Dielectric deposition
Assignee: Agere Systems LLC
•
Filing: 1991-07-10
•
Granted: 1993-09-21
•
Expires: 2011-07-10
Abstract
Abstract A method for forming a thin high quality interlevel dielectric is disclosed. The dielectric is produced in a plasma reactor utilizing a precursor gas such as TEOS. Pressure, power, temperature, gas flow, and showerhead spacing are controlled so that a dielectric of TEOS may be deposited at 60-5 Å / sec, thus making formation of thin (800 Å) high quality dielectrics feasible.
Inventors
- 👤 Chen-Hua D. Yu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:09
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/402; H10P14/66; H10P14/668; H10P14/6681; H10P14/6684; H10P14/6686; H10W; H10W20/00; H10W20/01; H10W20/071; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; Y; Y10; Y10S; Y10S148/00; Y10S148/118
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
154 words
A method of semiconductor integrated circuit fabrication comprising: depositing first and second dielectrics upon a substrate, each of said dielectrics being deposited in a plasma reactor utilizing a respective precursor gas and respective oxygen, said respective precursor gas and said respective oxygen having respective flow rates; said respective precursor gases and said respective oxygen being directed at said substrate through one or more showerheads located a respective predetermined distance from said substrate; said plasmas being characterized by total respective power; said substrate being positioned on a susceptor which is characterized by a respective temperature; and said reactor being characterized by a respective total pressure and characterized by: the ratio of said oxygen gas flow to said precursor flow for said second dielectric being greater than the ratio of said oxygen gas flow to said precursor gas flow for said first dielectric, thereby depositing said second dielectric at a lower rate than said first dielectric.
Claim 2
Independent Claim
154 words
A method of semiconductor integrated circuit fabrication comprising: depositing first and second dielectrics upon a substrate, each of said dielectrics being deposited in a plasma reactor utilizing a respective precursor gas and respective oxygen, said respective precursor gas and said respective oxygen having respective flow rates; said respective precursor gases and said respective oxygen being directed at said substrate through one or more showerheads located a respective predetermined distance from said substrate; said plasmas being characterized by total respective power; said substrate being positioned on a susceptor which is characterized by a respective temperature; and said reactor being characterized by a respective total pressure and characterized by: the ratio of said oxygen gas flow to said precursor flow for said second dielectric being greater than the ratio of said oxygen gas flow to said precursor gas flow for said first dielectric, thereby depositing said second dielectric at a lower rate than said first dielectric.
Claim 3
Dependent Claim
34 words
The method of claim 1 in which the said respective total pressure of said reactor for said second dielectric is less than the said respective total pressure of said reactor for said first dielectric.
Claim 4
Dependent Claim
32 words
The method of claim 1 in which the said respective temperature of said susceptor for said second dielectric is greater than the said respective temperature of said susceptor for said first dielectric.
Claim 5
Dependent Claim
32 words
The method of claim 1 in which the said respective power of said plasma for said second dielectric is less than the said respective power of said plasma for said first dielectric.
Claim 6
Dependent Claim
27 words
The method of claim 1 in which said ratio of oxygen gas flow to said precursor gas flow for said second dielectric is greater than approximately 2.4.
Claim 7
Dependent Claim
34 words
The method of claim 1 in which the pressure inside said reactor during deposition of said second dielectric is chosen from the group consisting of the ranges 8 Torr±10%, 6 Torr±10%, and 6-8 Torr.
Claim 8
Dependent Claim
40 words
The method of claim 1 in which said plasma utilized for the deposition of said second dielectric is characterized by a total power and said power is chosen from the group consisting of 350 watts±10%, 100-200 watts, and 200-300 watts.
Claim 9
Dependent Claim
20 words
The method of claim 1 in which said precursor gas utilized during the formation of said second dielectric is TEOS.
Claim 10
Dependent Claim
25 words
The method of claim 8 in which said TEOS flow rate is chosen from the group consisting of 200 sccm±10%, 100 sccm±10%, and 50 sccm±10%.
Claim 11
Dependent Claim
33 words
The method of claim 8 in which said oxygen flow rate utilized during the formation of said second dielectric is chosen from the group consisting of 600 sccm±10%, 700 sccm±10%, and 750 sccm±10%.
Claim 12
Dependent Claim
35 words
The method of claim 1 in which said substrate is positioned on a susceptor during the formation of said second dielectric and said susceptor temperature is greater than 390° C. and less than 410° C.
Claim 13
Dependent Claim
34 words
The method of claim 1 in which the distance between said showerhead and said susceptor during the formation of said second dielectric is chosen from the group consisting of 200-300 mils and 300 mils±10%.
Claim 14
Dependent Claim
20 words
The method of claim 1 in which said precursor gas utilized during the formation of said second dielectric is TMCTS.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-20 | 1997-03-22 | 1997-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-20 | 2001-03-22 | 2001-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-20 | 2005-03-22 | 2005-09-21 | $7700.00 | Window Closed / Lapsed |