Alloy powder mixture for brazing of superalloy articles

Claim 2

An improved braze material for brazing at least one superalloy substrate comprising: a high melt component having at least one metallic powder consisting essentially of, by weight, about 4 to about 18.5 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13.7 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities; and a low melt component having at least one metallic powder consisting essentially of, by weight, about 3.9 to about 25 percent cobalt, about 4.6 to about 22 percent chromium, 0 to about 12.2 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 2 percent molybdenum, 0 to about 5.4 percent tantalum, 0 to about 7 percent tungsten, 0 to about 3 percent niobium, 0 to about 1.5 percent rhenium, 0 to about 1.1 percent hafnium, 0 to about 10 percent silicon, 0 to about 2.3 percent boron, wherein the total amount of silicon plus boron is at least 0.5 percent, with the balance being nickel and incidental impurities; wherein the high melt component and the low melt component together comprise a bulk composition range consisting essentially of, by weight, about 3 to about 13.5 percent cobalt, about 2.8 to about 15 percent chromium, about 3 to about 7.5 percent aluminum, 0 to about 5 percent titanium, 0 to about 2.5 percent molybdenum, about 2.5 to about 6.9 percent tantalum, about 3 to about 8 percent tungsten, 0 to about 1.5 percent niobium, 0 to about 6 percent rhenium, 0 to about 1.5 percent hafnium, 0 to about 2.2 percent silicon, 0 to about 1 percent boron, with the balance being nickel and incidental impurities; wherein the bulk composition range comprises less than about 2.2 total weight percent of elements selected from the group consisting of boron and silicon; wherein the low melt component comprises about 30 to about 70 percent by weight of the braze material; wherein the braze material has an effective brazing temperature above about 2300° F.; wherein the high melt component is substantially solid at the effective brazing temperature; and wherein the low melt component is substantially liquid at the effective brazing temperature.

Claim 3

The braze material of claim 1 in which the bulk composition range comprises, by weight, about 8 to about 12 percent cobalt, about 8 to about 10 percent chromium, abut 4.5 to about 5.5 percent aluminum, about 2 to about 3 percent titanium, 1.5 to about 2.5 percent molybdenum, about 3 to about 4.2 percent tantalum, about 6 to about 8 percent tungsten, 0 to about 1 percent niobium, 0 to about 1 percent rhenium, about 1 to about 1.5 percent hafnium, 0 to about 1 percent boron, with the balance being nickel and incidental impurities.

Claim 4

The braze material of claim 1, in which the high melt component is comprised of at least two metallic powders, each having a composition range that contains boron and silicon only as incidental impurities.

Claim 5

The braze material of claim 1 in which the low melt component is comprised of at least two metallic powders, each having a composition range that includes at least one element selected from the group consisting of boron and silicon.

Claim 6

The braze material of claim 1, wherein the bulk composition comprises, by weight, about 10 to about 13. 5 percent cobalt, about 6 to about 9 percent chromium, about 5 to about 7 percent aluminum, 1 to about 2 percent molybdenum, about 5.5 to about 6.9 percent tantalum, about 4 to about 6 percent tungsten, about 2 to about 3.5 percent rhenium, about 1 to about 1.5 percent hafnium, about 0.1 to about 0.5 percent boron, with the balance being nickel and incidental impurities.

Claim 7

The braze material of claim 1, wherein the high melt component additionally includes a metallic powder consisting essentially of, by weight, about 33 to about 37 percent chromium, about 9 to about 11 percent tantalum, about 7.5 to about 9.5 percent tungsten, with the balance cobalt and incidental impurities.

Claim 8

An improved braze material for brazing at least one superalloy substrate comprising: a high melt component having at least one metallic powder having a composition range consisting essentially of, by weight, about 4 to about 12 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities; and a eutectic component having at least one metallic powder having a composition range consisting essentially of, by weight, about 3.1 to about 8.2 percent cobalt, about 6.8 to about 38.5 percent chromium, 0 to about 12.6 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 1.3 percent molybdenum, 0 to about 23.1 percent tantalum, 0 to about 2.4 percent tungsten, 0 to about 5.1 percent niobium, 0 to about 1 percent rhenium, 0 to about 0.4 percent hafnium, 0 to about 0.6 percent yttrium, less than about 0.15 percent carbon, with the balance being nickel and incidental impurities; wherein the high melt component and the eutectic component together comprise a bulk composition range consisting essentially of, by weight, about 6 to about 10.2 percent cobalt, about 6 to about 16 percent chromium, about 4.5 to about 6.6 percent aluminum, 0 to about 3.5 percent titanium, 0 to about 2 percent molybdenum, about 4 to about 7.5 percent tantalum, about 3 to about 6 percent tungsten, 0 to about 2 percent niobium, 0 to about 4 percent rhenium, 0 to about 1.08 percent hafnium, 0 to about 0.2 percent yttrium, with the balance being nickel and incidental impurities; wherein the eutectic component comprises about 20 to about 50 percent by weight of the braze material; wherein the braze material has an effective brazing temperature above about 2300° F.; wherein the high melt component is substantially solid at the effective brazing temperature; and wherein the eutectic component is substantially liquid at the effective brazing temperature.

