Method for recrystallization of preamorphized semiconductor surfaces zones

Claim 1

A method for manufacturing a semiconductor array of silicon with a surface zone of low penetration depth, wherein: said surface zone is amorphized by implantation of germanium ions, at an energy of approximately 70 keV and a dose of approximately 3·10 14 cm -2 , in the surface of a single-crystal semiconductor element, said surface zone is then doped by BF 2 + implantation at an energy of 15 keV to 25 keV and a dose of 3·10 13 cm -2 to 3·10 14 cm -2 , and finally the amorphous layer is recrystallized by a heat treatment consisting of a first furnace process step whose temperature is selected such that recrystallization of said amorphous layer does not yet take place but the interface zone is smoothed between said amorphous surface zone and said single-crystal semiconductor element, said first step being followed by a second furnace process step whose temperature is sufficiently high for said amorphous surface zone to recrystallize and low enough for the movability of the implanted impurity atoms to remain low, and said second step being followed by a final rapid thermal annealing process at a temperature high enough for said implanted impurity atoms to be activated and for a duration short enough to minimize the redistribution of said impurities.

Claim 2

A method for manufacturing a semiconductor array of silicon with a surface zone of low penetration depth, wherein: said surface zone is amorphized by implantation of germanium ions, at an energy of approximately 70 keV and a dose of approximately 3·10 14 cm -2 , in the surface of a single-crystal semiconductor element, said surface zone is then doped by BF 2 + implantation at an energy of 15 keV to 25 keV and a dose of 3·10 13 cm -2 to 3·10 14 cm -2 , and finally the amorphous layer is recrystallized by a heat treatment consisting of a first furnace process step whose temperature is selected such that recrystallization of said amorphous layer does not yet take place but the interface zone is smoothed between said amorphous surface zone and said single-crystal semiconductor element, said first step being followed by a second furnace process step whose temperature is sufficiently high for said amorphous surface zone to recrystallize and low enough for the movability of the implanted impurity atoms to remain low, and said second step being followed by a final rapid thermal annealing process at a temperature high enough for said implanted impurity atoms to be activated and for a duration short enough to minimize the redistribution of said impurities.

Claim 7

A method for manufacturing a semiconductor array of silicon with a surface zone of low penetration depth comprising the steps of: a) implanting germanium ions at an energy of approximately 70 keV and a dose of approximately 3×10 14 cm -2 in a single-crystal semiconductor element to amorphize a surface zone therein; b) doping said amorphous surface zone with impurity atoms by BF 2 + implantation at an energy of 15 keV to 25 keV and a dose of 3×10 13 cm -2 to 3×10 14 cm -2 ; c) heating said amorphous surface zone at a first temperature which is sufficiently high to smooth an interface region between said surface zone and said single-crystal semiconductor element, and which is sufficiently low to prevent recrystallization of said amorphous surface zone; d) next, heating said amorphous surface zone at a second temperature which is sufficiently high to recrystallize said amorphous surface zone, and which is sufficiently low to minimize movement of said implanted impurity atoms; and e) thereafter, heating said recrystallized surface zone by a rapid thermal annealing process at a third temperature sufficiently high to activate said implanted impurity atoms and for a duration sufficiently short to minimize redistribution of said impurity atoms.

Claim 8

A method for manufacturing a semiconductor array of silicon with a surface zone of low penetration depth comprising the steps of: a) implanting germanium ions at an energy of approximately 70 keV and a dose of approximately 3×10 14 cm -2 in a single-crystal semiconductor element to amorphize a surface zone therein; b) doping said amorphous surface zone with impurity atoms by BF 2 + implantation at an energy of 15 keV to 25 keV and a dose of 3×10 13 cm -2 to 3×10 14 cm -2 ; c) heating said amorphous surface zone at a first temperature which is sufficiently high to smooth an interface region between said surface zone and said single-crystal semiconductor element, and which is sufficiently low to prevent recrystallization of said amorphous surface zone; d) next, heating said amorphous surface zone at a second temperature which is sufficiently high to recrystallize said amorphous surface zone, and which is sufficiently low to minimize movement of said implanted impurity atoms; and e) thereafter, heating said recrystallized surface zone by a rapid thermal annealing process at a third temperature sufficiently high to activate said implanted impurity atoms and for a duration sufficiently short to minimize redistribution of said impurity atoms.