Stress relief technique of removing oxide from surface of trench-patterned semiconductor-on-insulator structure
Assignee: Intersil Corp
•
Filing: 1992-09-01
•
Granted: 1993-12-14
•
Expires: 2012-09-01
Abstract
Abstract Creation of structural defects in a trench-isolated island structure is obviated by protecting the bottom of the trench pattern during etching of the hard mask surface oxide. A layer of photoresist is non-selectively deposited on the hard mask oxide layer and in the trench pattern, so that the photoresist buffer layer fills the trench pattern and is formed atop the hard mask oxide layer. The deposited photoresist is controllably flood-irradiated, so as to expose the irradiated photoresist down to a depth in the trench pattern that is at or somewhat deeper than the surface of the hard mask insulating material. The exposed photoresist is then developed, so as to remove the irradiated depth portion of the photoresist lying atop the hard mask oxide layer and partially extending into the trench, thus exposing the hard mask oxide layer, but leaving a sufficient quantity of unexposed photoresist in the trench pattern that provides a surface barrier for the underlying oxide. A wet etch is then non-selectively applied to the hard mask oxide layer, so as to completely remove the hard mask oxide layer from the top surface of the semiconductor islands. Because of the barrier in the bottom of the trench pattern, the oxide etch does not attack the underlying oxide. The undeveloped photoresist is then stripped. Thereafter, when the sidewalls of the trench pattern are oxidized and the trench pattern is filled with material, lattice dislocations are not formed in the islands.
Inventors
- 👤 Donald F. Hemmenway
- 👤 Stephen J. Gaul
- 👤 Chris A. McCarty
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:51
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10W; H10W10/00; H10W10/01; H10W10/041; H10W10/061; H10W10/10; H10W10/181; H10W10/40; H10P90/1914; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/949
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
263 words
A method of manufacturing a semiconductor-on-insulator structure comprising the steps of: (a) providing a support layer on which an insulator layer is formed and a semiconductor layer formed atop said insulator layer; (b) selectively forming a trench pattern-defining masking layer on a top surface of said semiconductor layer, said masking layer exposing a selected portion of said top surface of said semiconductor layer; (c) using the masking layer formed in step (b), removing material from said semiconductor layer exposed by said masking layer, so as to form a trench pattern in said semiconductor layer that extends from the top surface of said semiconductor layer down to said insulator layer, so that sidewalls of said trench pattern expose semiconductor material of said semiconductor layer and said insulator layer therebeneath; and (d) subjecting said masking layer to the application of a non-selective surface treatment agent so as to remove said masking layer from said semiconductor layer, said subjecting step comprising: (d1) the preliminary step of selectively forming, only in said trench pattern, buffer material that covers the insulator layer exposed by said trench pattern and protects said insulator layer against the action of said surface treatment agent, while leaving said masking layer on said top surface of said semiconductor layer, and thereafter, (d2) non-selectively applying said surface treatment agent to the structure resulting from step (d1), so that said surface treatment agent removes said masking material from the top surface of said patterned semiconductor layer, yet is prevented from attacking the bottom of said trench pattern because of the presence of said buffer material therein.
Claim 2
Independent Claim
263 words
A method of manufacturing a semiconductor-on-insulator structure comprising the steps of: (a) providing a support layer on which an insulator layer is formed and a semiconductor layer formed atop said insulator layer; (b) selectively forming a trench pattern-defining masking layer on a top surface of said semiconductor layer, said masking layer exposing a selected portion of said top surface of said semiconductor layer; (c) using the masking layer formed in step (b), removing material from said semiconductor layer exposed by said masking layer, so as to form a trench pattern in said semiconductor layer that extends from the top surface of said semiconductor layer down to said insulator layer, so that sidewalls of said trench pattern expose semiconductor material of said semiconductor layer and said insulator layer therebeneath; and (d) subjecting said masking layer to the application of a non-selective surface treatment agent so as to remove said masking layer from said semiconductor layer, said subjecting step comprising: (d1) the preliminary step of selectively forming, only in said trench pattern, buffer material that covers the insulator layer exposed by said trench pattern and protects said insulator layer against the action of said surface treatment agent, while leaving said masking layer on said top surface of said semiconductor layer, and thereafter, (d2) non-selectively applying said surface treatment agent to the structure resulting from step (d1), so that said surface treatment agent removes said masking material from the top surface of said patterned semiconductor layer, yet is prevented from attacking the bottom of said trench pattern because of the presence of said buffer material therein.
