Claim 2

A process for applying heat shrink film to containers comprising the steps of: a) coating at least a portion of a heat shrinkable but unshrunken film segment with a reactive hot melt polyurethane adhesive having a free isocyanate content greater than 2% and a viscosity less than 3000 cps at 225° F.; b) applying the film to the longitudinal surface of the container; c) subjecting the container to heat to shrink the film onto the container so as to permanently affix it thereto; and d) subsequently subjecting the labelled container to a heating step.

Claim 3

The process of claim 1 wherein the hot melt adhesive composition additionally contains 0.05 to 1% by weight of a polyurethane catalyst.

Claim 4

The process of claim 1 wherein the hot melt adhesive is applied to a narrow region of the container or of the leading end of the film segment to secure the leading end of the film to the container, the film wrapped around the container and the film segment secured to the container by overlapping the trailing end, a narrow region of which has been coated with the hot melt adhesive.

Claim 5

The process of claim 1 wherein the urethane hot melt adhesive is prepared by the condensation polymerization of a polyisocyanate with a polyol.

Claim 6

The process of claim 4 wherein the polyisocyanate is selected from the group consisting of ethylene diisocyanate, ethylidene diisocyanate, propylene diisocyanate, butylene diisocyanate, hexamethylene diisocyante, toluene diisocyanate, cyclopentylene-1,3,-diisocyanate, cyclohexylene-1,4-diisocyanate, cyclohexylene-1,2-diisocyanate, 4,4'-diphenylmethane diisocyanate, 2,2-diphenylpropane-4,4'-diisocyanate, p-phenylene diisocyanate, m-phenylene diisocyanate, xylylene diisocyanate, 1,4-naphthylene diisocyanate, 1,5-naphthylene diisocyanate, diphenyl-4,4'-diisocyanate, azobenzene-4,4'-diisocyanate, diphenylsulphone-4,4'-diisocyanate, dichlorohexamethylene diisocyanate, furfurylidene diisocyanate, 1-chlorobenzene-2,4-diisocyanate, 4,4',4"-triisocyanatotriphenylmethane, 1,3,5-triisocyanato-benzene, 2,4,6-triisocyanatotoluene, and 4,4'-dimethyldiphenylmethane-2,2'5,5-tetraisocyanate, and the polyol is selected from the group consisting of polyhydroxy ethers, polyhydroxy polyesters, the ethylene or propylene oxide adducts of polyols and the mono-substituted esters of glycerol.

Claim 7

The process of claim 1 wherein the urethane polymer is characterized by a free isocyanate content of 2 to 10% and the isocyanate index is greater than 1 but no more than 3.5.

Claim 8

The process of claim 1 wherein the hot melt adhesive contains 10 to 95% of a polymer of ethylenically unsaturated monomers containing no active hydrogen.

Claim 9

The process of claim 1 wherein the hot melt adhesive additionally contains up to 40% by weight of a tackifying resin.

Claim 10

The process of claim 8 wherein the tackifying resin is present in an amount of 5 to 30% by weight.

Claim 11

The process of claim 8 wherein the tackifying resin is selected from the group consisting of glycerol and pentaerythritol esters of natural and modified rosins; copolymers and terpolymers of natural terpenes; polyterpene resins having a softening point, as determined by ASTM method E28-58T, of from about 60° to 150° C.; phenolic modified terpene resins and hydrogenated derivatives thereof; aliphatic petroleum hydrocarbon resins having a Ball and Ring softening point of from about 60° to 135° C.; aromatic petroleum hydrocarbon resins and the hydrogenated derivatives thereof; and alicyclic petroleum hydrocarbon resins and the hydrogenated derivatives thereof.