Dry etching method
Assignee: Sony Corp
•
Filing: 1991-10-03
•
Granted: 1993-11-30
•
Expires: 2011-10-03
Abstract
Abstract There is provided a method for anisotropic etching of a fine resist pattern at a practically useful etching rate wherein micro-loading effects are suppressed. If a resist layer is etched using an NH 3 /N 2 gas mixture, while the temperature of a sample wafer is controlled to be not higher than 50° C., a reaction product containing at least N, C and O is produced. The micro-loading effects are suppressed because deposition and sputtering of the reaction product occur competitively on the wafer surface. Since etching of the ion mode is accelerated by N 2 , the etching rate as well as anisotropy is improved. There ia also provided a method of supplying sulfur to a NH 3 -containing etching reaction system and utilizing the yielded ammonium sulfide for sidewall protection for further improving anisotropy. In more detail, sulfur is introduced by ion implantation into an area to be etched, at least the surface of a member of an apparatus provided in the vicinity of the sample wafer is formed of a sulfur-based material, or a sulfur compound such as H 2 S is added to an etching gas. Sulfur is supplied into the reaction system by sputtering with the first two methods, and by decomposition of the sulfur compound in the gaseous phase with the latter method.
Inventors
- 👤 Shingo Kadomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 08:04
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; G03F7/36; H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287; H10P50/71; H10P76/00; H10P76/20; H10P76/204; H10P76/2041
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
61 words
A dry etching method comprising the steps of providing a substrate having a layer of resist material formed thereon, etching the layer of resist material in a plasma by providing sulfur and by using an etching gas consisting of NH 3 and N 2 and controlling the temperature of the substrate to be etched to be not higher than 50° C.
Claim 2
Dependent Claim
61 words
A dry etching method comprising the steps of providing a substrate having a layer of resist material formed thereon, etching the layer of resist material in a plasma by providing sulfur and by using an etching gas consisting of NH 3 and N 2 and controlling the temperature of the substrate to be etched to be not higher than 50° C.
Claim 3
Dependent Claim
31 words
A dry etching method according to claim 1, wherein the step of providing sulfur is by ion implanting sulfur into an area of the layer of resist material prior to etching.
Claim 4
Dependent Claim
43 words
A dry etching method according to claim 1, wherein the step of providing sulfur is by arranging, prior to etching, an internal member having at least a surface being formed of a sulfur-containing material in the vicinity of the substrate to be etched.
Claim 5
Dependent Claim
22 words
A dry etching method according to claim 1, wherein the step of providing sulfur provides a sulfur gas in the etching gas.
Claim 6
Dependent Claim
23 words
A dry etching method according to claim 4, wherein the sulfur gas is at least one of H 2 S and carbon sulfide.
Claim 7
Dependent Claim
62 words
A dry etching method comprising the steps of providing a substrate having a layer of resist material in a plasma to be etched, etching the layer of resist material utilizing a gas containing NH 3 and a sulfur compound selected from the group consisting of carbon sulfide and H 2 S and controlling the temperature of the substrate to be ≦50° C.
Claim 8
Dependent Claim
62 words
A dry etching method comprising the steps of providing a substrate having a layer of resist material in a plasma to be etched, etching the layer of resist material utilizing a gas containing NH 3 and a sulfur compound selected from the group consisting of carbon sulfide and H 2 S and controlling the temperature of the substrate to be ≦50° C.
Claim 9
Dependent Claim
57 words
A dry etching method according to claim 3, wherein said sulfur-containing material is one of materials selected from the group consisting of a sulfur nitride polymer layer, a ceramic material having sulfur sintered to its surface, a material produced on sintering a mixture of ceramic powders and sulfur powders and a material obtained by bonding sulfur plates.
Claim 10
Dependent Claim
36 words
A dry etching method according to claim 3, wherein said internal member is at least one selected from a group of members consisting of a wafer clamp, a cathode cover, a wafer cover and a susceptor.
Claim 11
Dependent Claim
52 words
A dry etching method comprising the steps of providing a substrate with a layer of resist material to be etched, ion implanting sulfur into an area of the layer of resist material and then etching the resist material containing the sulfur in a plasma using an etching gas containing NH 3 .
Claim 12
Dependent Claim
52 words
A dry etching method comprising the steps of providing a substrate with a layer of resist material to be etched, ion implanting sulfur into an area of the layer of resist material and then etching the resist material containing the sulfur in a plasma using an etching gas containing NH 3 .
Claim 13
Dependent Claim
63 words
A dry etching method comprising the steps of providing a substrate having a layer of resist material to be etched, arranging an internal member having at least a surface being formed of a sulfur-containing material in the vicinity of the substrate to be etched, and then etching the layer of resist material in a plasma using an etching gas containing NH 3 .
Claim 14
Dependent Claim
63 words
A dry etching method comprising the steps of providing a substrate having a layer of resist material to be etched, arranging an internal member having at least a surface being formed of a sulfur-containing material in the vicinity of the substrate to be etched, and then etching the layer of resist material in a plasma using an etching gas containing NH 3 .
Claim 15
Dependent Claim
60 words
The dry etching method as claimed in claim 10 characterized in that said sulfur-containing material is one of materials selected from the group consisting of a sulfur nitride polymer layer, a ceramic material having sulfur sintered to its surface. a material produced on sintering a mixture of ceramic powders and sulfur powders and a material obtained by bonding sulfur plates.
Claim 16
Dependent Claim
38 words
The dry etching method according to claim 10 characterized in that said internal member is at least one of members selected from the group consisting of a wafer clamp, a cathode cover, a wafer cover and a susceptor.
References Cited (Backward Citations)
JPS5887824A
Cited
EP0151408A2
Cited
JPS60170238A
Cited
JPS61220432A
Cited
JPS61220433A
Cited
JPS63216346A
Cited
US4992136A
Cited
JPH01186622A
Cited
JPH01280316A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-29 | 1997-05-31 | 1997-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-29 | 2001-05-31 | 2001-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-29 | 2005-05-31 | 2005-11-30 | $7700.00 | Window Closed / Lapsed |