Claim 3
Dependent Claim
124 words
A method according to claim 1, wherein step (d1) comprises non-selectively depositing photoresist on said masking layer and in said trench pattern, so that said photoresist fills said trench pattern and is formed atop said masking layer, controllably irradiating the deposited photoresist so as to expose the irradiated photoresist down to a depth in said trench pattern deeper than the top surface of said semiconductor layer on which said masking layer has been formed but not the full depth of said trench, and developing the exposed photoresist, so as to remove that portion of said photoresist that lies atop said masking layer, thereby exposing said masking layer, but leaving unexposed photoresist in and covering the bottom of said trench pattern in said semiconductor layer.
Claim 4
Dependent Claim
59 words
A method according to claim 1, wherein step (d2) comprises non-selectively applying an etchant to the structure obtained by step (d1), said etchant etching said masking layer from the top surface of said semiconductor layer, while being prevented from attacking the bottom of said trench pattern in said semiconductor layer due to the presence of said unexposed photoresist thereon.
Claim 5
Dependent Claim
28 words
A method according to claim 3, further including the step of (e) removing the unexposed photoresist from the bottom of said trench pattern, thereby exposing said insulator layer.
Claim 6
Dependent Claim
29 words
A method according to claim 4, further including the step of (f) filling the trench pattern, from which unexposed photoresist has been removed in step (e), with conductive material.
Claim 7
Dependent Claim
90 words
A method according to claim 1, wherein step (d1) comprises (d1-1) non-selectively depositing buffer material on said insulator layer and in said trench pattern, so that said buffer material fills said trench pattern and is formed atop said masking layer, and (d1-2) controllably removing said buffer material down to a depth that extends into said trench pattern deeper than the top surface of said semiconductor layer, thereby exposing said masking layer, but leaving buffer material in said trench pattern covering the bottom of said trench pattern in said semiconductor layer.
Claim 8
Dependent Claim
20 words
A method according to claim 1, wherein each of said masking layer and said insulator layer comprises an oxide layer.
Claim 9
Independent Claim
386 words
A method of manufacturing a semiconductor-on-insulator structure comprising the steps of: (a) providing a support layer on which an insulator layer is formed and a semiconductor layer formed atop said insulator layer; (b) selectively forming a trench pattern-defining masking layer on a top surface of said semiconductor layer, said masking layer exposing a selected portion of said top surface of said semiconductor layer; (c) using the masking layer formed in step (b), removing material from said semiconductor layer exposed by said masking layer, so as to form a trench pattern in said semiconductor layer that extends from the top surface of said semiconductor layer down to said insulator layer, so that sidewalls of said trench pattern expose semiconductor material of said semiconductor layer and said insulator layer therebeneath; and (d) performing a masking layer-removal, trench fill process in such a manner as to fill said trench pattern with material capable of providing a conductive path through said trench pattern, while preventing the formation of stress-inducing, dislocation-type defects in the vicinity of the interface between sidewalls of said trench pattern in said semiconductor layer and said insulator layer therebeneath, said trench fill process performing step comprising the steps of (d1) subjecting said masking layer to the application of a non-selective surface treatment agent so as to remove said masking layer from said semiconductor layer, said subjecting step including the steps of (d1-1) the preliminary step of selectively forming, in said trench pattern, buffer material that covers the insulator layer exposed by said trench pattern and protects said insulator layer against the action of said surface treatment agent, and thereafter, (d1-2) non-selectively applying said surface treatment agent to the structure resulting from step (d1), so that said surface treatment agent removes said masking material from the top surface of said patterned semiconductor layer, yet is prevented from attacking the bottom of said trench pattern because of the presence of said buffer material therein, (d2) removing buffer material from the bottom of said trench pattern, (d3) forming dielectric material along sidewalls of said semiconductor layer exposed by the removal of said buffer material, and (d4) filling the remainder of said trench pattern with said material capable of providing a conductive path through said trench pattern that is insulated from said semiconductor layer by dielectric material formed in step (d3).
