US5283279A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Flame retardant coating compositions and coated articles
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1991-05-17
•
Granted: 1994-02-01
•
Expires: 2011-05-17
Abstract
Abstract A coating composition comprising (A) a polyorganosiloxane graft copolymer emulsion, (B) a reaction product between an amino functional silane and/or a hydrolyzate thereof and an acid anhydride, (C) colloidal silica, (D) a curing catalyst, and (E) an inorganic filler is useful in coating exterior and interior building materials. The composition is applicable to a substrate to form a coating at room temperature having sufficient extensibility to follow cracks in the underlying substrate as well as low-to-high temperature sensitive performance, moisture permeability, flame retardance, and decorative effect.
Inventors
- 👤 Yasuaki Hara
- 👤 Morizo Nakazato
- 👤 Yasunori Takaichi
- 👤 Tsuyoshi Urashima
- 👤 Tsuyoshi Aoyama
- 👤 Seiichi Nishimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:49
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/10
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
183 words
A flame retardant coating composition comprising (A) 100 parts by weight of a polyorganosiloxane graft copolymer in emulsion form comprised of 10 to 70% by weight of the polyorganosiloxane graft copolymer composed of a polyorganosiloxane of the general formula: R.sup.1.sub.n SiO.sub.(4-n)/2 ( 1) wherein R 1 is selected from the group consisting of hydrogen, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms and an aryl group having 6 to 12 carbon atoms, and n is a number equal to 0, 1 or 2 and 10 to 90% by weight of an unsaturated monomer selected from the group consisting of styrene, α-methyl styrene, acrylic acid, methacrylic acid, an acrylate, a methacrylate, butadiene and isoprene graft polymerized therewith, (B) 0.1 to 10 parts by weight of a reaction product of an amino functional silane and/or a hydrolyzate thereof and an acid anhydride, (C) 1 to 50 parts by weight of colloidal silica, (D) 0.01 to 10 parts by weight of a curing catalyst, and (E) 20 to 100 parts by weight of an inorganic filler.
Claim 2
Dependent Claim
183 words
A flame retardant coating composition comprising (A) 100 parts by weight of a polyorganosiloxane graft copolymer in emulsion form comprised of 10 to 70% by weight of the polyorganosiloxane graft copolymer composed of a polyorganosiloxane of the general formula: R.sup.1.sub.n SiO.sub.(4-n)/2 ( 1) wherein R 1 is selected from the group consisting of hydrogen, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms and an aryl group having 6 to 12 carbon atoms, and n is a number equal to 0, 1 or 2 and 10 to 90% by weight of an unsaturated monomer selected from the group consisting of styrene, α-methyl styrene, acrylic acid, methacrylic acid, an acrylate, a methacrylate, butadiene and isoprene graft polymerized therewith, (B) 0.1 to 10 parts by weight of a reaction product of an amino functional silane and/or a hydrolyzate thereof and an acid anhydride, (C) 1 to 50 parts by weight of colloidal silica, (D) 0.01 to 10 parts by weight of a curing catalyst, and (E) 20 to 100 parts by weight of an inorganic filler.
Claim 3
Dependent Claim
25 words
The composition of claim 1, said composition having been prepared by supplying components (B) and (C), as a mixture of components (B) and (C), respectively.
Claim 4
Dependent Claim
40 words
The composition of claim 1 said composition having been prepared by first preparing the emulsion of component (A), and mixing the prepared emulsion with a mixture of components (B) and (C), then with component (D), and finally with component (E).
Claim 5
Dependent Claim
15 words
An article coated with the coating composition of any one of claims 1, 2, 3.
Claim 6
Dependent Claim
21 words
The composition of claim 1 wherein the weight of the unsaturated monomer graft polymerized with the polyorganosiloxane is 20 to 60%.
Claim 7
Dependent Claim
33 words
The composition of claim 1 wherein the polyorganosiloxane of component (A) has a molecular weight of at least 10,000 and at least two hydroxy groups attached to silicon atoms in the molecule thereof.
Claim 8
Dependent Claim
33 words
The composition of claim 6 wherein the polyorganosiloxane of component (A) has a molecular weight of 10,000 to 1,000,000 and 2 to 10 hydroxy groups attached to silicon atoms in the molecule thereof.
Claim 9
Dependent Claim
33 words
The composition of claim 6 wherein the polyorganosiloxane of component (A) has a molecular weight of 100,000 to 1,000,000 and 4 to 6 hydroxy groups attached to silicon atoms in the molecule thereof.
Claim 10
Dependent Claim
78 words
The composition of claim 1 wherein the reaction product of components (B) is of the general formula: R.sup.3.sub.m Si(OR.sup.1).sub.4-m ( 6) wherein R 3 is an amino-containing monovalent organic group and R 1 is selected from the group consisting of hydrogen, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms and an aryl group having 6 to 12 carbon atoms, and m is an integer of 1 to 4.
Claim 11
Dependent Claim
28 words
The composition of claim 1, wherein the reaction product of component (B) is selected from the group consisting of 3-aminopropyltriethoxysilane, N-(2-aminoethyl)-3-aminopropylmethyldimethoxysilane, 3-aminopropyltrimethoxysilane, N-triethylenediaminepropyltrimethoxysilane, N-triethylenediaminepropylmethyldimetoxysilane and a mixture thereof.
Claim 12
Dependent Claim
58 words
The composition of claim 1 wherein the reaction product of component (B) is selected from the group consisting of methyltetrahydrophthalic anhydride, methylhymic anhydride, benzophenonetetracarboxylic anhydride, phthalic anhydride, ethylene glycol bistrimellitate, maleic anhydride, pyromellitic anhydride, succinic anhydride, polyazelaic polyanhydride, trimellitic anhydride, nadic anhydride, phenylmaleic anhydride, methylhexahydrophthalic anhydride, hexahydrophthalic anhydride, dodecylsuccinic anhydride, dichloromaleic anhydride, chlororendic anhydride and a mixture thereof.
Claim 13
Dependent Claim
21 words
The composition of claim 1 wherein the colloidal silica of component (C) has a particle size of 10 to 40 mμ.
Claim 14
Dependent Claim
30 words
The composition of claim 1 wherein the curing catalyst of component (D) is a metal salt of an organic acid, an amine compound or a salt of an amine compound.
Claim 15
Dependent Claim
38 words
The composition of claim 1 wherein the curing catalyst of component (D) is selected from the group consisting of dibutyltin dilaurate, dioctyltin, dilaurate, dibutyltin diacetate, tin octylate, tin laurate, iron octylate, lead octylate, tetrabutyltitanate and a mixture thereof.
Claim 16
Dependent Claim
28 words
The composition of claim 1 wherein the curing catalyst of component (D) is selected from the group consisting of n-hexylamine, guanidine an a salt thereof with hydrochloric acid.
Claim 17
Dependent Claim
16 words
The composition of claim 1 wherein the inorganic filler of component (E) is an extender pigment.
Claim 18
Dependent Claim
43 words
The composition of claim 1 wherein the inorganic filler of component (E) is selected from the group consisting of calcium carbonate, silica other than colloidal silica, clay, kaoline, talc, titanium dioxide, carbon black, aluminum oxide, quartz, zinc oxide, mica and a mixture thereof.
References Cited (Backward Citations)
US4769405A
Cited
US5004771A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-31 | 1997-08-02 | 1998-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-31 | 2001-08-02 | 2002-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-31 | 2005-08-02 | 2006-02-01 | $7700.00 | Window Closed / Lapsed |