Claim 1

Independent Claim 128 words

A wrought and annealed iron-aluminum alloy consisting essentially of 8 to 9.5% aluminum, an effective amount of chromium sufficient to promote resistance to aqueous corrosion of the alloy, and an alloying constituent selected from the group of elements consisting of an effective amount of molybdenum sufficient to promote solution hardening of the alloy and resistance of the alloy to pitting when exposed to solutions containing chloride, up to about 0.05% carbon with up to about 0.5% of a carbide former which combines with the carbon to form carbides for controlling grain growth at elevated temperatures, and mixtures thereof, and the balance iron, wherein said alloy has a single disordered α phase crystal structure, is substantially non-susceptible to hydrogen embrittlement, and has a room-temperature ductility of greater than 20%.

Claim 2

Dependent Claim 128 words

A wrought and annealed iron-aluminum alloy consisting essentially of 8 to 9.5% aluminum, an effective amount of chromium sufficient to promote resistance to aqueous corrosion of the alloy, and an alloying constituent selected from the group of elements consisting of an effective amount of molybdenum sufficient to promote solution hardening of the alloy and resistance of the alloy to pitting when exposed to solutions containing chloride, up to about 0.05% carbon with up to about 0.5% of a carbide former which combines with the carbon to form carbides for controlling grain growth at elevated temperatures, and mixtures thereof, and the balance iron, wherein said alloy has a single disordered α phase crystal structure, is substantially non-susceptible to hydrogen embrittlement, and has a room-temperature ductility of greater than 20%.

Claim 3

Dependent Claim 17 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the carbide former is zirconium.

Claim 4

Dependent Claim 30 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the effective amount of chromium is in a range of more than incidental impurities up to about 7.0%.

Claim 5

Dependent Claim 104 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the alloy contains both the carbon and the carbide former with the carbon being present in an effective amount in the range of more than incidental impurities up to about 0.05% and with the carbide former being in an effective amount sufficient amount in the range of more than incidental impurities up to about 0.5%, and wherein the effective amounts of the carbon and the carbide former are each sufficient to together provide for the formation of sufficient carbides to control grain growth in the alloy during exposure thereof to increasing temperatures.

Claim 6

Dependent Claim 17 words

A wrought and annealed iron-aluminum alloy as claimed in claim 4, wherein the carbide former is zirconium.

Claim 7

Dependent Claim 23 words

A wrought and annealed iron-aluminum alloy as claimed in claim 4, wherein the alloy further includes yttrium in a concentration of about 0.1%.

Claim 8

Dependent Claim 44 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the alloying constituents are provided by molybdenum, carbon and the carbide former, and wherein the effective amount of molybdenum is in a range of more than incidental impurities up to about 4.0%.

Claim 9

Dependent Claim 30 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the effective amount of chromium is in the range of more than incidental impurities up to about 7.0%.

Claim 10

Dependent Claim 87 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the alloy consists essentially of 8 to 9.5% aluminum, about 2 to 7% chromium, about 1 to 4% molybdenum, about 0.02 to 0.05% carbon, about 0.1 to 0.5% of the carbide former, and the balance iron, wherein the alloy has a room-temperature yield strength at 0.2% yield of at least about 70 ksi in longitudinal and transverse directions and a room-temperature ultimate tensile strength of at least about 90 ksi in longitudinal and transverse directions.

Claim 11

Dependent Claim 21 words

A wrought and annealed iron-aluminum alloy as claimed in claim 9, wherein the aluminum is in a concentration of essentially 8.5%.

Claim 12

Dependent Claim 25 words

A wrought and annealed iron-aluminum alloy as claimed in claim 9, wherein the carbide former is zirconium in a concentration of about 0.2 to 0.5%.

Claim 13

Dependent Claim 66 words

A wrought and annealed iron-aluminum alloy consisting essentially of 8 to 9% aluminum, about 4.5 to 5.5% chromium, about 1.8 to 2.2% molybdenum, about 0.020 to 0.032% carbon, about 0.15 to 0.25% zirconium, and the balance iron, wherein said alloy has a single disordered α phase with a body-centered-cubic crystal structure, is substantially non-susceptible to hydrogen embrittlement, and has a room-temperature ductility of greater than 20%.

Claim 14

Dependent Claim 66 words

A wrought and annealed iron-aluminum alloy consisting essentially of 8 to 9% aluminum, about 4.5 to 5.5% chromium, about 1.8 to 2.2% molybdenum, about 0.020 to 0.032% carbon, about 0.15 to 0.25% zirconium, and the balance iron, wherein said alloy has a single disordered α phase with a body-centered-cubic crystal structure, is substantially non-susceptible to hydrogen embrittlement, and has a room-temperature ductility of greater than 20%.

Claim 15

Dependent Claim 66 words

A wrought and annealed iron-aluminum alloy as claimed in claim 12, wherein the alloy has a room-temperature ductility of at least about 22% in both longitudinal and transverse directions, has a room-temperature yield strength at 0.2% yield of at least about 70 ksi in longitudinal and transverse directions, and has a room-temperature ultimate tensile strength of at least about 90 ksi in longitudinal and transverse directions.

Claim 16

Dependent Claim 29 words

A wrought and annealed iron-aluminum alloy as claimed in claim 1, wherein the room temperature elongation of greater than 20% is in the range of 20 to about 29%.

