Assignee: Avago Technologies International Sales Pte Ltd
•
Filing: 1991-06-12
•
Granted: 1993-10-26
•
Expires: 2011-06-12
Abstract
Abstract The present invention comprises a method of fabricating devices and circuits employing at least one heteroepitaxial layer under strain. The thickness of the heteroepitaxial layer is more than two times the calculated equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, based on previously known equilibrium theory for the uncapped layer. Subsequent to growth of the heteroepitaxial layer, the structure is processed at temperatures higher than the growth temperature of the heteroepitaxial layer. The strained heteroepitaxial layer (second layer) is epitaxially grown upon the surface of a first, underlaying crystalline layer, creating a heterojunction. Subsequently a third crystalline layer is deposited or grown upon the major exposed surface of the second, strained heteroepitaxial layer. The preferred manner of growth of the third crystalline layer is epitaxial growth. The composition of the third crystalline layer must be such that upon deposition or growth, the third layer substantially continuously binds to the heteroepitaxial structure of the second layer. Subsequent to growth of the at least three layer structure, the structure is processed at temperatures in excess of the growth temperature of the second heteroepitaxial layer. Presence of the third crystalline layer prevents the generation of a substantial amount of misfit dislocations between the first crystalline layer substrate and the second heteroepitaxial layer.
Inventors
- 👤 Stephen Laderman
- 👤 Martin Scott
- 👤 Theodore I. Kamins
- 👤 Judy L. Hoyt
- 👤 Clifford A. King
- 👤 James F. Gibbons
- 👤 David B. Noble
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:35
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/22; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/32; H10P14/3202; H10P14/3204; H10P14/3211; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; Y; Y10; Y10S; Y10S148/00; Y10S148/015; Y10S438/00; Y10S438/902; Y10S438/938
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
241 words
A method of fabricating a device having at least one heteroepitaxial layer under strain, wherein processing of the device subsequent to growth of the heteroepitaxial layer is done at temperatures higher than the growth temperature of said heteroepitaxial layer and wherein the thickness of the strained heteroepitaxial layer is more than two times the equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, calculated from equilibrium theory for the uncapped layer, the method comprising the steps of: (a) providing a first crystalline substrate layer that comprises silicon; (b) forming a second heteroepitaxial layer upon the surface of the first crystalline layer, where the second layer is comprised of a material selected from the group consisting of silicon-germanium, gallium-arsenide, germaniumtin, indium-phosphide and indium-antimonide; (c) providing the second layer with oxygen atoms of concentration approximately 10 20 cm -3 ; (d) forming a thin third crystalline layer, which comprises silicon, upon the surface of the second heteroepitaxial layer so that the third layer substantially continuously binds to the crystal structure of the second heteroepitaxial layer while the second heteroepitaxial layer remains under strain; and (e) subsequently processing the resultant structure at temperatures higher than the growth temperature of the second heteroepitaxial layer; whereby the presence of the third crystalline layer prevents substantial formation of misfit dislocations at the interface between the first crystalline layer and the second heteroepitaxial layer which would occur in the absence of the third crystalline layer.
Claim 2
Independent Claim
241 words
A method of fabricating a device having at least one heteroepitaxial layer under strain, wherein processing of the device subsequent to growth of the heteroepitaxial layer is done at temperatures higher than the growth temperature of said heteroepitaxial layer and wherein the thickness of the strained heteroepitaxial layer is more than two times the equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, calculated from equilibrium theory for the uncapped layer, the method comprising the steps of: (a) providing a first crystalline substrate layer that comprises silicon; (b) forming a second heteroepitaxial layer upon the surface of the first crystalline layer, where the second layer is comprised of a material selected from the group consisting of silicon-germanium, gallium-arsenide, germaniumtin, indium-phosphide and indium-antimonide; (c) providing the second layer with oxygen atoms of concentration approximately 10 20 cm -3 ; (d) forming a thin third crystalline layer, which comprises silicon, upon the surface of the second heteroepitaxial layer so that the third layer substantially continuously binds to the crystal structure of the second heteroepitaxial layer while the second heteroepitaxial layer remains under strain; and (e) subsequently processing the resultant structure at temperatures higher than the growth temperature of the second heteroepitaxial layer; whereby the presence of the third crystalline layer prevents substantial formation of misfit dislocations at the interface between the first crystalline layer and the second heteroepitaxial layer which would occur in the absence of the third crystalline layer.