Claim 10
Independent Claim
386 words
A method of manufacturing a semiconductor-on-insulator structure comprising the steps of: (a) providing a support layer on which an insulator layer is formed and a semiconductor layer formed atop said insulator layer; (b) selectively forming a trench pattern-defining masking layer on a top surface of said semiconductor layer, said masking layer exposing a selected portion of said top surface of said semiconductor layer; (c) using the masking layer formed in step (b), removing material from said semiconductor layer exposed by said masking layer, so as to form a trench pattern in said semiconductor layer that extends from the top surface of said semiconductor layer down to said insulator layer, so that sidewalls of said trench pattern expose semiconductor material of said semiconductor layer and said insulator layer therebeneath; and (d) performing a masking layer-removal, trench fill process in such a manner as to fill said trench pattern with material capable of providing a conductive path through said trench pattern, while preventing the formation of stress-inducing, dislocation-type defects in the vicinity of the interface between sidewalls of said trench pattern in said semiconductor layer and said insulator layer therebeneath, said trench fill process performing step comprising the steps of (d1) subjecting said masking layer to the application of a non-selective surface treatment agent so as to remove said masking layer from said semiconductor layer, said subjecting step including the steps of (d1-1) the preliminary step of selectively forming, in said trench pattern, buffer material that covers the insulator layer exposed by said trench pattern and protects said insulator layer against the action of said surface treatment agent, and thereafter, (d1-2) non-selectively applying said surface treatment agent to the structure resulting from step (d1), so that said surface treatment agent removes said masking material from the top surface of said patterned semiconductor layer, yet is prevented from attacking the bottom of said trench pattern because of the presence of said buffer material therein, (d2) removing buffer material from the bottom of said trench pattern, (d3) forming dielectric material along sidewalls of said semiconductor layer exposed by the removal of said buffer material, and (d4) filling the remainder of said trench pattern with said material capable of providing a conductive path through said trench pattern that is insulated from said semiconductor layer by dielectric material formed in step (d3).
Claim 11
Dependent Claim
124 words
A method according to claim 8, wherein step (d1-1) comprises non-selectively depositing photoresist on said masking layer and in said trench pattern, so that said photoresist fills said trench pattern and is formed atop said masking layer, controllably irradiating the deposited photoresist so as to expose the irradiated photoresist down to a depth in said trench pattern deeper than the top surface of said semiconductor layer on which said masking layer has been formed but not the full depth of said trench, and developing the exposed photoresist, so as to remove that portion of said photoresist that lies atop said masking layer, thereby exposing said masking layer, but leaving unexposed photoresist in and covering the bottom of said trench pattern in said semiconductor layer.
Claim 12
Dependent Claim
58 words
A method according to claim 8, wherein step (d1-2) comprises non-selectively applying an etchant to the structure obtained by step (d1-1), said etchant said masking layer from the top surface of said semiconductor layer, while being prevented from attacking the bottom of said trench pattern in said semiconductor layer due to the presence of said unexposed photoresist thereon.
Claim 13
Dependent Claim
88 words
A method according to claim 10, wherein step (d1-1) comprises non-selectively depositing buffer material on said insulator layer and in said trench pattern, so that said buffer material fills said trench pattern and is formed atop said masking layer, and controllably removing said buffer material down to a depth that extends into said trench pattern deeper than the top surface of said semiconductor layer, thereby exposing said masking layer, but leaving buffer material in said trench pattern covering the bottom of said trench pattern in said semiconductor layer.
Claim 14
Dependent Claim
20 words
A method according to claim 8, wherein each of said masking layer and said insulator layer comprises an oxide layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-12-13 | 1997-06-14 | 1997-12-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-12-13 | 2001-06-14 | 2001-12-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-12-13 | 2005-06-14 | 2005-12-14 | $7700.00 | Window Closed / Lapsed |