Polyamide resin thermoplastic blend containing a multi-phase structure thermoplastic resin compatibilization agent and progess for the production thereof
Assignee: NOF Corp
•
Filing: 1990-08-08
•
Granted: 1993-09-14
•
Expires: 2010-08-08
Abstract
Abstract A thermoplastic resin composition is here disclosed which is prepared by blending (I) 99 to 1% by weight of a polyamide resin, (II) 1 to 99% by weight of at least one kind of resin selected from the group consisting of a polyphenylene ether resin alone or a mixture of the polyphenylene ether resin and a styrene polymer, an aromatic polyester resin, a polycarbonate resin, a polyoxymethylene resin, an ABS resin, a polyarylene sulfide resin and a polyarylate resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I)+(II), of a multi-phase structure thermoplastic resin.
Inventors
- 👤 Suehiro Sakazume
- 👤 Yuichi Orikasa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:53
CPC Classifications
C; C08; C08L; C08L77/00; C08L55/00; C08L55/02; C08L67/00; C08L67/02; C08L67/03; C08L69/00; C08L71/00; C08L71/08; C08L71/10; C08L71/12; C08L71/123; C08L59/00; C08L59/02; C08L81/00; C08L81/02
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
117 words
A thermoplastic resin composition which is a blend of (I) 90 to 10% by weight of a polyamide resin, (II) 10 to 90% by weight of a polyphenylene ether resin and, (III) 1 to 50 parts by weight, based on 100 parts by weight of said resins (I)+(II), of a multi-phase structure thermoplastic resin which is a graft copolymer composed of (A) 5 to 95% by weight of a copolymer segment of ethylene-ethyl acrylate-maleic anhydride and (B) 95 to 5% by weight of a, polystyrene segment, one segment dispersed in the other segment and the particle diameter of the dispersion phase formed from said (A) or said (B) being in the range of 0.001 to 10 μm.
Claim 2
Dependent Claim
117 words
A thermoplastic resin composition which is a blend of (I) 90 to 10% by weight of a polyamide resin, (II) 10 to 90% by weight of a polyphenylene ether resin and, (III) 1 to 50 parts by weight, based on 100 parts by weight of said resins (I)+(II), of a multi-phase structure thermoplastic resin which is a graft copolymer composed of (A) 5 to 95% by weight of a copolymer segment of ethylene-ethyl acrylate-maleic anhydride and (B) 95 to 5% by weight of a, polystyrene segment, one segment dispersed in the other segment and the particle diameter of the dispersion phase formed from said (A) or said (B) being in the range of 0.001 to 10 μm.
Claim 3
Dependent Claim
182 words
A thermoplastic resin composition according to claim 1 wherein said multi-phase structure thermoplastic resin III is a graft polymerization precursor obtained by copolymerizing at least one styrene monomer with at least one of radical polymerizable or copolymerizable organic peroxides of the formulae (a) and (b): ##STR7## (wherein R 1 is a hydrogen atom or an alkyl group having 1 or 2 carbon atoms, each of R 2 and R 7 is a hydrogen atom or a methyl group, R 6 is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, each of R 3 , R 4 , R 8 and R 9 is an alkyl group having 1 to 4 carbon atoms, each of R 5 and R 10 is an alkyl group having 1 to 12 carbon atoms, a phenyl group, an alkyl-substituted phenyl group or a cycloalkyl group having 3 to 12 carbon atoms, m is 1 or 2, and n is 0, 1 or 2) in particles of at least one ethylene-ethyl acrylate-maleic anhydride copolymer, and optionally melting and kneading said graft polymerization precursor.
Claim 4
Dependent Claim
32 words
A thermoplastic resin composition according to claim 1 wherein said multi-phase structure thermoplastic resin is composed of 20 to 90% by weight of (A) and 80 to 10% by weight of (B).
Claim 5
Dependent Claim
34 words
A thermoplastic resin composition according to claim 1 wherein said ethylene-ethyl acrylate-maleic anhydride copolymer is a copolymer of 60-99.5% by weight ethylene, 0.5-40% by weight maleic anhydride and 0.39-5% by weight of ethyl acrylate.
Claim 6
Dependent Claim
21 words
A thermoplastic resin composition according to claim 1 wherein said particle diameter is in the range of 0.01 to 5 μm.
Claim 7
Dependent Claim
23 words
A thermoplastic resin composition according to claim 1 wherein said polystyrene segment (B) has a number average polymerization degree of 5 to 10,000.
Claim 8
Dependent Claim
18 words
A thermoplastic resin composition according to claim 6 wherein said number average polymerization degree is 10 to 5,000.
Claim 9
Dependent Claim
93 words
A thermoplastic resin composition according to claim 1 in which said polyamide resin is 6-nylon or 6,6-nylon, the amount of polyphenylene ether resin is 10 to 90% by weight, the amount of multi-phase structure thermoplastic resin is 1 to 50 parts by weight based on 100 parts by weight of said resins (I) and (II), said polystyrene has a number average polymerization degree of 10 to 5,000 and constitutes 80 to 10% of said multi-phase structure thermoplastic resin and in which said particle diameter is in the range of 0.01 to 5 μm.
Claim 10
Dependent Claim
12 words
The thermoplastic resin composition of claim 1 consisting essentially of said blend.
Claim 11
Dependent Claim
11 words
The thermoplastic resin composition of claim 1 consisting of said blend.
References Cited (Backward Citations)
EP0304041A2
Cited
US4962148A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-13 | 1997-03-15 | 1997-09-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-13 | 2001-03-15 | 2001-09-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-13 | 2005-03-15 | 2005-09-14 | $7700.00 | Window Closed / Lapsed |