Method of manufacturing ferrite crystals
Assignee: NGK Insulators Ltd
•
Filing: 1990-04-30
•
Granted: 1993-10-26
•
Expires: 2010-04-30
Abstract
Abstract A method of manufacturing ferrite crystals such as single crystal bodies and polycrystal bodies with garnet structure is disclosed, which includes the steps of effecting a composition controlling for raw powders, forming raw powders, sintering formed bodies and effecting hot isostatic press treatment for sintered bodies. Also, a method of producing ferrite powders preferably used for the ferrite crystal manufacturing method mentioned above. The thus obtained ferrite crystal bodies with garnet structure show good magnetooptical properties such as light transmissivity, Faraday rotation angle and Verdet constant, and are preferably used for magnetooptical elements such as optical isolators and optical magnetic field sensors etc.
Inventors
- 👤 Minoru Imaeda
- 👤 Emi Asai
- 👤 Katsunori Okamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:19
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/34; H01F1/342; H01F1/344; H01F1/346; C; C01; C01G; C01G49/00; C01G49/0018; C01G49/0036; C01G49/0054; C04; C04B; C04B35/00; C04B35/01; C04B35/26; C04B35/622; C04B35/64; C04B35/645; C04B35/6455; C01P; C01P2002/00; C01P2002/30; C01P2002/50; C01P2004/00; C01P2004/51; C01P2004/52; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/42; C01P2006/60
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
119 words
A method of manufacturing ferrite crystals with garnet structure, comprising the steps of: preparing first and second ferrite powders each having garnet structure, said powders having components, the molar percentages of which are higher and lower, respectively, than a target composition; mixing said first and second ferrite powders at a predetermined ratio to obtain a composition controlled ferrite powder such that the components of the composition controlled ferrite powder have molar percentages which are within 0.1 mol % of the target composition; forming said composition controlled ferrite powder to obtain a formed body; sintering said formed body to obtain a sintered body; and subjecting said sintered body to a hot isostatic pressing treatment to obtain a ferrite polycrystal body.
Claim 2
Independent Claim
119 words
A method of manufacturing ferrite crystals with garnet structure, comprising the steps of: preparing first and second ferrite powders each having garnet structure, said powders having components, the molar percentages of which are higher and lower, respectively, than a target composition; mixing said first and second ferrite powders at a predetermined ratio to obtain a composition controlled ferrite powder such that the components of the composition controlled ferrite powder have molar percentages which are within 0.1 mol % of the target composition; forming said composition controlled ferrite powder to obtain a formed body; sintering said formed body to obtain a sintered body; and subjecting said sintered body to a hot isostatic pressing treatment to obtain a ferrite polycrystal body.
Claim 3
Dependent Claim
58 words
The method of claim 1, wherein said ferrite powders are manufactured by preparing mixed solutions containing at least ferrous ion and yttrium ion or rare earth metal ion, coprecipitating hydroxides with the aid of base from the mixed solution, synthesizing the coprecipitated compounds by oxidizing ferrous ion int ferric ion, and separating, drying and calcining the coprecipitated compounds.
Claim 4
Dependent Claim
47 words
The method of claim 1 wherein said ferrite powders are manufactured by preparing mixed solutions containing at least ferric nitrate and nitrate of yttrium or rare earth metal, dropping the mixed solution into a base solution to coprecipitate hydroxides, and separating, drying and calcining the coprecipitated compounds.
Claim 5
Dependent Claim
30 words
The method of claim 1 further comprising the steps of connecting a mother ferrite single crystal to said ferrite polycrystal body; and growing single crystal into said ferrite polycrystal body.
Claim 6
Dependent Claim
51 words
A method according to claim 4, wherein with respect to said single crystal growing step is effected a heat-treatment at 800˜1600° C. under oxygen atmosphere in a normal pressure, a normal HIP treatment under Ar atmosphere in 100˜2000 atm, and an oxygen HIP treatment under 0.1˜20% oxygen atmosphere in 100˜2000 atm.
Claim 7
Dependent Claim
23 words
The method of claim 1, wherein said hot isostatic pressing treatment is effected under ambient gases including an oxygen component greater than 0.1%.
Claim 8
Independent Claim
119 words
A method of manufacturing ferrite crystals with garnet structure, comprising the steps of: preparing first and second ferrite powders each having garnet structure, said powders having components, the molar percentages of which are higher and lower, respectively, than a target composition; mixing said first and second ferrite powders at a predetermined ratio to obtain a composition controlled ferrite powder such that the components of the composition controlled ferrite powder have molar percentages which are within 0.05 mol % of the target composition; forming said composition controlled ferrite powder to obtain a formed body; sintering said formed body to obtain a sintered body; and subjecting said sintered body to a hot isostatic pressing treatment to obtain a ferrite polycrystal body.
Claim 9
Independent Claim
119 words
A method of manufacturing ferrite crystals with garnet structure, comprising the steps of: preparing first and second ferrite powders each having garnet structure, said powders having components, the molar percentages of which are higher and lower, respectively, than a target composition; mixing said first and second ferrite powders at a predetermined ratio to obtain a composition controlled ferrite powder such that the components of the composition controlled ferrite powder have molar percentages which are within 0.05 mol % of the target composition; forming said composition controlled ferrite powder to obtain a formed body; sintering said formed body to obtain a sintered body; and subjecting said sintered body to a hot isostatic pressing treatment to obtain a ferrite polycrystal body.
References Cited (Backward Citations)
US3853973A
Cited
EP0105122A2
Cited
US4552710A
Cited
JPS611391A
Cited
DE3529756A1
Cited
JPS6335496A
Cited
JPS6335490A
Cited
JPS63163815A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-10-25 | 1997-04-26 | 1997-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-10-25 | 2001-04-26 | 2001-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-10-25 | 2005-04-26 | 2005-10-26 | $7700.00 | Window Closed / Lapsed |