Method of fabricating a polycrystalline silicon film having a reduced resistivity
Assignee: NEC Electronics Corp
•
Filing: 1992-09-29
•
Granted: 1993-09-07
•
Expires: 2012-09-29
Abstract
Abstract Disclosed is a method of forming a polycrystalline silicon film on a silicon oxide film in which the polycrystalline silicon film includes crystal grains having a large size, typically 4 micrometers, thereby permitting the resistivity of the polycrystalline silicon film to effectively be reduced. An amorphous silicon film is deposited on the silicon oxide film by using a chemical vapor deposition in which the flow rate of impurity gas remains at zero during an initial deposition, after which the flow rate is gradually increased from zero to a predetermined value during a final deposition. Thus, the amorphous silicon film comprises double layers, or an impurity unmixed region abutting the silicon oxide film and an impurity mixed region. After that, by a heat treatment, the amorphous silicon film is crystallized to form a polycrystalline silicon film. Concurrently, the impurity diffusion is accomplished.
Inventors
- 👤 Shizuo Oguro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:31
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/38; H10P14/3802; H10P95/00; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
103 words
A method of forming a polycrystalline silicon film, comprising the steps of: depositing a first layer made of amorphous silicon having a dopant concentration of approximately zero on a silicon oxide film or a quartz substrate; depositing a second layer made of amorphous silicon having a dopant concentration greater than zero on said first layer; and subjecting said first and second layers to a heat treatment so that said first and second layers made of amorphous silicon are crystallized to form a polycrystalline silicon film having a large crystal grain size and a diffusion of dopant into said first layer is concurrently accomplished.
Claim 2
Independent Claim
103 words
A method of forming a polycrystalline silicon film, comprising the steps of: depositing a first layer made of amorphous silicon having a dopant concentration of approximately zero on a silicon oxide film or a quartz substrate; depositing a second layer made of amorphous silicon having a dopant concentration greater than zero on said first layer; and subjecting said first and second layers to a heat treatment so that said first and second layers made of amorphous silicon are crystallized to form a polycrystalline silicon film having a large crystal grain size and a diffusion of dopant into said first layer is concurrently accomplished.
Claim 3
Dependent Claim
59 words
The method of forming a polycrystalline silicon film as claimed in claim 1, wherein said first and second layers made of amorphous silicon are deposited by using a chemical vapor deposition method in which deposition of said first layer uses a growth gas only but deposition of said second layer uses both said growth gas and an impurity gas.
Claim 4
Dependent Claim
58 words
The method of forming a polycrystalline silicon film as claimed in claim 2, wherein the flow rate of said impurity gas remains at approximately zero during deposition of said first layer after which said flow rate of said impurity gas is gradually increased from approximately zero to a value greater than zero during deposition of said second layer.
Claim 5
Dependent Claim
30 words
The method of forming a polycrystalline silicon film as claimed in claim 3, wherein during deposition of said second layer, said flow rate of said impurity gas is continuously increased.
Claim 6
Dependent Claim
30 words
The method of forming a polycrystalline silicon film as claimed in claim 3, wherein during deposition of said second layer, said flow rate of said impurity gas is discontinuously increased.
Claim 7
Dependent Claim
30 words
The method of forming a polycrystalline silicon film as claimed in claim 1, wherein said crystal grain size of said polycrystalline silicon film is approximately 4 micrometers on the average.
Claim 8
Independent Claim
107 words
A method of forming polycrystalline silicon film, comprising the steps of: forming a silicon oxide film on a silicon substrate; depositing a first layer made of amorphous silicon having a dopant concentration of approximately zero on said silicon oxide film; depositing a second layer made of amorphous silicon having a dopant concentration greater than zero on said first layer; and subjecting said first and second layers to a heat treatment so that said first and second layers made of amorphous silicon are crystallized to form a polycrystalline silicon film having a large crystal grain size and a diffusion of dopant into said first layer is concurrently accomplished.
Claim 9
Independent Claim
107 words
A method of forming polycrystalline silicon film, comprising the steps of: forming a silicon oxide film on a silicon substrate; depositing a first layer made of amorphous silicon having a dopant concentration of approximately zero on said silicon oxide film; depositing a second layer made of amorphous silicon having a dopant concentration greater than zero on said first layer; and subjecting said first and second layers to a heat treatment so that said first and second layers made of amorphous silicon are crystallized to form a polycrystalline silicon film having a large crystal grain size and a diffusion of dopant into said first layer is concurrently accomplished.
Claim 10
Dependent Claim
59 words
The method of forming a polycrystalline silicon film as claimed in claim 7, wherein said first and second layers made of amorphous silicon are deposited by using a chemical vapor deposition method in which deposition of said first layer uses a growth gas only but deposition of said second layer uses both said growth gas and an impurity gas.
Claim 11
Dependent Claim
58 words
The method of forming a polycrystalline silicon film as claimed in claim 8, wherein the flow rate of said impurity gas remains at approximately zero during deposition of said first layer after which said flow rate of said impurity gas is gradually increased from approximately zero to a value greater than zero during deposition of said second layer.
Claim 12
Dependent Claim
30 words
The method of forming a polycrystalline silicon film as claimed in claim 9, wherein during deposition of said second layer, said flow rate of said impurity gas is continuously increased.
Claim 13
Dependent Claim
30 words
The method of forming a polycrystalline silicon film as claimed in claim 9, wherein during deposition of said second layer, said flow rate of said impurity gas is discontinuously increased.
Claim 14
Dependent Claim
30 words
The method of forming a polycrystalline silicon film as claimed in claim 7, wherein said crystal grain size of said polycrystalline silicon film is approximately 4 micrometers on the average.
References Cited (Backward Citations)
GB2171844A
Cited
JPS6459867A
Cited
JPH01223719A
Cited
JPH0281421A
Cited
US5155051A
Cited
US5147826A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-06 | 1997-03-08 | 1997-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-06 | 2001-03-08 | 2001-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-06 | 2005-03-08 | 2005-09-07 | $7700.00 | Window Closed / Lapsed |