Multiple material systems for selective beam sintering
Assignee: The University of Texas System
•
Filing: 1992-09-25
•
Granted: 1994-03-22
•
Expires: 2012-09-25
Abstract
Abstract A method and apparatus for selectively sintering a layer of powder to produce a part comprising a plurality of sintered layers. The apparatus includes a computer controlling a laser to direct the laser energy onto the powder to produce a sintered mass. The computer either determines or is programmed with the boundaries of the desired cross-sectional regions of the part. For each cross-section, the aim of the laser beam is scanned over a layer of powder and the beam is switched on to sinter only the powder within the boundaries of the cross-section. Powder is applied and successive layers sintered until a completed part is formed. Preferably, the powder comprises a plurality of materials having different dissociation or bonding temperatures. The powder preferably comprises blended or coated materials.
Inventors
- 👤 David L. Bourell
- 👤 Harris L. Marcus
- 👤 Joel W. Barlow
- 👤 Joseph L. Beaman
- 👤 Carl R. Deckard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:49
CPC Classifications
B; B05; B05C; B05C19/00; B05C19/008; B22; B22F; B22F10/00; B22F10/20; B22F10/28; B22F3/00; B22F3/004; B22F3/10; B22F3/105; B22F7/00; B22F7/02; B23; B23K; B23K26/00; B23K26/08; B23K26/082; B23K26/34; B29; B29C; B29C41/00; B29C41/02; B29C41/12; B29C41/34; B29C41/46; B29C64/00; B29C64/10; B29C64/141; B29C64/153; B33; B33Y; B33Y10/00; C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C23; C23C; C23C24/00; C23C24/08; C23C24/10; C23C26/00; C23C26/02; G; G05; G05B; G05B19/00; G05B19/02; G05B19/18; G05B19/41; B22F10/30; B22F10/36; B22F10/366; B22F10/60; B22F10/64; B22F12/00; B22F12/22; B22F12/40; B22F12/41; B22F12/44; B22F12/49; B22F12/50; B22F12/52; B22F2003/1052; B22F2998/00; B22F2998/10; B29C35/00; B29C35/02; B29C35/04; B29C35/045; G05B2219/00; G05B2219/30; G05B2219/49; G05B2219/49013; G05B2219/49018; Y; Y02; Y02P; Y02P10/00; Y02P10/25
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
123 words
A method of producing a part, comprising the steps of: depositing a layer of a powder onto a target surface, said powder comprising particles of a first material coated with a second material, said second material having a lower softening temperature than said first material; irradiating a selected portion of said powder corresponding to a cross-section of the part with a directed energy beam, so that the second material in said selected portion bonds particles of said first material; repeating said depositing and irradiating steps for a plurality of layers so that bonded portions of adjacent layers bond to one another to form a mass; removing unbonded portions of the powder to yield the mass; and heating the mass after said removing step.
Claim 2
Independent Claim
123 words
A method of producing a part, comprising the steps of: depositing a layer of a powder onto a target surface, said powder comprising particles of a first material coated with a second material, said second material having a lower softening temperature than said first material; irradiating a selected portion of said powder corresponding to a cross-section of the part with a directed energy beam, so that the second material in said selected portion bonds particles of said first material; repeating said depositing and irradiating steps for a plurality of layers so that bonded portions of adjacent layers bond to one another to form a mass; removing unbonded portions of the powder to yield the mass; and heating the mass after said removing step.
Claim 3
Dependent Claim
30 words
The method of claim 1, wherein said second material is driven off in said heating step; and wherein said heating step fuses particles of said first material to one another.
Claim 4
Dependent Claim
16 words
The method of claim 2, wherein said second material comprises a polymer of the PMMA type.
Claim 5
Dependent Claim
16 words
The method of claim 1, wherein said first and second materials interact in said heating step.
Claim 6
Dependent Claim
22 words
The method of claim 1, wherein the thermal conductivity of said first material is substantially greater than that of said second material.
Claim 7
Dependent Claim
19 words
The method of claim 1, further comprising: controlling the temperature of bonded and unbonded powder at the target surface.
Claim 8
Dependent Claim
17 words
The method of claim 6, wherein said controlling step comprises: heating the powder at the target surface.
Claim 9
Dependent Claim
42 words
The method of claim 1, wherein said first and second materials have different absorptivity characteristics; and wherein the wavelength of the directed energy beam is selected so as to be more highly absorbed by said second material than by said first material.
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein the second material in said selected portions is sintered during said irradiating step in such a manner as to bond particles of said first material.
Claim 11
Independent Claim
138 words
A method of producing a part, comprising the steps of: depositing a layer of a powder onto a target surface, said powder comprising a first material and a second material, said second material having a lower softening temperature than said first material; irradiating a selected portion of said powder corresponding to a cross-section of the part with a directed energy beam, so that the second material in said selected portion bonds particles of said first material; during said irradiating step, exposing said powder to a gas phase to promote infiltration of the second material within particles of the first material; repeating said depositing, irradiating and exposing steps for a plurality of layers so that bonded portions of adjacent layers fuse to one another to form a mass; and removing unbonded portions of the powder to yield the mass.
Claim 12
Independent Claim
138 words
A method of producing a part, comprising the steps of: depositing a layer of a powder onto a target surface, said powder comprising a first material and a second material, said second material having a lower softening temperature than said first material; irradiating a selected portion of said powder corresponding to a cross-section of the part with a directed energy beam, so that the second material in said selected portion bonds particles of said first material; during said irradiating step, exposing said powder to a gas phase to promote infiltration of the second material within particles of the first material; repeating said depositing, irradiating and exposing steps for a plurality of layers so that bonded portions of adjacent layers fuse to one another to form a mass; and removing unbonded portions of the powder to yield the mass.
Claim 13
Dependent Claim
11 words
The method of claim 10, wherein said gas phase is inert.
Claim 14
Dependent Claim
11 words
The method of claim 10, wherein said gas phase is active.
Claim 15
Dependent Claim
17 words
The method of claim 10, wherein said first material is copper and said second material is tin.
Claim 16
Dependent Claim
18 words
The method of claim 10, wherein said first material is tungsten carbide and said second material is cobalt.
Claim 17
Dependent Claim
34 words
The method of claim 10, wherein the second material at the selected portion of the powder in said irradiating step is sintered in such a manner as to bond particles of said first material.
Claim 18
Independent Claim
117 words
A method of producing a part, comprising the steps of: depositing a layer of a powder onto a target surface, said powder comprising a first material and a second material, said second material being a metal and having a lower softening temperature than said first material; irradiating a selected portion of said powder corresponding to a cross-section of the part with a directed energy beam, so that the second material in said selected portion bonds particles of said first material; repeating said depositing and irradiating steps for a plurality of layers so hat bonded portions of adjacent layers fuse to one another to form a mass; and removing unbonded portions of the powder to yield the mass.
Claim 19
Independent Claim
117 words
A method of producing a part, comprising the steps of: depositing a layer of a powder onto a target surface, said powder comprising a first material and a second material, said second material being a metal and having a lower softening temperature than said first material; irradiating a selected portion of said powder corresponding to a cross-section of the part with a directed energy beam, so that the second material in said selected portion bonds particles of said first material; repeating said depositing and irradiating steps for a plurality of layers so hat bonded portions of adjacent layers fuse to one another to form a mass; and removing unbonded portions of the powder to yield the mass.
Claim 20
Dependent Claim
26 words
The method of claim 16, further comprising: heating the mass after said removing step so that the second material infiltrates the first material within the mass.
Claim 21
Dependent Claim
17 words
The method of claim 17, wherein said first material is copper and said second material is tin.
Claim 22
Dependent Claim
34 words
The method of claim 16, wherein the second material in said selected portion of said powder is sintered in said irradiating step in such a manner as to bond particles of said first material.
References Cited (Backward Citations)
DE137951C
Cited
US2076952A
Cited
GB1215184A
Cited
DE2263777A1
Cited
US3985995A
Cited
US4117302A
Cited
US4135902A
Cited
US4300474A
Cited
US4270675A
Cited
US4323756A
Cited
US4247508A
Cited
US4247508B1
Cited
JPS5945089A
Cited
JPS5976689A
Cited
US4587396A
Cited
US4474861A
Cited
US4540867A
Cited
US4575330B1
Cited
US4575330A
Cited
JPS61296976A
Cited
EP0209366A1
Cited
EP0221276A1
Cited
US4752352A
Cited
US4944817A
Cited
US4863538A
Cited
US4938816A
Cited
US5017753A
Cited
US5076869A
Cited
WO1988002677A2
Cited
US4818562A
Cited
EP0283003A2
Cited
US5053090A
Cited
US5017317A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-21 | 1997-09-20 | 1998-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-21 | 2001-09-20 | 2002-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-21 | 2005-09-20 | 2006-03-22 | $7700.00 | Window Closed / Lapsed |