Woven material of inorganic fiber and process for making the same
Assignee: Nitto Boseki Co Ltd
•
Filing: 1991-12-13
•
Granted: 1994-01-25
•
Expires: 2011-12-13
Abstract
Abstract A woven material of inorganic fiber, and a process for making the same, are disclosed in which exposed surfaces of warps and wefts constituting the woven material are opened as a result of being impinged by jets of pressurized water, whereby the fibers on the surface of the woven material are uniformly raised.
Inventors
- 👤 Shin Kasai
- 👤 Hideharu Waketa
- 👤 Keiichi Kato
- 👤 Yutaka Kawaguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:06
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0366; D; D06; D06C; D06C29/00; H05K2201/00; H05K2201/02; H05K2201/0275; H05K2201/029; H05K2201/20; H05K2201/2072; H05K2203/00; H05K2203/07; H05K2203/0736; H05K2203/0746; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10S428/902; Y10T; Y10T428/00; Y10T428/30; Y10T442/00; Y10T442/30; Y10T442/3033; Y10T442/3041; Y10T442/3065; Y10T442/3089
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
83 words
A process for manufacturing a woven material of inorganic fibers having warps and wefts, each of which is composed of a plurality of continuous filaments for reinforcing resins, including the steps of: impinging said woven material with jets of pressurized water to loosen said plurality of filaments and spread the filaments of which the warps and wefts are composed to close gaps between said warps and between said wefts, and impregnating said woven material with a resin uniformly throughout said plurality of filaments.
Claim 2
Dependent Claim
83 words
A process for manufacturing a woven material of inorganic fibers having warps and wefts, each of which is composed of a plurality of continuous filaments for reinforcing resins, including the steps of: impinging said woven material with jets of pressurized water to loosen said plurality of filaments and spread the filaments of which the warps and wefts are composed to close gaps between said warps and between said wefts, and impregnating said woven material with a resin uniformly throughout said plurality of filaments.
Claim 3
Dependent Claim
164 words
In a process for making a woven material of inorganic fibers used for reinforcing resins and obtained by weaving inorganic fibers, the improvement comprising the steps of: selecting a woven material having band-shaped warps and wefts, each of the warps and wefts being composed of continuous filament yarn having a number of twisted continuous filaments; arranging a plurality of nozzles in a transverse direction relative to said woven material, each of said nozzles having an eccentric rotating axis; rotating said nozzles about said axis at a high speed and uniformly impinging jets of pressurized water from the rotating nozzles onto the said warps and wefts of the woven material with a water jet pressure that is regulated to effect a substantially uniform loosening and opening of the warps and wefts widthwise relative to their originally woven form at the exposed surface of the woven material, so that the distance between said filaments is widened to facilitate uniform impregnation of said woven material with resin.
Claim 4
Dependent Claim
164 words
In a process for making a woven material of inorganic fibers used for reinforcing resins and obtained by weaving inorganic fibers, the improvement comprising the steps of: selecting a woven material having band-shaped warps and wefts, each of the warps and wefts being composed of continuous filament yarn having a number of twisted continuous filaments; arranging a plurality of nozzles in a transverse direction relative to said woven material, each of said nozzles having an eccentric rotating axis; rotating said nozzles about said axis at a high speed and uniformly impinging jets of pressurized water from the rotating nozzles onto the said warps and wefts of the woven material with a water jet pressure that is regulated to effect a substantially uniform loosening and opening of the warps and wefts widthwise relative to their originally woven form at the exposed surface of the woven material, so that the distance between said filaments is widened to facilitate uniform impregnation of said woven material with resin.
Claim 5
Dependent Claim
21 words
A process according to claim 2, in which said pressure is in the range of 30 to 150 kg/cm 2 .
Claim 6
Dependent Claim
16 words
A process according to claim 2, wherein said woven material is used as printed circuit boards.
Claim 7
Dependent Claim
13 words
A process according to claim 2, wherein said inorganic fibers are glass fibers.
Claim 8
Dependent Claim
186 words
In a process for making a woven material of inorganic fiber used for reinforcing resins and obtained by weaving inorganic fibers, the improvement comprising the steps of: selecting a woven material having band-shaped warps and wefts, each of the warps and wefts being composed of continuous filament yarn having a number of twisted continuous filaments; arranging a plurality of nozzles in a traverse direction relative to said woven material, each of said nozzles having an eccentric rotating axis; rotating said nozzles about said axis at a high speed and uniformly impinging jets of pressurized water from the rotating nozzles onto the woven material with a water jet pressure that is regulated to effect a substantially uniform loosening and opening of the warps and wefts widthwise relative to their originally woven form at the exposed surface of the woven material so as to widen the distance between said filaments and so as to effect a raising of said warps and wefts due to some of said continuous filaments being broken and damaged by the water jets, to thereby facilitate uniform impregnation of said woven material with resin.
Claim 9
Dependent Claim
186 words
In a process for making a woven material of inorganic fiber used for reinforcing resins and obtained by weaving inorganic fibers, the improvement comprising the steps of: selecting a woven material having band-shaped warps and wefts, each of the warps and wefts being composed of continuous filament yarn having a number of twisted continuous filaments; arranging a plurality of nozzles in a traverse direction relative to said woven material, each of said nozzles having an eccentric rotating axis; rotating said nozzles about said axis at a high speed and uniformly impinging jets of pressurized water from the rotating nozzles onto the woven material with a water jet pressure that is regulated to effect a substantially uniform loosening and opening of the warps and wefts widthwise relative to their originally woven form at the exposed surface of the woven material so as to widen the distance between said filaments and so as to effect a raising of said warps and wefts due to some of said continuous filaments being broken and damaged by the water jets, to thereby facilitate uniform impregnation of said woven material with resin.
Claim 10
Dependent Claim
21 words
A process according to claim 6, in which said pressure is in the range of 200 to 500 kg/cm 2 .
References Cited (Backward Citations)
US4145468A
Cited
US4146663A
Cited
US4251587A
Cited
US4476186A
Cited
US4548628A
Cited
US4647490A
Cited
US4741075A
Cited
US4612237A
Cited
US4967456A
Cited
US5136761A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-24 | 1997-07-26 | 1998-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-24 | 2001-07-26 | 2002-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-24 | 2005-07-26 | 2006-01-25 | $7700.00 | Window Closed / Lapsed |