Method of forming water-repellent metal oxide film coated on glass substrate
Assignee: Nissan Motor Co Ltd
•
Filing: 1992-06-02
•
Granted: 1993-11-30
•
Expires: 2012-06-02
Abstract
Abstract The disclosure relates to a metal oxide film formed on a glass substrate by a sol-gel method using a solution of at least one metal alkoxide or acetylacetonate. Water which is in the amount ranging from 50 to 400 mol % of the at least one metal alkoxide or acetylacetonate, an organic solvent and a catalyst are added to the solution, thereby to form a first sol. To afford water repellency to the oxide film, a fluoroalkylsilane in the amount more than 0.30 mol % of and less than 3.0 mol % of the at least one metal alkoxide or acetylacetonate, or an alkylsilane compound in the amount more than 4.0 mol % of and less than 20 mol % of the at least one metal alkoxide or acetylacetonate, is added to the first sol, thereby forming a second sol. The concentration of the at least one metal alkoxide or acetylacetonate in the second sol is adjusted to fall within the range from 0.005 to 3.0 mol %. The second sol is applied to the glass substrate to form a gel film. The gel film is heated at a temperature not lower than 100° C. The obtained oxide film is superior in durability of water repellency.
Inventors
- 👤 Ryuzo Uemura
- 👤 Toshikazu Nishide
- 👤 Ichiro Nakamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:35
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/229; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/113
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
181 words
A method of forming a water-repellent metal oxide film on a glass substrate, the method comprising the steps of: (i) mixing a first solution of at least one metal oxide precursor selected from the group consisting of metal alkoxides and metal acetylacetonates with an organic solvent; and about 50 to 400 mol %, based on said metal oxide precursor, or water; thereby forming a first sol through hydrolysis and polycondensation of said metal oxide precursor; (ii) adding to said first solution at least one water-repellency agent selected from the group consisting of: about 0.30-3.0 mol % based on said metal oxide precursor of at least one fluoroalkylsilane compound, and about 4.0-20 mol % based on said metal oxide precursor of a n alkysilane compound to form a second sol; wherein the concentration of said metal oxide precursor in said second sol is therefore adjusted to about 0.005-3.0 mol %; (iii) applying said second sol to a glass substrate to form a gel film on the glass substrate; and (iv) heating said gel film at a temperature greater than about 100° C.
Claim 2
Independent Claim
181 words
A method of forming a water-repellent metal oxide film on a glass substrate, the method comprising the steps of: (i) mixing a first solution of at least one metal oxide precursor selected from the group consisting of metal alkoxides and metal acetylacetonates with an organic solvent; and about 50 to 400 mol %, based on said metal oxide precursor, or water; thereby forming a first sol through hydrolysis and polycondensation of said metal oxide precursor; (ii) adding to said first solution at least one water-repellency agent selected from the group consisting of: about 0.30-3.0 mol % based on said metal oxide precursor of at least one fluoroalkylsilane compound, and about 4.0-20 mol % based on said metal oxide precursor of a n alkysilane compound to form a second sol; wherein the concentration of said metal oxide precursor in said second sol is therefore adjusted to about 0.005-3.0 mol %; (iii) applying said second sol to a glass substrate to form a gel film on the glass substrate; and (iv) heating said gel film at a temperature greater than about 100° C.
Claim 3
Dependent Claim
39 words
A method according to claim 1, wherein said metal oxide precursor is selected from the group consisting of alkoxides of Si, Ti, Al, Zr, W, Ce, and Sn and acetylacetonatos of Si, Ti, Al, Zr, W, Ce, and Sn.
Claim 4
Dependent Claim
14 words
A method according to claim 2, wherein said metal alkoxide comprises a silicon alkoxide.
Claim 5
Dependent Claim
28 words
A method according to claim 1, wherein a catalyst is added to said first solution to increase the rate of hydrolysis and polycondensation of said metal oxide precursor.
Claim 6
Dependent Claim
13 words
A method according to claim 4, wherein said catalyst comprises an acid compound.
Claim 7
Dependent Claim
31 words
A method according to claim 5, wherein said acid compound is at least one selected from the group consisting of hydrochloric acid, hydrofluoric acid, nitric acid, acetic acid and formic acid.
Claim 8
Dependent Claim
13 words
A method according to claim 6, wherein said acid compound comprises nitric acid.
Claim 9
Dependent Claim
29 words
A method according to claim 1, wherein each of said metal alkoxides comprises an alkyl group selected from the group consisting of methyl, ethyl, isopropyl, propyl and butyl groups.
Claim 10
Dependent Claim
26 words
A method according to claim 1, wherein a ligand is added to said first solution to adjust the rate of hydrolysis of said metal oxide precursor.
Claim 11
Dependent Claim
24 words
A method according to claim 9, wherein said ligand is selected from the group consisting of a diketone, an alcohol ether and a glycol.
Claim 12
Dependent Claim
22 words
A method according to claim 10, wherein said glycol is selected from the group consisting of hexylene glycol, 2,3-butanediol, 1,2-propandiol, and 2-methyl-1,2-propanediol.
Claim 13
Dependent Claim
114 words
A method according to claim 1, wherein said fluoroalkylsilane compound is selected from the group consisting of CF 3 CH 2 CH 2 Si(Me) 3 , CF 3 CH 2 CH 2 SiCl 3 , CF 3 (CF 2 ) 5 CH 2 CH 2 SiCl 3 , CF 3 (CF 2 ) 5 CH 2 CH 2 Si(OMe) 3 , CF 3 (CF 2 ) 7 CH 2 CH 2 SiCl 3 , CF 3 (CF 2 ) 7 CH 2 CH 2 Si(OMe) 3 , CF 3 (CF 2 ) 7 CH 2 CH 2 SiMeCl 2 , and CF 3 (CF 2 ) 7 CH 2 CH 2 SiMe(OMe) 2 .
Claim 14
Dependent Claim
165 words
A method according to claim 1, wherein said alkylsilane compound is selected from the group consisting of SiC 6 H 15 Cl, SiC 3 H 8 Cl 2 , SiC 4 H 9 Cl 3 , SiC 4 H 10 Cl 2 , SiC 12 H 10 Cl 2 , SiC 16 H 20 O 2 , SiC 14 H 16 O 2 , SiC 9 H 22 O 3 , SiC 7 H 18 O 3 , SiC 4 H 12 O 3 , SiC 13 H 13 Cl, SiC 7 H 8 Cl2, SiC 20 H 43 Cl, SiC 19 H 40 Cl, SiC 21 H 46 O 2 , SiC 18 H 37 Cl 3 , SiC 24 H 52 O 3 , SiC 21 H 46 O 3 , SiC 6 H 15 Cl 3 , SiC 12 H 20 O 3 , SiC 9 H 14 O 3 , SiC 18 H 15 Cl and SiC 9 H 21 Cl.
Claim 15
Dependent Claim
24 words
A method according to claim 1, wherein said organic solvent is selected from the group consisting of a lower alcohol and an aromatic hydrocarbon.
Claim 16
Dependent Claim
12 words
A method according to claim 14, wherein said organic solvent comprises ethanol.
Claim 17
Dependent Claim
28 words
A method according to claim 1, wherein said fluoroalkylsilane compound is added and the gel film is heated at a temperature ranging from about 300° to 420° C.
Claim 18
Dependent Claim
27 words
A method according to claim 1, wherein said alkylsilane is added and the gel film is heated at a temperature ranging from about 150° to 170° C.
References Cited (Backward Citations)
US4125673A
Cited
US4596745A
Cited
US4830879A
Cited
JPS6468477A
Cited
JPH01126244A
Cited
US5137749A
Cited
US4997684A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-29 | 1997-05-31 | 1997-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-29 | 2001-05-31 | 2001-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-29 | 2005-05-31 | 2005-11-30 | $7700.00 | Window Closed / Lapsed |