Method for the preparation of silicon carbide-carbon fiber composite
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1992-10-15
•
Granted: 1994-03-15
•
Expires: 2012-10-15
Abstract
Abstract A novel method is disclosed for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers having an outstandingly high mechanical strength. The method comprises impregnating carbon fibers with a mixture of fine silicon particles and a thermosetting resin such as a phenolic resin to give a carbon fiber compact body impregnated with the mixture, which is then subjected to a heat treatment at about 1400° C. in an inert atmosphere so that the thermosetting resin is thermally decomposed to produce free carbon capable of reacting with the silicon particles without affecting the carbon fibers embedded in the matrix due to the preferential reactivity of the silicon particles with the free carbon produced from the resin thus not to decrease the recinforcing effect of the carbon fibers.
Inventors
- 👤 Eiji Tani
- 👤 Kazuhisa Shobu
- 👤 Tadahiko Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:07
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/571; C04B35/573; C04B35/71; C04B35/78; C04B35/80; D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/126
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
151 words
A method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers which comprises the steps of: (a) mixing particles of elementary silicon and a thermosetting resin in such a proportion that the molar ratio of the silicon and the carbon in the thermosetting resin is in the range from 0.3 to 1.2 to form a mixture; (b) impregnating carbon fibers with the mixture prepared in step (a) to form a green carbon fiber compact impregnated with the mixture of the silicon particles and the thermosetting resin; and (c) heating the green carbon fiber compact at a temperature in the range from 1300° C. to 1500° C. in an atmosphere of an inert gas to effect thermal decomposition of the thermosetting resin forming free carbon and to effect the reaction of the silicon particles with the free carbon produced from the thermosetting resin to form silicon carbide.
Claim 2
Independent Claim
151 words
A method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers which comprises the steps of: (a) mixing particles of elementary silicon and a thermosetting resin in such a proportion that the molar ratio of the silicon and the carbon in the thermosetting resin is in the range from 0.3 to 1.2 to form a mixture; (b) impregnating carbon fibers with the mixture prepared in step (a) to form a green carbon fiber compact impregnated with the mixture of the silicon particles and the thermosetting resin; and (c) heating the green carbon fiber compact at a temperature in the range from 1300° C. to 1500° C. in an atmosphere of an inert gas to effect thermal decomposition of the thermosetting resin forming free carbon and to effect the reaction of the silicon particles with the free carbon produced from the thermosetting resin to form silicon carbide.
Claim 3
Dependent Claim
30 words
The method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers as claimed in claim 1 in which the thermosetting resin is a phenolic resin.
Claim 4
Dependent Claim
37 words
The method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers as claimed in claim 1 in which the particles of elementary silicon have an average particle diameter not exceeding 20 μm.
Claim 5
Dependent Claim
61 words
The method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers as claimed in claim 1 in which the carbon fibers are impregnated with the mixture of the silicon particles and the thermosetting resin in such an amount that the volume fraction of the carbon fibers in the composite ceramic body is at least 20% .
Claim 6
Dependent Claim
39 words
The method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers as claimed in claim 1 in which the temperature of heating in step (c) is in the range from 1400° to 1500° C.
Claim 7
Independent Claim
195 words
A method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers which comprises the steps of: (a) mixing particles of elementary silicon and a thermosetting resin in such a proportion that the molar ratio of the silicon and the carbon in the thermosetting resin is in the range from 0.3 to 1.2 to form a mixture; (b) impregnating carbon fibers with the mixture prepared in step (a) to form a green carbon fiber compact impregnated with the mixture of the silicon particles and the thermosetting resin; (c) heating the green carbon fiber compact at a temperature in the range from 1300° C. to 1500° C. in an atmosphere of an inert gas to effect thermal decomposition of the thermosetting resin forming free carbon and to effect the reaction of the silicon particles with the free carbon produced from the thermosetting resin to form a silicon carbide-based porous body; (d) infiltrating the silicon carbide-based porous body with an organosilicon compound; and (e) calcining the silicon carbide-based porous body infiltrated with the organosilicon compound at a temperature in the range from 1000° to 1700° C. in an atmosphere of an inert gas.
Claim 8
Independent Claim
195 words
A method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers which comprises the steps of: (a) mixing particles of elementary silicon and a thermosetting resin in such a proportion that the molar ratio of the silicon and the carbon in the thermosetting resin is in the range from 0.3 to 1.2 to form a mixture; (b) impregnating carbon fibers with the mixture prepared in step (a) to form a green carbon fiber compact impregnated with the mixture of the silicon particles and the thermosetting resin; (c) heating the green carbon fiber compact at a temperature in the range from 1300° C. to 1500° C. in an atmosphere of an inert gas to effect thermal decomposition of the thermosetting resin forming free carbon and to effect the reaction of the silicon particles with the free carbon produced from the thermosetting resin to form a silicon carbide-based porous body; (d) infiltrating the silicon carbide-based porous body with an organosilicon compound; and (e) calcining the silicon carbide-based porous body infiltrated with the organosilicon compound at a temperature in the range from 1000° to 1700° C. in an atmosphere of an inert gas.
Claim 9
Dependent Claim
29 words
The method for the preparation of a silicon carbide-based composite ceramic body reinforced with carbon fibers as claimed in claim 6 in which the organosilicon compound is a polysilastyrene.
References Cited (Backward Citations)
US3079273A
Cited
US3385723A
Cited
US3628985A
Cited
US4696827A
Cited
DE3311553A1
Cited
US5196235A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-14 | 1997-09-13 | 1998-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-14 | 2001-09-13 | 2002-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-14 | 2005-09-13 | 2006-03-15 | $7700.00 | Window Closed / Lapsed |