Precipitation of homogeneous polymer mixtures from supercritical fluid solutions
Assignee: University of Delaware
•
Filing: 1991-03-27
•
Granted: 1994-03-01
•
Expires: 2011-03-27
Abstract
Abstract Homogeneous polymer blends are prepared from otherwise thermodynamically immiscible polymers. Thus, mixtures of polymers such as poly (methyl methacrylate) and poly (ethyl methacrylate) are dissolved under pressure in supercritical fluid solvents such as chlorodifluoromethane and expanded through a fine nozzle. As the SCF solvent evaporates, the polymer mixture deposits as a substantially homogeneous blend.
Inventors
- 👤 Annette D. Shine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:41
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/14; C08J3/005; C08L; C08L101/00; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/54
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
88 words
A process for preparing a homogeneous blend of otherwise thermodynamically immiscible polymers, comprising: a) preparing a solution of said polymers in a supercritical fluid solvent to form a single-phase solution blend;, b) rapidly expanding the solution from step (a) across a small diameter nozzle; and c) removing said supercritical fluid solvent to precipitate the solid polymer blend at a final temperature which is no more than about 30° C. above the glass transition temperature of the polymer blend, whereby, the non-equilibrium homogeneous morphology of the blend is maintained.
Claim 2
Dependent Claim
88 words
A process for preparing a homogeneous blend of otherwise thermodynamically immiscible polymers, comprising: a) preparing a solution of said polymers in a supercritical fluid solvent to form a single-phase solution blend;, b) rapidly expanding the solution from step (a) across a small diameter nozzle; and c) removing said supercritical fluid solvent to precipitate the solid polymer blend at a final temperature which is no more than about 30° C. above the glass transition temperature of the polymer blend, whereby, the non-equilibrium homogeneous morphology of the blend is maintained.
Claim 3
Dependent Claim
24 words
A process according to claim 1 wherein the solubility of the polymers in the supercritical fluid solvent is at least about 0.01% by weight.
Claim 4
Dependent Claim
23 words
A process according to claim 1 wherein the concentration of the polymers in the supercritical fluid is less than about 5% by weight.
Claim 5
Dependent Claim
34 words
A process according to claim 1 wherein the supercritical fluid solvent is a member selected from the group consisting of chlorodifluoromethane, liquefied CO 2 , N 2 O, and C 2 -C 4 alkanes.
Claim 6
Dependent Claim
51 words
A process according to claim 1 wherein the polymer blend comprises two or more otherwise thermodynamically immiscible polymers selected from the group consisting of polyolefins; the polystyrenes; the polyamides; silicone polymers; polyesters; polyacrylates; polycyanoacrylates; polymethacrylates; polycyanomethacrylates; polycarbonates; poly(dienes); poly(oxides); vinyl polymers; polyurethanes; polysulfones; cellulosic polymers; polyaminoacids; polyimides; and random copolymers thereof.
Claim 7
Dependent Claim
33 words
A process according to claim 1 which is carried out at a pressure from about 2000 psi to about 10,000 psi and at a temperature from about 30° C. to about 150° C.
Claim 8
Dependent Claim
25 words
A process according to claim 1 wherein the polymer blend comprises poly (methyl methacrylate) and poly (ethyl methacrylate) and the supercritical fluid solvent is chlorodifluoromethane.
Claim 9
Dependent Claim
10 words
A homogeneous blend of polymers prepared according to claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-28 | 1997-08-30 | 1998-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-28 | 2001-08-30 | 2002-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-28 | 2005-08-30 | 2006-03-01 | $7700.00 | Window Closed / Lapsed |