 words
The method of claim 1 in which the particulate inorganic filler which exhibits net expansion when heated to the sintering temperature consists of inorganic material selected from the group consisting of pyrophyllite, wollastonite, mica, talc, montmorillonite, kyanite and their mixtures.
Claim 7
Dependent Claim
49 words
The method of claim 1 further including the step of forming a fiber reinforced ceramic composite matrix preform wherein the matrix mixture consists essentially of, by weight, 50-93% ceramic particles and 7-50% filler prior to the step of sintering and after the step of heating to a second temperature.
Claim 8
Dependent Claim
17 words
The method of claim 6 in which the ceramic particles are alumina and the filler is pyrophyllite.
Claim 9
Dependent Claim
77 words
The method of claim 1 in which: the reinforcing fibers expand relative to the matrix mixture during the step of sintering; and the proportion of the inorganic filler in the matrix mixture is selected so that expansion of the filler during the step of sintering counteracts stresses resulting from consolidation of the discontinuous material in the substantially solid state whereby after sintering, the matrix is substantially free of cracks from residual stresses perpendicular to the reinforcing fiber.
Claim 10
Dependent Claim
35 words
The method of claim 8 in which: the discontinuous material comprises ceramic particles; and the filler consists of inorganic material selected from the group consisting of pyrophyllite, wollastonite, mica, talc, montmorillonite, kyanite and their mixtures.
Claim 11
Dependent Claim
13 words
The method of claim 9 in which the filler consists essentially of wollastonite.
Claim 12
Dependent Claim
21 words
The method of claim 10 in which the sintered article preform consists essentially of, by weight, 50-93% alumina and 7-50% pyrophyllite.
Claim 13
Dependent Claim
13 words
The method of claim 9 in which the filler consists essentially of wollastonite.
Claim 14
Dependent Claim
166 words
A composite member preform, comprising: a plurality of reinforcing fibers; and a matrix mixture interspersed about the fibers; the matrix mixture including a solvent, a binder, and a plasticizer, at least the solvent and binder being removable from the matrix mixture by heating the preform to a first temperature below a preselected sintering temperature, the matrix mixture further including a discontinuous ceramic material which consolidates in a substantially solid phase and produces a predetermined shrinkage amount and associated stresses by heating at a preselected sintering temperature at ambient pressure, and a particulate inorganic filler having a lathy-type crystal shape which exhibits net expansion relative to the discontinuous material when heated to the preselected sintering temperature, the matrix preform being pliable prior to heating to the first temperature; The proportion of the inorganic filler in the mixture being selected so that expansion of the filler substantially counteracts matrix stresses due to consolidation of the discontinuous material and thermal stresses between the matrix and fibers at elevated temperatures.
Claim 15
Dependent Claim
166 words
A composite member preform, comprising: a plurality of reinforcing fibers; and a matrix mixture interspersed about the fibers; the matrix mixture including a solvent, a binder, and a plasticizer, at least the solvent and binder being removable from the matrix mixture by heating the preform to a first temperature below a preselected sintering temperature, the matrix mixture further including a discontinuous ceramic material which consolidates in a substantially solid phase and produces a predetermined shrinkage amount and associated stresses by heating at a preselected sintering temperature at ambient pressure, and a particulate inorganic filler having a lathy-type crystal shape which exhibits net expansion relative to the discontinuous material when heated to the preselected sintering temperature, the matrix preform being pliable prior to heating to the first temperature; The proportion of the inorganic filler in the mixture being selected so that expansion of the filler substantially counteracts matrix stresses due to consolidation of the discontinuous material and thermal stresses between the matrix and fibers at elevated temperatures.
Claim 16
Dependent Claim
17 words
The preform of claim 13 in which the reinforcing fibers comprise 10-50 volume percent of the preform.
Claim 17
Dependent Claim
25 words
The preform of claim 13 which comprises a plurality of plies, each having the matrix mixture interspersed about the reinforcing fibers, laminated into the preform.
Claim 18
Dependent Claim
28 words
The preform of claim 14 in which the filler consists of inorganic material selected from the group consisting of pyrophyllite, wollastonite, mica, talc, montmorillonite, kyanite and their mixtures.
Claim 19
Dependent Claim
13 words
The preform of claim 16 in which the filler consists essentially of pyrophyllite.
Claim 20
Dependent Claim
25 words
The preform of claim 17 in which the matrix mixture consists essentially of by weight, 50-93% ceramic, wherein the ceramic is alumina and 7-50% pyrophyllite.
Claim 21
Dependent Claim
13 words
The preform of claim 16 in which the filler consists essentially of wollastonite.
Claim 22
Dependent Claim
49 words
A sintered consolidated reinforced composite member comprising reinforcing fibers and a matrix interspersed about the fibers, wherein: the matrix is a mixture of a discontinuous ceramic material and a filler of an inorganic material selected from the group consisting of wollastonite and pyrophyllite, and having a lathy-type crystal shape.
Claim 23
Dependent Claim
49 words
A sintered consolidated reinforced composite member comprising reinforcing fibers and a matrix interspersed about the fibers, wherein: the matrix is a mixture of a discontinuous ceramic material and a filler of an inorganic material selected from the group consisting of wollastonite and pyrophyllite, and having a lathy-type crystal shape.
Claim 24
Dependent Claim
17 words
The member of claim 20 in which the reinforcing fibers are 10-50 volume percent of the member.
Claim 25
Dependent Claim
19 words
The member of claim 20 in which the matrix consists essentially of, by weight 50-93% alumina and 7-50% pyrophyllite.
Claim 26
Dependent Claim
172 words
A composite member preform comprising: a plurality of reinforcing fibers; and a matrix mixture interspersed about the fibers; the reinforcing fibers exhibiting expansion relative to the matrix mixture when heated to elevated temperatures; the matrix mixture including a solvent, a plasticizer and a binder blended with the matrix mixture, at least the solvent and plasticizer being removable by heating the member to a first temperature below a preselected sintering temperature, the matrix mixture further including a discontinuous ceramic material which will consolidate, in a substantially solid phase by heating at the preselected sintering temperature, and a particulate inorganic filler having a lathy-type crystal shape which will exhibit net expansion relative to the discontinuous material when heated to the preselected sintering temperature; the proportion of the inorganic filler in the matrix mixture being selected so that the net effect of expansion of the filler and the fibers and consolidation of the discontinuous material after preform sintering substantially eliminates matrix cracks perpendicular to the fiber axis resulting from overall preform shrinkage and associated stresses.
Claim 27
Dependent Claim
172 words
A composite member preform comprising: a plurality of reinforcing fibers; and a matrix mixture interspersed about the fibers; the reinforcing fibers exhibiting expansion relative to the matrix mixture when heated to elevated temperatures; the matrix mixture including a solvent, a plasticizer and a binder blended with the matrix mixture, at least the solvent and plasticizer being removable by heating the member to a first temperature below a preselected sintering temperature, the matrix mixture further including a discontinuous ceramic material which will consolidate, in a substantially solid phase by heating at the preselected sintering temperature, and a particulate inorganic filler having a lathy-type crystal shape which will exhibit net expansion relative to the discontinuous material when heated to the preselected sintering temperature; the proportion of the inorganic filler in the matrix mixture being selected so that the net effect of expansion of the filler and the fibers and consolidation of the discontinuous material after preform sintering substantially eliminates matrix cracks perpendicular to the fiber axis resulting from overall preform shrinkage and associated stresses.
Claim 28
Dependent Claim
17 words
The preform of claim 23 in which the reinforcing fibers comprise 10-50 volume percent of the preform.
Claim 29
Dependent Claim
26 words
The preform of claim 23 which comprises a plurality of plies, each ply comprised of a matrix mixture about the reinforcing fibers, laminated into a preform.
Claim 30
Dependent Claim
13 words
The preform of claim 23 in which the discontinuous material comprises ceramic particles.
Claim 31
Dependent Claim
28 words
The preform of claim 26 in which the filler consists of inorganic material selected from the group consisting of pyrophyllite, wollastonite, mica, talc, montmorillonite, kyanite and their mixture.
Claim 32
Dependent Claim
14 words
The preform of claim 27 in which the filler consists of essentially of pyrophyllite.
Claim 33
Dependent Claim
20 words
The preform of claim 28 in which the matrix mixture consists essentially of, by weight, 50-90% alumina and 7-50% pyrophyllite.
Claim 34
Dependent Claim
13 words
The preform of claim 27 in which the filler consists essentially of wollastonite.
Claim 35
Dependent Claim
25 words
The preform of claim 23 in which the reinforcing fibers are selected from the group of monofilaments consisting of sapphire, silicon carbide and mixtures thereof.
Claim 36
Dependent Claim
30 words
The preform of claim 23 in which the reinforcing fibers are selected from the group of rovings and yarns consisting of aluminum oxide, silicon dioxide, boron oxide and mixtures thereof.
Claim 37
Dependent Claim
31 words
The preform of claim 23 in which the reinforcing fibers are selected from the group of chopped fibers and whiskers consisting of aluminum oxide, silicon dioxide, boron oxide and mixtures thereof.
References Cited (Backward Citations)
US3549393A
Cited
US3827892A
Cited
US4020234A
Cited
WO1980001109A1
Cited
US4284664A
Cited
US4265669A
Cited
WO1986000189A1
Cited
EP0227019A2
Cited
WO1988000396A1
Cited
US4885199A
Cited
US4849382A
Cited
US4861646A
Cited
US4919991A
Cited
US4935387A
Cited
US4892846A
Cited
US5034356A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-04-25 | 1997-10-25 | 1998-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-04-25 | 2001-10-25 | 2002-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-04-25 | 2005-10-25 | 2006-04-26 | $7700.00 | Window Closed / Lapsed |