Thermoplastic resin composition and method for preparing the same
Assignee: NOF Corp
•
Filing: 1988-09-08
•
Granted: 1990-10-09
•
Expires: 2008-09-08
Abstract
Abstract There is here provided a thermoplastic resin composition containing (I) 99 to 1% by weight of a polypropylene, (II) 1 to 99% by weight of at least one kind of resin selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer and an ABS resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I)+(II), of a multi-phase structure thermoplastic resin which is composed of 5 to 95% by weight of a polyolefin and 95 to 5% by weight of a vinyl polymer or copolymer obtained from at least one kind of vinyl monomer, either of both the components being in the state of a dispersion phase having a particle diameter of 0.001 to 10 μm. A method for preparing the above-mentioned thermoplastic resin composition is also provided here.
Inventors
- 👤 Yuichi Orikasa
- 👤 Suehiro Sakazume
- 👤 Sadahiro Nishimura
- 👤 Yoshinori Maki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:14
CPC Classifications
C; C08; C08L; C08L55/00; C08L55/02; C08L29/00; C08L29/10; C08F; C08F4/00; C08F4/28; C08F4/32; C08F4/34; C08L101/00; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08L67/00; C08L67/02; C08L69/00; C08L77/00; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/14; C08L2205/00; C08L2205/02; C08L2205/03; C08L2205/08; C08L23/04; C08L23/08; C08L23/0846; C08L23/0853; C08L25/00; C08L25/02; C08L25/04; C08L25/06; C08L25/08; C08L25/12; C08L51/00; C08L51/06; C08L71/00; C08L71/08; C08L71/10; C08L71/12
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
201 words
A thermoplastic resin composition consisting essentially of: (I) 99 to 1% by weight of a polypropylene, (II) 1 to 99% by weight of at least one resin selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin, a mixture of the polyphenylene ether resin and a styrene polymer, and an ABS resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I)+(II), of a multi-phase structure thermoplastic resin which is composed of 5 to 95% by weight of a polyolefin or olefin copolymer and 95 to 5% by weight of a vinyl polymer or copolymer obtained from at least one vinyl monomer, wherein said multi-phase structure thermoplastic resin is a graft polymerization precursor obtained by copolymerizing at least one vinyl monomer and at least one radical polymerizable or copolymerizable organic peroxide in particles of the polyolefin or olefin copolymer, or a multi-phase structure resin obtained by melting and kneading the graft polymerization precursor, and wherein at least one of the components of the multi-phase structure thermoplastic resin is present in a dispersion phase having a particle diameter of 0.001 to 10 μm.
Claim 2
Dependent Claim
201 words
A thermoplastic resin composition consisting essentially of: (I) 99 to 1% by weight of a polypropylene, (II) 1 to 99% by weight of at least one resin selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin, a mixture of the polyphenylene ether resin and a styrene polymer, and an ABS resin, and (III) 0.1 to 100 parts by weight, based on 100 parts by weight of the aforesaid resins (I)+(II), of a multi-phase structure thermoplastic resin which is composed of 5 to 95% by weight of a polyolefin or olefin copolymer and 95 to 5% by weight of a vinyl polymer or copolymer obtained from at least one vinyl monomer, wherein said multi-phase structure thermoplastic resin is a graft polymerization precursor obtained by copolymerizing at least one vinyl monomer and at least one radical polymerizable or copolymerizable organic peroxide in particles of the polyolefin or olefin copolymer, or a multi-phase structure resin obtained by melting and kneading the graft polymerization precursor, and wherein at least one of the components of the multi-phase structure thermoplastic resin is present in a dispersion phase having a particle diameter of 0.001 to 10 μm.
Claim 3
Dependent Claim
57 words
A thermoplastic resin composition according to claim 1 wherein the polyolefin or olefin copolymer in the multi-phase structure thermoplastic resin is at least one resin selected from the group consisting of a propylene polymer, an epoxy group-containing ethylene copolymer, an ethylene-unsaturated carboxylic acid or its alkyl ester copolymer, or its metallic salt, and an ethylene-vinyl ester copolymer.
Claim 4
Dependent Claim
29 words
A thermoplastic resin composition according to claim 1 wherein the vinyl polymer or copolymer in the multi-phase structure thermoplastic resin has an average polymerization degree of 5 to 10,000.
