Abstract A green tinted, ultraviolet absorbing glass is obtained by the addition of colorant to a standard soda-lime-silica base glass composition and a colorant includes less than 0.5 weight percent of cerium oxide (CeO2), greater than 0.85 weight percent of total iron expressed as Fe2O3 and a ratio of ferric iron expressed as FeO to total iron of less than 0.275. The glass has a low ultraviolet transmittance, viz., no greater than 31 percent over the wavelength range of 300 to 390 nanometers at a reference glass thickness of 3.9 millimeters. An advantage of the glass of this invention over competing ultraviolet absorbing glass is the use of larger amounts of total iron and smaller proportions of iron in the ferrous state to obtain the low ultraviolet transmittance. In this manner, the amounts of cerium oxide which is expensive is reduced.
A green tinted, ultraviolet absorbing glass having a base glass composition consisting essentially of: ______________________________________
SiO.sub.2 68-75 weight %
Na.sub.2 O 10-20
CaO 5-15
MgO 0-5
Al.sub.2 O.sub.3 0-5
K.sub.2 O 0-5
______________________________________ and a colorant portion consisting essentially of: ______________________________________
CeO.sub.2 Less than 0.5 weight %
Total Iron Greater than 0.85 weight %
(as Fe.sub.2 O.sub.3)
FeO/total iron Less than 0.275
______________________________________ exhibiting ultraviolet transmittance no greater than 31 percent (300 to 390 nanometers) and luminous transmittance (illuminant A) of at least 70 percent, both at a reference thickness of 3.9 millimeters.
Claim 2
Dependent Claim
93 words
A green tinted, ultraviolet absorbing glass having a base glass composition consisting essentially of: ______________________________________
SiO.sub.2 68-75 weight %
Na.sub.2 O 10-20
CaO 5-15
MgO 0-5
Al.sub.2 O.sub.3 0-5
K.sub.2 O 0-5
______________________________________ and a colorant portion consisting essentially of: ______________________________________
CeO.sub.2 Less than 0.5 weight %
Total Iron Greater than 0.85 weight %
(as Fe.sub.2 O.sub.3)
FeO/total iron Less than 0.275
______________________________________ exhibiting ultraviolet transmittance no greater than 31 percent (300 to 390 nanometers) and luminous transmittance (illuminant A) of at least 70 percent, both at a reference thickness of 3.9 millimeters.
Claim 3
Dependent Claim
18 words
The glass of claim 1 wherein the glass contains less than 0.4 percent by weight CeO 2 .
Claim 4
Dependent Claim
17 words
The glass of claim 1 wherein the glass exhibits a dominant wavelength from 495 to 535 nanometers.
Claim 5
Dependent Claim
25 words
The glass of claim 1 wherein the glass exhibits a total solar energy transmittance less than 45 percent at a reference thickness of 3.9 millimeters.
Claim 6
Dependent Claim
48 words
The glass of claim 1 wherein the glass contains 0.20-0.40 percent by weight CeO 2 and 0.85-1.132 percent by weight total iron (as Fe 2 O 3 ), and a value of FeO/total iron of equal to or greater than 0.161 and equal to or less tan 0.275.