Composition for making multilayer ceramic substrates and dielectric materials with low firing temperature
Assignee: BLU TECHNOLOGY 2 LLC
•
Filing: 1992-03-04
•
Granted: 1993-09-07
•
Expires: 2012-03-04
Abstract
Abstract A composition for multilayer ceramic substrates and dielectric materials with low firing temperatures is disclosed. The composition, based on the total weight of the composition, includes 40-80% of amorphous borosilicate glass which contains 60-80% by weight of SiO2, 15-30% by weight of B2O3, 0.5-1.5% by weight of Al2O3 and 0.5-3% by weight of alkali oxides; and 20-60% of fillers selected from the groups of alumina, forsterite, quartz, fused SiO2, mullite, cordierite, BN, and AlN.
Inventors
- 👤 Jane-Chyi Lin
- 👤 Chian-Lii Cherng
- 👤 Chien-Min Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:26
CPC Classifications
C; C03; C03C; C03C14/00; C03C14/004; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; C03C2214/00; C03C2214/04
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
92 words
A composition for multi-layer ceramic substrates and dielectric materials with low firing temperature consisting essentially of (1) 45 to 70% by weight of an amorphous borosilicate glass comprising 60-80% by weight SiO 2 , 15-30% by weight of B 2 O 3 , 0.5-0 1.5% by weight of Al 2 O 3 and 0.5-3% by weight of alkali oxides and (2) 30 to 55% by weight of a filler wherein said filler is a mixture of fosterite and alumina by which the coefficient of thermal expansion can be adjusted to match alumina.
Claim 2
Dependent Claim
92 words
A composition for multi-layer ceramic substrates and dielectric materials with low firing temperature consisting essentially of (1) 45 to 70% by weight of an amorphous borosilicate glass comprising 60-80% by weight SiO 2 , 15-30% by weight of B 2 O 3 , 0.5-0 1.5% by weight of Al 2 O 3 and 0.5-3% by weight of alkali oxides and (2) 30 to 55% by weight of a filler wherein said filler is a mixture of fosterite and alumina by which the coefficient of thermal expansion can be adjusted to match alumina.
References Cited (Backward Citations)
US4547625A
Cited
US4624934A
Cited
US4939021A
Cited
US4849379A
Cited
US5024975A
Cited
US5070046A
Cited
US5079194A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-06 | 1997-03-08 | 1997-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-06 | 2001-03-08 | 2001-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-06 | 2005-03-08 | 2005-09-07 | $7700.00 | Window Closed / Lapsed |