Claim 5
Dependent Claim
217 words
A thermoplastic resin composition according to claim 1 wherein the multi-phase structure thermoplastic resin (III) is a mixture a grafted compound prepared by melting and mixing the mixture, which mixture comprises 1 to 100% by weight of a graft polymerization precursor (A) obtained by copolymerizing at least one vinyl monomer with at least one of radical polymerizable or copolymerizable organic peroxides represented by the following general formulae (a) and (b) ##STR4## wherein R 1 is a hydrogen atom or an alkyl group having 1 or 2 carbon atoms, each of R 2 and R 7 is a hydrogen atom or a methyl group, R 6 is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, each of R 3 , R 4 , R 8 and R 9 is an alkyl group having 1 to 4 carbon atoms, each of R 5 and R 10 is an alkyl group having 1 to 12 carbon atoms, a phenyl group, an alkyl-substituted phenyl group or a cycloalkyl group having 3 to 12 carbon atoms, m is 1 or 2, and n is 0, 1 or 2, in particles of a polyolefin or olefin copolymer, 0to 99% by weight of a polyolefin (B), and 0 to 99% by weight of a vinyl polymer or copolymer (C).
Claim 6
Dependent Claim
39 words
A thermoplastic resin composition according to claim 1 wherein the vinyl monomer is at least one vinyl monomer selected from the group consisting of vinyl aromatic monomers, acrylate and methacrylate monomers, acrylonitrile and methacrylonitrile monomers, and vinyl ester monomers.
Claim 7
Dependent Claim
47 words
A thermoplastic resin composition according to claim 2 wherein the epoxy group containing ethylene copolymer is a copolymer composed of 60 to 99.5% by weight of ethylene, 40 to 0.5% by weight of glycidyl acrylate or methacrylate, and 0 to 39.5% by weight of another unsaturated monomer.
Claim 8
Dependent Claim
62 words
A thermoplastic resin composition according to claim 2 wherein the resin is a copolymer or its' metallic salt which comprises 50 to 99.5% by weight of ethylene, 50 to 0.5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids, their alkyl esters and vinyl esters, and 0 to 49.5% by weight of another unsaturated monomer.
Claim 9
Dependent Claim
33 words
A thermoplastic resin composition according to claim 1 wherein the vinyl polymer or copolymer comprises a vinyl monomer in which the content of a vinyl aromatic monomer is 50% by weight or more.
Claim 10
Dependent Claim
34 words
A thermoplastic resin composition according to claim 1 containing an inorganic filler in an amount of 1 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I)+(II)+(III).
Claim 11
Dependent Claim
34 words
A thermoplastic resin composition according to claim 1 containing a flame retardant in an amount of 5 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I)+(II)+III).
Claim 12
Independent Claim
223 words
A method for preparing a thermoplastic resin composition which comprises the step of melting and mixing a polypropylene (I) and at least one resin (II) selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer and an ABS resin, with 1 to 100% by weight of a graft polymerization precursor (A) which is obtained by mixing at least one vinyl monomer, at least one radical polymerizable or copolymerizable organic peroxide, a radical polymerization initiator and an aqueous suspension of a polyolefin, heating the suspension under such conditions that the decomposition of the radical polymerization initiator does not occur substantially, in order to impregnate the polyolefin with the vinyl monomer, the radical polymerizable or copolymerizable organic peroxide and the radical polymerization initiator and raising the temperature of this aqueous suspension, when the degree of the impregnation has reached 50% by weight of the original total weight of the vinyl monomer, peroxide and initiator, in order to copolymerize the vinyl monomer with the radical polymerizable or copolymerizable organic peroxide in the polyolefin, 0to 99% by weight of the polyolefin (B), and 0 to 99% by weight of a vinyl polymer or copolymer (C) obtained by polymerizing at least one kind of vinyl monomer.
Claim 13
Independent Claim
223 words
A method for preparing a thermoplastic resin composition which comprises the step of melting and mixing a polypropylene (I) and at least one resin (II) selected from the group consisting of an aromatic polyester resin, a polycarbonate resin, a polyamide resin, a polyphenylene ether resin or a mixture of the polyphenylene ether resin and a styrene polymer and an ABS resin, with 1 to 100% by weight of a graft polymerization precursor (A) which is obtained by mixing at least one vinyl monomer, at least one radical polymerizable or copolymerizable organic peroxide, a radical polymerization initiator and an aqueous suspension of a polyolefin, heating the suspension under such conditions that the decomposition of the radical polymerization initiator does not occur substantially, in order to impregnate the polyolefin with the vinyl monomer, the radical polymerizable or copolymerizable organic peroxide and the radical polymerization initiator and raising the temperature of this aqueous suspension, when the degree of the impregnation has reached 50% by weight of the original total weight of the vinyl monomer, peroxide and initiator, in order to copolymerize the vinyl monomer with the radical polymerizable or copolymerizable organic peroxide in the polyolefin, 0to 99% by weight of the polyolefin (B), and 0 to 99% by weight of a vinyl polymer or copolymer (C) obtained by polymerizing at least one kind of vinyl monomer.
Claim 14
Dependent Claim
153 words
A method for preparing a thermoplastic resin composition according to claim 11 wherein the radical polymerizable or copolymerizable organic peroxide is at least one peroxycarbonate compound represented by the following general formulae (a) and (b) ##STR5## wherein R 1 is a hydrogen atom or an alkyl group having 1 or 2 carbon atoms, each of R 2 and R 7 is a hydrogen atom or a methyl group, R 6 is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, each of R 3 , R 4 , R 8 and R 9 is an alkyl group having 1 to 4 carbon atoms, each of R 5 and R 10 is an alkyl group having 1 to 12 carbon atoms, a phenyl group, an alkyl-substituted phenyl group or a cycloalkyl group having 3 to 12 carbon atoms, m is 1 or 2, and n is 0, 1 or 2.
Claim 15
Dependent Claim
33 words
A method for preparing a thermoplastic resin composition according to claim 11 wherein the vinyl polymer or copolymer in the multi-phase structure thermoplastic resin has an average polymerization degree of 5 to 10,000.
Claim 16
Dependent Claim
58 words
A method for preparing a thermoplastic resin composition according to claim 11 wherein the polyolefin in the multi-phase structure thermoplastic resin is at least one resin selected from the group consisting of a propylene polymer, an epoxy group-containing ethylene copolymer, an ethylene-unsaturated carboxylic acid or its alkyl ester copolymer, or its metallic salt, and an ethylene-vinyl ester copolymer.
Claim 17
Dependent Claim
43 words
A method for preparing a thermoplastic resin composition according to claim 11 wherein the vinyl monomer is at least one vinyl monomer selected from the group consisting of vinyl aromatic monomers, acrylate and methacrylate monomers, acrylonitrile and methacrylonitrile monomers, and vinyl ester monomers.
Claim 18
Dependent Claim
47 words
A method for preparing a thermoplastic resin composition according to claim 14 wherein the resin is a copolymer composed of 60 to 99.5% by weight of ethylene, 40 to 0.5% by weight of glycidyl acrylate or methacrylate, and 0 to 39.5% by weight of another unsaturated monomer.
Claim 19
Dependent Claim
65 words
A method for preparing a thermoplastic resin composition according to claim 14 wherein the resin is a copolymer or its metallic salt comprises 50 to 99.5% by weight of ethylene, 50 to 0.5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids, their alkyl esters and vinyl esters, and 0 to 49.5% by weight of another unsaturated monomer.
Claim 20
Dependent Claim
37 words
A method for preparing a thermoplastic resin composition according to claim 11 wherein the vinyl polymer or copolymer comprises a vinyl monomer in which the content of a vinyl aromatic monomer is 50% by weight or more.
Claim 21
Dependent Claim
41 words
A method for preparing a thermoplastic resin composition according o claim 11 wherein an inorganic filler is additionally blended in an amount of 1 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I)+(II)+(III).
Claim 22
Dependent Claim
41 words
A method for preparing a thermoplastic resin composition according to claim 11 wherein a flame retardant is additionally blended in an amount of 5 to 150 parts by weight based on 100 parts by weight of the thermoplastic resin composition (I)+(II)+(III).
Claim 23
Dependent Claim
42 words
A method for preparing a thermoplastic resin according to claim 11 wherein components A, B and C are mixed and melted at a temperature of 200 ° to 300° C., and the resulting resin is mixed and melted with I and II.
References Cited (Backward Citations)
US4481330A
Cited
US4520164A
Cited
EP0177151A2
Cited
US4753990A
Cited
US4801645A
Cited
US4839423A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-08 | 1994-04-09 | 1994-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-08 | 1998-04-09 | 1998-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-08 | 2002-04-09 | 2002-10-09 | $7700.00 | Window Closed / Lapsed |