Claim 9

An improved braze material for brazing at least one superalloy substrate comprising: a high melt component having at least one metallic powder having a composition range consisting essentially of, by weight, about 4 to about 12 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities; and a eutectic component having at least one metallic powder having a composition range consisting essentially of, by weight, about 3.1 to about 8.2 percent cobalt, about 6.8 to about 38.5 percent chromium, 0 to about 12.6 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 1.3 percent molybdenum, 0 to about 23.1 percent tantalum, 0 to about 2.4 percent tungsten, 0 to about 5.1 percent niobium, 0 to about 1 percent rhenium, 0 to about 0.4 percent hafnium, 0 to about 0.6 percent yttrium, less than about 0.15 percent carbon, with the balance being nickel and incidental impurities; wherein the high melt component and the eutectic component together comprise a bulk composition range consisting essentially of, by weight, about 6 to about 10.2 percent cobalt, about 6 to about 16 percent chromium, about 4.5 to about 6.6 percent aluminum, 0 to about 3.5 percent titanium, 0 to about 2 percent molybdenum, about 4 to about 7.5 percent tantalum, about 3 to about 6 percent tungsten, 0 to about 2 percent niobium, 0 to about 4 percent rhenium, 0 to about 1.08 percent hafnium, 0 to about 0.2 percent yttrium, with the balance being nickel and incidental impurities; wherein the eutectic component comprises about 20 to about 50 percent by weight of the braze material; wherein the braze material has an effective brazing temperature above about 2300° F.; wherein the high melt component is substantially solid at the effective brazing temperature; and wherein the eutectic component is substantially liquid at the effective brazing temperature.

Claim 10

The braze material of claim 7 in which the bulk composition range comprises, by weight, about 6 to about 10 percent cobalt, about 12 to about 16 percent chromium, about 4.5 to about 6 percent aluminum, 1.5 to about 3.5 percent titanium, 0 to about 2 percent molybdenum, about 4 to about 6 percent tantalum, about 3 to about 5 percent tungsten, 0 to about 2 percent niobium, 0 to about 3 percent rhenium, 0 to about 0.3 percent hafnium, with the balance being nickel and incidental impurities.

Claim 11

The braze material of claim 7 in which the bulk composition range comprises, by weight, about 6 to about 10 percent cobalt, about 6 to about 8 percent chromium, about 5.5 to about 6.6 percent aluminum, 0 to about 2 percent molybdenum, about 5.5 to about 7.5 percent tantalum, about 4 to about 6 percent tungsten, 0 to about 1 percent niobium, about 2 to about 4 percent rhenium, 0 to about 0.3 percent hafnium, with the balance being nickel and incidental impurities.

Claim 12

The braze material of claim 7 in which the high melt component is comprised of at least two metallic powders based on the group of elements consisting of cobalt and nickel, each having a composition range that contains boron and silicon only as incidental impurities.

Claim 13

The braze material of claim 7 in which the eutectic component is comprised of at least two nickel-base alloys, each having a composition range.

Claim 14

The braze material of claim 7 in which the eutectic component is comprised of at least two nickel-base alloys, each having a composition range.

Claim 15

An improved braze material for brazing at last one superalloy substrate comprising: a high melt component having at least one metallic powder consisting essentially of, by weight, about 4 to about 18.5 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13.7 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities; a low melt component having at least one metallic powder consisting essentially of, by weight, about 3.9 to about 25 percent cobalt, about 4.6 to about 22 percent chromium, 0 to about 12.2 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 2 percent molybdenum, 0 to about 5.4 percent tantalum, 0 to about 7 percent tungsten, 0 to about 3 percent niobium, 0 to about 1.5 percent rhenium, 0 to about 1.1 percent hafnium, 0 to about 10 percent silicon, 0 to about 2.3 percent boron, wherein the total amount of silicon plus boron is at least 0.5 percent, with the balance being nickel and incidental impurities; and a eutectic component having at least one metallic powder having a composition range consisting essentially of, by weight, about 3.1 to about 8.2 percent cobalt, about 6.8 to about 38.5 percent chromium, 0 to about 12.6 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 1.3 percent molybdenum, 0 to about 23.1 percent tantalum, 0 to about 2.4 percent tungsten, 0 to about 5.1 percent niobium, 0 to about 1 percent rhenium, 0 to about 0.4 percent hafnium, 0 to about 0.6 percent yttrium, less than about 0.15 percent carbon, with the balance being nickel and incidental impurities; wherein the high melt component and the low melt component and the eutectic component together comprise a bulk composition range consisting essentially of, by weight, about 6 to about 12 percent cobalt, about 7 to about 18 percent chromium, about 3 to about 6.5 percent aluminum, 0 to about 5.5 percent titanium, 0 to about 2 percent molybdenum, about 3 to about 8.5 percent tantalum, about 2.5 to about 5.5 percent tungsten, 0 to about 1.2 percent niobium, 0 to about 3.5 percent rhenium, 0 to about 1.5 percent hafnium, 0 to about 1.8 percent silicon, 0 to about 1 percent boron, 0 to about 0.1 percent carbon, with the balance being nickel and incidental impurities; wherein the bulk composition range comprises less than about 2.0 total weight percent of elements selected from the group consisting of boron and silicon; wherein the low melt component comprises about 10 to about 40 percent by weight of the braze material and the eutectic component comprises about 10 to about 30 percent by weight of the braze material; wherein the braze material has an effective brazing temperature above about 2300° F.; wherein the high melt component is substantially solid at the effective brazing temperature; and wherein the low melt and eutectic components are substantially liquid at the effective brazing temperature.

Claim 16

An improved braze material for brazing at last one superalloy substrate comprising: a high melt component having at least one metallic powder consisting essentially of, by weight, about 4 to about 18.5 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13.7 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities; a low melt component having at least one metallic powder consisting essentially of, by weight, about 3.9 to about 25 percent cobalt, about 4.6 to about 22 percent chromium, 0 to about 12.2 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 2 percent molybdenum, 0 to about 5.4 percent tantalum, 0 to about 7 percent tungsten, 0 to about 3 percent niobium, 0 to about 1.5 percent rhenium, 0 to about 1.1 percent hafnium, 0 to about 10 percent silicon, 0 to about 2.3 percent boron, wherein the total amount of silicon plus boron is at least 0.5 percent, with the balance being nickel and incidental impurities; and a eutectic component having at least one metallic powder having a composition range consisting essentially of, by weight, about 3.1 to about 8.2 percent cobalt, about 6.8 to about 38.5 percent chromium, 0 to about 12.6 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 1.3 percent molybdenum, 0 to about 23.1 percent tantalum, 0 to about 2.4 percent tungsten, 0 to about 5.1 percent niobium, 0 to about 1 percent rhenium, 0 to about 0.4 percent hafnium, 0 to about 0.6 percent yttrium, less than about 0.15 percent carbon, with the balance being nickel and incidental impurities; wherein the high melt component and the low melt component and the eutectic component together comprise a bulk composition range consisting essentially of, by weight, about 6 to about 12 percent cobalt, about 7 to about 18 percent chromium, about 3 to about 6.5 percent aluminum, 0 to about 5.5 percent titanium, 0 to about 2 percent molybdenum, about 3 to about 8.5 percent tantalum, about 2.5 to about 5.5 percent tungsten, 0 to about 1.2 percent niobium, 0 to about 3.5 percent rhenium, 0 to about 1.5 percent hafnium, 0 to about 1.8 percent silicon, 0 to about 1 percent boron, 0 to about 0.1 percent carbon, with the balance being nickel and incidental impurities; wherein the bulk composition range comprises less than about 2.0 total weight percent of elements selected from the group consisting of boron and silicon; wherein the low melt component comprises about 10 to about 40 percent by weight of the braze material and the eutectic component comprises about 10 to about 30 percent by weight of the braze material; wherein the braze material has an effective brazing temperature above about 2300° F.; wherein the high melt component is substantially solid at the effective brazing temperature; and wherein the low melt and eutectic components are substantially liquid at the effective brazing temperature.

Claim 17

The braze material of claim 13 in which the bulk composition range comprises, by weight, about 9 to about 12 percent cobalt, about 13 to about 16 percent chromium, abut 4.5 to about 5.5 percent aluminum, about 1.5 to about 3 percent titanium, 0.5 to about 1.5 percent molybdenum, about 3.5 to about 5.5 percent tantalum, about 2.5 to about 4 percent tungsten, 0 to about 1.2 percent niobium, 1 to about 2.5 percent rhenium, about 0.5 to about 1.5 percent hafnium, 0 to about 0.7 percent boron, with the balance being nickel and incidental impurities.

Claim 18

The braze material of claim 13 in which the high melt component is comprised of at least two metallic powders based on the group of elements consisting of cobalt and nickel, each having a composition range that contains boron and silicon only as incidental impurities.

Claim 19

The braze material of claim 13 in which the low melt component is comprised of at least two nickel-base alloys, each having a composition range that includes a amount of at least one element selected from the group consisting of boron and silicon.