US5300452A Expired / Lapsed US ⏱️ 0.0 years remaining

Method of manufacturing an optoelectronic semiconductor device

Assignee: Uniphase Opto Holdings Inc
•
Filing: 1992-10-27
•
Granted: 1994-04-05
•
Expires: 2012-10-27
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A method of manufacturing an optoelectronic semiconductor device whereby a surface (1) of a semiconductor (2) built up from a number of layers of semiconductor material (4, 5, 6, 7) grown epitaxially on a semiconductor substrate (3), with a top layer (4) of GaAs adjoining the surface (1) and a subjacent layer (5) comprising InP, in particular made of (Al x Ga 1-x ) y In 1-y P with 0.5<x<0.8 and 0.4<y<0.6, is provided with an etching mask (8), after which the top layer (4) and the subjacent layer (5) are locally etched in a plasma generated in a gas mixture comprising SiCl 4 and Ar. According to the invention, CH 4 is added to the gas mixture in which the plasma is generated. This measure leads to the creation of a smooth surface during etching of both layers, and in particular during etching of the layer comprising InP. The walls (10) of the ridge (9) formed in the layers are also smooth and steep.

Inventors

  • 👤 Chang V. J. M. Chang
  • 👤 Johannes C. N. Rijpers

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-09 18:14
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/24; H10P50/246; H10H; H10H20/00; H10H20/01; H10H20/011; H10H20/013

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 98 words
A method of manufacturing an optoelectronic semiconductor device whereby a surface of a semiconductor body, which is built up from a number of semiconductor material layers epitaxially grown on a semiconductor substrate with a top layer of GaAs adjoining the surface and a subjacent layer comprising InP, is provided with an etching mask, after which the top layer and the subjacent layer are locally etched away in a plasma which is generated in a gas mixture comprising SiCl 4 and Ar, characterized in that CH 4 is added to the gas mixture in which the plasma is generated.
Claim 2
Independent Claim 98 words
A method of manufacturing an optoelectronic semiconductor device whereby a surface of a semiconductor body, which is built up from a number of semiconductor material layers epitaxially grown on a semiconductor substrate with a top layer of GaAs adjoining the surface and a subjacent layer comprising InP, is provided with an etching mask, after which the top layer and the subjacent layer are locally etched away in a plasma which is generated in a gas mixture comprising SiCl 4 and Ar, characterized in that CH 4 is added to the gas mixture in which the plasma is generated.
Claim 3
Dependent Claim 33 words
A method as claimed in claim 1, characterized in that the layer comprising InP is formed by a layer of (Al x Ga 1-x ) y In 1-y P, with 0.5<x<0.8 and 0.4<y<0.6.
Claim 4
Dependent Claim 29 words
A method as claimed in claim 2, characterized in that 10 to 40 vol. % CH 4 is added to the gas mixture in which the plasma is generated.
Claim 5
Dependent Claim 44 words
A method as claimed in claim 3, characterized in that the plasma is generated in a gas mixture with i vol. % SiCl 4 , j vol. % CH 4 and 100-i-j vol. % Ar, in which i=25 to 30 and j=20 to 25.
Claim 6
Dependent Claim 26 words
A method as claimed in claim 1, characterized in that the semiconductor body is heated to a temperature of between 100° and 150° C. during etching.
Claim 7
Dependent Claim 24 words
A method as claimed in claim 2 wherein the semiconductor body is heated to a temperature of between 100° and 150° C. during etching.
Claim 8
Dependent Claim 24 words
A method as claimed in claim 3 wherein the semiconductor body is heated to a temperature of between 100° and 150° C. during etching.
Claim 9
Dependent Claim 24 words
A method as claimed in claim 4 wherein the semiconductor body is heated to a temperature of between 100° and 150° C. during etching.

References Cited (Backward Citations)

US5074955A Cited
US5017511A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1997-04-04 1997-10-04 1998-04-05 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 2001-04-04 2001-10-04 2002-04-05 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 2005-04-04 2005-10-04 2006-04-05 $7700.00 Window Closed / Lapsed