Lithium rechargeable battery and method of making the same
Assignee: Panasonic Holdings Corp
•
Filing: 1992-06-26
•
Granted: 1993-11-02
•
Expires: 2012-06-26
Abstract
Abstract The subject invention is a lithium battery comprising a positive electrode mainly of vanadium pentoxide, a negative electrode mainly of lithium doped niobium pentoxide, and, an electrolyte mainly of an anhydrous solvent with dissolved lithium salt. By using for the said niobium pentoxide a mixture of T type and H type crystals heat treated at 850 DEG to 1300 DEG C., preferably 850 DEG to 1100 DEG C., a lithium battery having superior charging cycle characteristics and also having high discharge voltage is obtained.
Inventors
- 👤 Kenichi Takata
- 👤 Nobuharu Koshiba
- 👤 Atsushi Ohtsuka
- 👤 Tatsuo Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:41
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/485; H01M10/00; H01M10/05; H01M10/052; H01M10/0525; H01M4/13; H01M4/131; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
89 words
A lithium rechargeable battery, in its charged state and comprising a positive electrode, a negative electrode consisting primarily of lithium doped niobium pentoxide and an electrolyte consisting primarily of an anhydrous solvent with dissolved lithium salt, wherein said negative electrode has X-ray diffraction image peak valves corresponding to niobium pentoxide crystals, when using copper (Cu) as the target of at least 3.74 Å, 3.64 Å and 3.48 Å (respectively ±0.05 Å); and where the strength ratio of the said X-ray diffraction image peak values are 3.74 Å:3.64 Å:3.48 Å=90±20:100:90±20.
Claim 2
Dependent Claim
89 words
A lithium rechargeable battery, in its charged state and comprising a positive electrode, a negative electrode consisting primarily of lithium doped niobium pentoxide and an electrolyte consisting primarily of an anhydrous solvent with dissolved lithium salt, wherein said negative electrode has X-ray diffraction image peak valves corresponding to niobium pentoxide crystals, when using copper (Cu) as the target of at least 3.74 Å, 3.64 Å and 3.48 Å (respectively ±0.05 Å); and where the strength ratio of the said X-ray diffraction image peak values are 3.74 Å:3.64 Å:3.48 Å=90±20:100:90±20.
Claim 3
Dependent Claim
35 words
A lithium rechargeable battery in claim 1, wherein the positive electrode is composed primarily of one of a group of vanadium pentoxide, manganese dioxide containing lithium, cobalt dioxide containing lithium, and nickel oxide containing lithium.
Claim 4
Dependent Claim
91 words
A lithium rechargeable battery, in its charged state and comprising a positive electrode, a negative electrode consisting primarily of lithium doped niobium pentoxide and an electrolyte consisting primarily of an anhydrous solvent with dissolved lithium salt, wherein said negative electrode has X-ray diffraction image peak values, when using copper (Cu) as the target, corresponding to niobium pentoxide crystals, of at least 3.93 Å, 3.74 Å, 3.64 Å, 3.48 Å, 3.15 Å, 3.09 Å and 2.46 Å (each ±0.05), and peak values of the X-ray diffraction images in the ratio of ##EQU1##
Claim 5
Dependent Claim
91 words
A lithium rechargeable battery, in its charged state and comprising a positive electrode, a negative electrode consisting primarily of lithium doped niobium pentoxide and an electrolyte consisting primarily of an anhydrous solvent with dissolved lithium salt, wherein said negative electrode has X-ray diffraction image peak values, when using copper (Cu) as the target, corresponding to niobium pentoxide crystals, of at least 3.93 Å, 3.74 Å, 3.64 Å, 3.48 Å, 3.15 Å, 3.09 Å and 2.46 Å (each ±0.05), and peak values of the X-ray diffraction images in the ratio of ##EQU1##
Claim 6
Dependent Claim
36 words
A lithium rechargeable battery in claim 3, wherein the positive electrode is comprised mainly of one of a group consisting of vanadium pentoxide, manganese dioxide containing lithium, cobalt dioxide containing lithium, and, nickel oxide containing lithium.
Claim 7
Dependent Claim
64 words
Method of making a lithium rechargeable battery consisting, in the charged state; and a positive electrode, a negative electrode composed mainly of lithium doped niobium pentoxide and an electrolyte composed mainly of anhydrous solvent with dissolved lithium salt, wherein said niobium pentoxide is heat treated for roughly 3 hours at a temperature from 1150° C. to 1300° C. prior to assembly into said battery.
Claim 8
Dependent Claim
64 words
Method of making a lithium rechargeable battery consisting, in the charged state; and a positive electrode, a negative electrode composed mainly of lithium doped niobium pentoxide and an electrolyte composed mainly of anhydrous solvent with dissolved lithium salt, wherein said niobium pentoxide is heat treated for roughly 3 hours at a temperature from 1150° C. to 1300° C. prior to assembly into said battery.
Claim 9
Dependent Claim
64 words
Method of making a lithium rechargeable battery consisting, in the charged state, of a positive electrode, a negative electrode consisting mainly of lithium doped niobium pentoxide and an electrolyte composed mainly of anhydrous solvent with dissolved lithium salt, wherein said niobium pentoxide is heat treated for roughly 3 hours at a temperature from 850° C. to 1100° C. prior to assembly into said battery.
Claim 10
Dependent Claim
64 words
Method of making a lithium rechargeable battery consisting, in the charged state, of a positive electrode, a negative electrode consisting mainly of lithium doped niobium pentoxide and an electrolyte composed mainly of anhydrous solvent with dissolved lithium salt, wherein said niobium pentoxide is heat treated for roughly 3 hours at a temperature from 850° C. to 1100° C. prior to assembly into said battery.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-01 | 1997-05-03 | 1997-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-01 | 2001-05-03 | 2001-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-01 | 2005-05-03 | 2005-11-02 | $7700.00 | Window Closed / Lapsed |