Claim 3
Dependent Claim
33 words
The method of claim 1, wherein said second heteroepitaxial layer is a silicon-germanium heteroepitaxial layer, and the germanium concentration in said silicon-germanium heteroepitaxial layer ranges from about 6 percent to about 50 percent.
Claim 4
Dependent Claim
23 words
The method of claim 2, wherein said germanium concentration in said silicon-germanium heteroepitaxial layer ranges from about 12 percent to about 35 percent.
Claim 5
Dependent Claim
27 words
The method of claim 2, wherein the thickness of said second heteroepitaxial layer is at least four times said calculated critical thickness of said uncapped heteroepitaxial layer.
Claim 6
Dependent Claim
22 words
The method of claim 2 wherein said step of subsequently processing (e) is accomplished at a temperature of at least 850° C.
Claim 7
Dependent Claim
22 words
The method of claim 5 wherein said step of subsequently processing (e) is accomplished at a temperature of at least 900° C.
Claim 8
Dependent Claim
22 words
The method of claim 6 wherein said step of subsequently processing (e) is accomplished at a temperature of at least 1,000° C.
Claim 9
Dependent Claim
13 words
The method of claim 1, wherein said third crystalline layer is epitaxially grown.
Claim 10
Dependent Claim
23 words
The method of claim 1, further comprising the step of providing said third crystalline layer with a thickness of at least 200 Å.
Claim 11
Dependent Claim
36 words
The method of claim 1, wherein said second heteroepitaxial layer has a thickness that is at least four times said calculated critical thickness of said uncapped heteroepitaxial layer, and said third crystalline layer is epitaxially grown.
Claim 12
Independent Claim
214 words
A method of fabricating a device having at least one heteroepitaxial layer under strain, wherein processing of the device subsequent to growth of the heteroepitaxial layer is done at temperatures higher than the growth temperature of said heteroepitaxial layer and wherein the thickness of the strained heteroepitaxial layer is more than two times the equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, calculated from equilibrium theory for the uncapped layer, the method comprising the steps of: (a) providing a first crystalline substrate layer; (b) forming a second heteroepitaxial layer, containing a silicon-germanium material with a concentration of oxygen atoms of approximately 10 20 cm -3 , upon the surface of the first crystalline layer; (c) forming a third crystalline layer upon the surface of the second heteroepitaxial layer so that the third layer substantially continuously binds to the crystal structure of the second heteroepitaxial layer while the second heteroepitaxial layer remains under strain; and (d) subsequently processing the resultant structure at temperatures higher than the growth temperature of the second heteroepitaxial layer; whereby the presence of the third crystalline layer prevents substantial formation of misfit dislocations at the interface between the first crystalline layer and the second heteroepitaxial layer which would occur in the absence of the third crystalline layer.
Claim 13
Independent Claim
214 words
A method of fabricating a device having at least one heteroepitaxial layer under strain, wherein processing of the device subsequent to growth of the heteroepitaxial layer is done at temperatures higher than the growth temperature of said heteroepitaxial layer and wherein the thickness of the strained heteroepitaxial layer is more than two times the equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, calculated from equilibrium theory for the uncapped layer, the method comprising the steps of: (a) providing a first crystalline substrate layer; (b) forming a second heteroepitaxial layer, containing a silicon-germanium material with a concentration of oxygen atoms of approximately 10 20 cm -3 , upon the surface of the first crystalline layer; (c) forming a third crystalline layer upon the surface of the second heteroepitaxial layer so that the third layer substantially continuously binds to the crystal structure of the second heteroepitaxial layer while the second heteroepitaxial layer remains under strain; and (d) subsequently processing the resultant structure at temperatures higher than the growth temperature of the second heteroepitaxial layer; whereby the presence of the third crystalline layer prevents substantial formation of misfit dislocations at the interface between the first crystalline layer and the second heteroepitaxial layer which would occur in the absence of the third crystalline layer.