Claim 17

Independent Claim 154 words

A method for preparing an iron-aluminum alloy having a single disordered α phase crystal structure and characterized by a room-temperature ductility of greater than 20% and by being essentially non-susceptible to hydrogen embrittlement, comprising the steps of: (a) forming a blend of alloy constituents comprising 8 to 9.5% aluminum, one or more alloying elements selected from chromium in a concentration up to about 7%, molybdenum in a concentration up to about 4%, carbon in a concentration up to about 0.05%, and a carbide former in a concentration up to about 0.5% and adequate to combine with the carbon for forming grain-growth inhibiting carbides in the alloy; (b) forming a melt of the alloy constituents; (c) working the resulting alloy; and (d) annealing the resulting wrought alloy at a selected temperature greater than about 700° C. followed by air cooling or oil quenching for providing the alloy with said room-temperature ductility of greater than 20%.

Claim 18

Independent Claim 154 words

A method for preparing an iron-aluminum alloy having a single disordered α phase crystal structure and characterized by a room-temperature ductility of greater than 20% and by being essentially non-susceptible to hydrogen embrittlement, comprising the steps of: (a) forming a blend of alloy constituents comprising 8 to 9.5% aluminum, one or more alloying elements selected from chromium in a concentration up to about 7%, molybdenum in a concentration up to about 4%, carbon in a concentration up to about 0.05%, and a carbide former in a concentration up to about 0.5% and adequate to combine with the carbon for forming grain-growth inhibiting carbides in the alloy; (b) forming a melt of the alloy constituents; (c) working the resulting alloy; and (d) annealing the resulting wrought alloy at a selected temperature greater than about 700° C. followed by air cooling or oil quenching for providing the alloy with said room-temperature ductility of greater than 20%.

Claim 19

Dependent Claim 82 words

A method for preparing an iron-aluminum alloy as claimed in claim 15, wherein the step of annealing the wrought alloy at a selected temperature greater than about 700° C. is provided by heating the wrought alloy to a temperature in the range of about 700° C. to about 1100° C., and wherein the heating of the wrought alloy to the selected temperature in said range provides the wrought alloy with a selected room-temperature ductility in the range of 20 to about 29%.

Claim 20

Dependent Claim 22 words

A method for preparing an iron-aluminum alloy as claimed in claim 15, wherein the carbide former is about 0.2 to 0.5% zirconium.

Claim 21

Dependent Claim 20 words

A method for preparing an iron-aluminum alloy as claimed in claim 15, wherein the alloy constituents include about 0.1% yttrium.

Claim 22

Dependent Claim 33 words

A method for preparing an iron-aluminum alloy as claimed in claim 15, wherein the step of working the resulting alloy is provided by mechanically working the alloy though a series of thickness reductions.

Claim 23

Dependent Claim 54 words

A method for preparing an iron-aluminum alloy as claimed in claim 15, wherein the step of working the resulting alloy includes working the alloy at room temperature through a series of thickness reductions with heat treating of the alloy at a temperature of about 800° C. after each of said series of thickness reductions.

Claim 24

Dependent Claim 45 words

A method for preparing an iron-aluminum alloy as claimed in claim 15, wherein the alloy constituents comprise 8 to 9% aluminum, about 4.5 to 5.5% chromium, about 1.8 to 2.2% molybdenum, about 0.020 to 0.032% carbon, about 0.15 to 0.25% zirconium, and the balance iron.

Claim 25

Dependent Claim 57 words

A method for preparing an iron-aluminum alloy as claimed in claim 21, wherein the room-temperature ductility of greater than 20% is a room-temperature ductility in the range of 20 to about 29%, and wherein the selected annealing temperature greater than about 700° C. is a temperature in the range of about 700° C. to about 900° C.

Claim 26

Dependent Claim 21 words

A method for preparing an iron-aluminum alloy as claimed in claim 22, wherein the alloy constituents further comprise about 0.1% yttrium.

Claim 27

Dependent Claim 82 words

An iron-aluminum alloy comprising 8 to 9% aluminum, about 4.5 to 5.5% chromium, about 1.8 to 2.2% molybdenum, about 0.020 to 0.032% carbon, about 0.15 to 0.25% zirconium, about 0.1% yttrium, and the balance iron, wherein said alloy has a single disordered α phase with a body-centered-cubic crystal structure, is substantially non-susceptible to hydrogen embrittlement, and has a room-temperature ductility of greater than 20% when wrought and annealed at a temperature greater than about 700° C. and air cooled or oil quenched.

Claim 28

Dependent Claim 82 words

An iron-aluminum alloy comprising 8 to 9% aluminum, about 4.5 to 5.5% chromium, about 1.8 to 2.2% molybdenum, about 0.020 to 0.032% carbon, about 0.15 to 0.25% zirconium, about 0.1% yttrium, and the balance iron, wherein said alloy has a single disordered α phase with a body-centered-cubic crystal structure, is substantially non-susceptible to hydrogen embrittlement, and has a room-temperature ductility of greater than 20% when wrought and annealed at a temperature greater than about 700° C. and air cooled or oil quenched.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1996-08-23	1997-02-22	1997-08-24	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	2000-08-23	2001-02-22	2001-08-24	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2004-08-23	2005-02-22	2005-08-24	$7700.00	Window Closed / Lapsed

Iron-aluminum alloys having high room-temperature and method for making same

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag