US5242647A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of casting aerogels
Assignee: University of California
•
Filing: 1991-07-30
•
Granted: 1993-09-07
•
Expires: 2011-07-30
Abstract
Abstract The invention describes a method for making monolithic castings of transparent silica aerogel with densities in the range from 0.001 g/cm 3 to 0.6 g/cm 3 . Various shapes of aerogels are cast in flexible polymer molds which facilitate removal and eliminate irregular surfaces. Mold dimensions are preselected to account for shrinkage of alcogel which occurs during the drying step of supercritical extraction of solvent.
Inventors
- 👤 John F. Poco
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:35
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/113; C01B33/12; C01B33/14; C01B33/157; C01B33/158; C01B33/1585; B; B01; B01J; B01J13/00; B01J13/0091; C03; C03C; C03C1/00; C03C1/006; Y; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
179 words
A method for producing a monolithic piece of low-density aerogel, having a pre-selected size, shape, and density, comprising the steps: (a) selecting a smooth surface mandrel of a predetermined size and shape, wherein the size of the mandrel is determined from the desired dimensions of the final aerogel piece and form a known shrinkage ratio of aerogel at the pre-selected density; (b) forming a flexible casting mold over the mandrel with a flexible molding polymer material, whereby the shape of the mold conforms to the shape of the mandrel; (c) removing the mandrel from the flexible casting mold; (d) casting the gel precursor solution in the flexible casting mold; (e) curing the solution to form an alcogel, which contains a solvent; (f) removing the alcogel from the flexible casting mold by flexing the mold; (g) supporting at least one surface of the alcogel with a sheet of rigid material that does not stick to the alcogel for preventing deformation of the alcogel; and (h) removing the solvent from the alcogel by supercritical extraction to form a monolithic aerogel piece.
Claim 2
Independent Claim
179 words
A method for producing a monolithic piece of low-density aerogel, having a pre-selected size, shape, and density, comprising the steps: (a) selecting a smooth surface mandrel of a predetermined size and shape, wherein the size of the mandrel is determined from the desired dimensions of the final aerogel piece and form a known shrinkage ratio of aerogel at the pre-selected density; (b) forming a flexible casting mold over the mandrel with a flexible molding polymer material, whereby the shape of the mold conforms to the shape of the mandrel; (c) removing the mandrel from the flexible casting mold; (d) casting the gel precursor solution in the flexible casting mold; (e) curing the solution to form an alcogel, which contains a solvent; (f) removing the alcogel from the flexible casting mold by flexing the mold; (g) supporting at least one surface of the alcogel with a sheet of rigid material that does not stick to the alcogel for preventing deformation of the alcogel; and (h) removing the solvent from the alcogel by supercritical extraction to form a monolithic aerogel piece.
Claim 3
Dependent Claim
22 words
A method for producing a monolithic aerogel piece as recited in claim 1, wherein the flexible molding polymer material comprises silicon rubber.
Claim 4
Dependent Claim
22 words
A method for producing a monolithic aerogel piece as recited in claim 1, wherein the flexible molding polymer material comprises polyvinyl pyrrolidine.
Claim 5
Dependent Claim
30 words
A method for producing a monolithic aerogel piece as recited in claim 1, further comprising the step: selecting the mandrel with the pre-determined shape having at least two parallel surfaces.
Claim 6
Dependent Claim
26 words
A method for producing a monolithic aerogel piece as recited in claim 1, further comprising the step: selecting the mandrel with the pre-determined shape being spherical.
Claim 7
Dependent Claim
31 words
A method as recited in claim 1, further comprising the step: placing the mold with the alcogel into an environment comprising methanol vapor before removing the alcogel as in step (f).
Claim 8
Dependent Claim
28 words
A method as recited in claim 1, further comprising the step: submerging the alcogel in a container comprising the solvent after removing the alcogel as in step (f).
Claim 9
Independent Claim
181 words
A method for producing a monolithic piece of low-density aerogel, having a pre-selected size, shape, and density, comprising the steps: (a) selecting a smooth surface mandrel of a predetermined size and shape, wherein the size of the mandrel is determined from the desired dimensions of the final aerogel piece and from a known shrinkage ratio of aerogel at the pre-selected density; (b) forming a flexible casting mold over the mandrel with a flexible molding polymer material, whereby the shape of the mold conforms to the shape of the mandrel; (c) removing the mandrel from the flexible casting mold; (d) selecting a gel precursor solution which produces a monolithic aerogel piece having the pre-selected density in a range of about 0.001 g/cm 3 to about 0.02 g/cm 3 ; (e) casting the gel precursor solution in the flexible casting mold; (f) curing the solution to form an alcogel, which contains a solvent; (g) removing the alcogel from the flexible casting mold by flexing the mold; and (h) removing the solvent from the alcogel by supercritical extraction to from a monolithic aerogel piece.
Claim 10
Independent Claim
181 words
A method for producing a monolithic piece of low-density aerogel, having a pre-selected size, shape, and density, comprising the steps: (a) selecting a smooth surface mandrel of a predetermined size and shape, wherein the size of the mandrel is determined from the desired dimensions of the final aerogel piece and from a known shrinkage ratio of aerogel at the pre-selected density; (b) forming a flexible casting mold over the mandrel with a flexible molding polymer material, whereby the shape of the mold conforms to the shape of the mandrel; (c) removing the mandrel from the flexible casting mold; (d) selecting a gel precursor solution which produces a monolithic aerogel piece having the pre-selected density in a range of about 0.001 g/cm 3 to about 0.02 g/cm 3 ; (e) casting the gel precursor solution in the flexible casting mold; (f) curing the solution to form an alcogel, which contains a solvent; (g) removing the alcogel from the flexible casting mold by flexing the mold; and (h) removing the solvent from the alcogel by supercritical extraction to from a monolithic aerogel piece.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-06 | 1997-03-08 | 1997-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-06 | 2001-03-08 | 2001-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-06 | 2005-03-08 | 2005-09-07 | $7700.00 | Window Closed / Lapsed |