Claim 14
Dependent Claim
29 words
The method of claim 11, further comprising the step of choosing the material of at least one of said first crystalline layer and said third crystalline layer as silicon.
Claim 15
Dependent Claim
29 words
The method of claim 11, further comprising the step of choosing the concentration of said germanium in said second heteroepitaxial layer in the range 6 percent to 50 percent.
Claim 16
Dependent Claim
22 words
The method of claim 13 wherein said step of subsequently processing (d) is accomplished at a temperature of at least 850° C.
Claim 17
Dependent Claim
22 words
The method of claim 13 wherein said step of subsequently processing (d) is accomplished at a temperature of at least 1,000° C.
Claim 18
Dependent Claim
19 words
The method of claim 11, further comprising the step of forming said third crystalline layer as an epitaxial layer.
Claim 19
Dependent Claim
42 words
The method of claim 16 further comprising the steps of: forming said second heteroepitaxial layer at a second layer growth temperature; and forming said third crystalline layer at a third layer growth temperature that is higher than the second layer growth temperature.
Claim 20
Independent Claim
201 words
A method of fabricating a device having at least one heteroepitaxial layer under strain, wherein processing of the device subsequent to growth of the heteroepitaxial layer is done at temperatures higher than the growth temperature of said heteroepitaxial layer and wherein the thickness of the strained heteropitaxial layer is more than two times the equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, calculated from equilibrium theory for the uncapped layer, the method comprising the steps of: (a) providing a first crystalline substrate layer; (b) forming a second heteroepitaxial layer upon the surface of the first crystalline layer by an LRP technique; (c) forming a third crystalline layer upon the surface of the second heteroepitaxial layer so that the third layer substantially continously binds to the crystal structure of the second heteropitaxial layer while the second heteroepitaxial layer remains under strain; and (d) subsequently processing the resultant structure at temperatures higher than the growth temperature of the second heteroepitaxial layer; whereby the presence of the third crystalline layer prevents substantial formation of misfit dislocations at the interface between the first crystalline layer and the second heteroepitaxial layer which would occur in the absence of the third crystalline layer.
Claim 21
Independent Claim
201 words
A method of fabricating a device having at least one heteroepitaxial layer under strain, wherein processing of the device subsequent to growth of the heteroepitaxial layer is done at temperatures higher than the growth temperature of said heteroepitaxial layer and wherein the thickness of the strained heteropitaxial layer is more than two times the equilibrium critical thickness for an uncapped heteroepitaxial layer upon a crystalline substrate, calculated from equilibrium theory for the uncapped layer, the method comprising the steps of: (a) providing a first crystalline substrate layer; (b) forming a second heteroepitaxial layer upon the surface of the first crystalline layer by an LRP technique; (c) forming a third crystalline layer upon the surface of the second heteroepitaxial layer so that the third layer substantially continously binds to the crystal structure of the second heteropitaxial layer while the second heteroepitaxial layer remains under strain; and (d) subsequently processing the resultant structure at temperatures higher than the growth temperature of the second heteroepitaxial layer; whereby the presence of the third crystalline layer prevents substantial formation of misfit dislocations at the interface between the first crystalline layer and the second heteroepitaxial layer which would occur in the absence of the third crystalline layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-10-25 | 1997-04-26 | 1997-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-10-25 | 2001-04-26 | 2001-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-10-25 | 2005-04-26 | 2005-10-26 | $7700.00 | Window Closed / Lapsed |